Abstract: Three-dimensional nanoporous aerogels and suitable preparation methods are provided. Nanoporous aerogels may include a carbide material such as a silicon carbide, a metal carbide, or a metalloid carbide. Elemental (e.g., metallic or metalloid) aerogels may also be produced. In some embodiments, a cross-linked aerogel having a conformal coating on a sol-gel material is processed to form a carbide aerogel, metal aerogel, or metalloid aerogel. A three-dimensional nanoporous network may include a free radical initiator that reacts with a cross-linking agent to form the cross-linked aerogel. The cross-linked aerogel may be chemically aromatized and chemically carbonized to form a carbon-coated aerogel. The carbon-coated aerogel may be suitably processed to undergo a carbothermal reduction, yielding an aerogel where oxygen is chemically extracted. Residual carbon remaining on the surface of the aerogel may be removed via an appropriate cleaning treatment.

Abstract: Three-dimensional nanoporous aerogels and suitable preparation methods are provided. Nanoporous aerogels may include a carbide material such as a silicon carbide, a metal carbide, or a metalloid carbide. Elemental (e.g., metallic or metalloid) aerogels may also be produced. In some embodiments, a cross-linked aerogel having a conformal coating on a sol-gel material is processed to form a carbide aerogel, metal aerogel, or metalloid aerogel. A three-dimensional nanoporous network may include a free radical initiator that reacts with a cross-linking agent to form the cross-linked aerogel. The cross-linked aerogel may be chemically aromatized and chemically carbonized to form a carbon-coated aerogel. The carbon-coated aerogel may be suitably processed to undergo a carbothermal reduction, yielding an aerogel where oxygen is chemically extracted. Residual carbon remaining on the surface of the aerogel may be removed via an appropriate cleaning treatment.

Abstract: Three-dimensional nanoporous aerogels and suitable preparation methods are provided. Nanoporous aerogels may include a carbide material such as a silicon carbide, a metal carbide, or a metalloid carbide. Elemental (e.g., metallic or metalloid) aerogels may also be produced. In some embodiments, a cross-linked aerogel having a conformal coating on a sol-gel material is processed to form a carbide aerogel, metal aerogel, or metalloid aerogel. A three-dimensional nanoporous network may include a free radical initiator that reacts with a cross-linking agent to form the cross-linked aerogel. The cross-linked aerogel may be chemically aromatized and chemically carbonized to form a carbon-coated aerogel. The carbon-coated aerogel may be suitably processed to undergo a carbothermal reduction, yielding an aerogel where oxygen is chemically extracted. Residual carbon remaining on the surface of the aerogel may be removed via an appropriate cleaning treatment.