Abstract: A method of manufacturing a reinforced plate glass by which glass surface strength is sufficiently increased, and a stable quality reinforced plate glass is manufactured at high production efficiency. The reinforced plate glass is formed of an inorganic oxide glass, and is provided with a compression stress layer by chemical reinforcement on plate surfaces opposed to each other in a plate thickness direction. Plate end faces have regions where a compression stress is formed and regions where no compression stress is formed.

Abstract: Provided is a method of cleaving and separating a glass sheet (G), the method comprising: a cleaving step of cleaving the glass sheet (G) along preset cleaving lines (X, Y) by a laser cleaving method; and a separation step of separating adjacent pieces of the cleaved glass sheet (G) from each other, wherein the cleaving step is performed under a state in which the glass sheet (G) is placed on a sheet (S) having stretchability, and the separation step is performed by stretching the sheet (S).

Abstract: Provided is a method of cleaving and separating a glass sheet, the method comprising: a cleaving step of cleaving a glass sheet (G) along preset cleaving lines (X, Y) by a laser cleaving method; and a separation step of separating adjacent pieces of the cleaved glass sheet (G) from each other, wherein the cleaving step is performed under a state in which the glass sheet (G) is placed on support members (1) provided respectively in segment regions (P1 to P9), which are segmented by the preset cleaving lines (X, Y), and the separation step is performed by separating the support members (1) from each other in adjacent segment regions (P1 to P9).

Abstract: A method of manufacturing a glass roll, includes: a forming step (S1) of forming, while conveying a glass film, the glass film by a downdraw method; a temporary rolling step (S3) of rolling the glass film while superposing a protective film on the glass film at a downstream end of a path of the conveying in the forming step (S1), to thereby manufacture a source glass roll; and a main rolling step (S4) of unrolling, while conveying the glass film to a downstream side, the glass film from the source glass roll, and then rerolling the glass film while superposing a protective film on the glass film at a downstream end of a path of the conveying, to thereby manufacture a glass roll. Higher tension in a rolling direction is applied to the glass film in the main rolling step (S4) than in the temporary rolling step (S3).

Abstract: A tempered glass of the present invention having a compression stress layer is characterized in that a ?-OH value is 0.01 to 0.5/mm. Here, the “?-OH value” is a value obtained from the following equation by measuring the transmittance of glass by FT-IR.