Abstract: The present invention discloses a process for providing a cross-linked composition, the process comprising the steps of (a) providing an ethylene-?-olefin plastomer having—a density of from 850 kg/m3 to 900 kg/m3; and—an melt flow rate (ISO 1133, 2.16 kg, 190° C.) of 0.3 to 50 g/10 min; (b) grafting the ethylene-?-olefin plastomer with silane crosslinker such that the content of silane crosslinker is in the range of 0.1 to 10.0 wt. % with respect to the grafted ethylene-?-olefin plastomer; (c) contacting said grafted ethylene-?-olefin plastomer with 2 to 8 wt. % of a tin-free silane crosslinking catalyst with respect to the resulting mixture of grafted ethylene-?-olefin plastomer and tin-freesilane crosslinking catalyst, wherein said tin-free catalyst comprises a Brönsted acid at 23° C. and 50% relative humidity for at least 15 minutes thus forming a cross-linked composition, wherein gel content of said cross-linked composition after 15 min is at least 60%.

Abstract: Articles comprising a polymer composition, wherein the polymer composition is obtainable by grafting an ethylene copolymer with comonomer units comprising hydrolysable silane groups, wherein the polymer composition shows high gel content and low compression set at ?25° C. These articles have applications in automotive weather-stripping, such as sealing systems for doors, trunks and hoods.

Abstract: The present invention provides a polyolefin composition, said composition comprising a terpolymer comprising a cross-linkable polyolefin comprising hydrolysable silane groups and a polar comonomer, the polyolefin composition further comprising a cross-linking catalyst and a silicon containing compound. The polar comonomer Is present in an amount of 5-35 wt %.

Abstract: The present invention relates to an ethylene polymer composition comprising: (A) an ethylene polymer comprising epoxy-groups, and (B) a cross-linking agent comprising: (B1) an organo-metallic Lewis acid, and at least one of: (B2) a compound comprising at least one amino group; and (B3) a compound comprising at least one hydroxyl group.

Abstract: The present invention provides a method for producing an at least partially crosslinked polymer composition, having a first melt index (MI) value and a first tensile strength, comprising the steps of: a. providing an ethylene vinyl acetate (EVA) copolymer, the EVA copolymer having a second MI value and a second tensile strength and containing at least 30 wt % units derived from vinyl acetate, b. adding from 0.01 to 0.03 wt % of an organic peroxide, wherein the organic peroxide is diluted in 0.001 to 0.05 wt % of white oil, and c. blending the EVA copolymer and the organic peroxide at a temperature sufficient to initiate crosslinking. The first MI value of the at least partially crosslinked polymer composition is less than 5 g/10 min (190° C., 2.16 kg).

Abstract: The present invention relates to a cross-linkable polyolefin composition comprising a first olefin polymer (A) comprising a first comonomer comprising epoxy groups, and a second olefin polymer (B) comprising a second comonomer comprising carboxylic acid groups and/or precursor thereof.

Abstract: The invention provides a polyolefin composition comprising (i) a polyolefin (A) comprising epoxy groups; and (ii) a polyolefin (B) comprising carboxylic acid groups and/or precursors thereof, with the proviso that at least one of (A) and (B) is polyethylene. Preferably one of (A) and (B) is a low density polyethylene (LDPE) and the other is a polypropylene.

Abstract: The present invention refers to a method for improving the storage stability and/or transport stability of polymer (A) comprising the following steps: a) providing polymer (A) selected from the group consisting of copolymers of ethylene and a C4C12 alpha olefin comonomer, copolymers of propylene and mixtures thereof containing additionally comonomer units comprising hydrolysable silane groups; b) providing a stabilizer (B) selected from the group consisting of sterically hindered phenols, alkyltri-alkoxysilanes, alkenyltrialkoxysilanes and mixtures thereof; c) mixing polymer (A) and stabilizer (B) to obtain a stabilized polymer composition (I); and d) transferring the stabilized polymer composition (I) obtained in step c) in a container comprising at least one barrier layer. In addition, the present invention relates to the use of stabilizer (B) for improving the storage stability and/or transport stability of polymer (A) stored and/or transported in a container having a barrier layer.

Abstract: The present invention discloses a process for providing a cross-linked composition, the process comprising the steps of (a) providing an ethylene-?-olefin plastomer having—a density of from 850 kg/m3 to 900 kg/m3; and—an melt flow rate (ISO 1133, 2.16 kg, 190° C.) of 0.3 to 50 g/10 min; (b) grafting the ethylene-?-olefin plastomer with silane crosslinker such that the content of silane crosslinker is in the range of 0.1 to 10.0 wt.-% with respect to the grafted ethylene-?-olefin plastomer; (c) contacting said grafted ethylene-?-olefin plastomer with 2 to 8 wt.-% of a tin-free silane crosslinking catalyst with respect to the resulting mixture of grafted ethylene-?-olefin plastomer and tin-freesilane crosslinking catalyst, wherein said tin-free catalyst comprises a Brönsted acid at 23° C. and 50% relative humidity for at least 15 minutes thus forming a cross-linked composition, wherein gel content of said cross-linked composition after 15 min is at least 60%.

Abstract: The invention provides a polymer composition comprising (i) an LDPE; (ii) polyolefin (A) comprising epoxy groups; and (iii) polyolefin (B) comprising carboxylic acid groups and/or precursor thereof.

Abstract: The invention provides a polymer composition comprising (i) an LDPE; (ii) a polypropylene; (iii) polyolefin (A) comprising epoxy groups; and (iii) polyolefin (B) comprising carboxylic acid groups and/or precursor thereof.

Abstract: The present invention relates to silane crosslinking catalyst comprising: —75 to 85 wt.-% of an olefin acrylate interpolymer and—15 to 25 wt.-% of a hindered amine light stabilizer (HALS) having a number average molecular weight Mn of 1500 to 4000 g/mol; and—optionally up to 5 wt.-% wax, wherein the silane crosslinking catalyst is free of tin, carboxylic acid(s) and sulphonic acid(s), all weight percentages with respect to the total weight of the silane crosslinking catalyst.

Abstract: The invention relates to a foamable polymer composition comprising a blowing agent and a foamed polymer composition obtained by foaming this foamable polymer composition. The invention further relates to a cable comprising at least one layer which comprises the foamable polymer composition or a foamed polymer composition.

Abstract: The present invention concerns a foamable polymer composition and a foamed polymer composition obtained by foaming this foamable polymer composition. The invention is also concerned with a cable comprising at least one layer which comprises the foamable polymer composition or the foamed polymer composition. The invention further provides a process for producing a foamed polymer composition.

Abstract: Articles comprising a polymer composition, wherein the polymer composition is obtainable by grafting an ethylene copolymer with comonomer units comprising hydrolysable silane groups, wherein the polymer composition shows high gel content and low compression set at ?25° C. These articles have applications in automotive weather-stripping, such as sealing systems for doors, trunks and hoods.

Abstract: The present invention is directed to a foamable polyolefin composition which is crosslinkable by silane groups, to a crosslinked foam obtained from such a foamable polyolefin composition, and to a process for producing a crosslinked foam based on the foamable polyolefin composition. The foamable polyolefin composition comprises a polyethylene bearing hydrolysable silane groups and comonomer units comprising a polar group selected from the group consisting of acrylic acid, methacrylic acid, acrylates, methacrylates, vinyl esters, and mixtures thereof, a silanol condensation catalyst, a physical blowing agent, and a cell nucleating agent.

Abstract: The present invention relates to silane crosslinking catalyst comprising: —75 to 85 wt.-% of an olefin acrylate interpolymer and—15 to 25 wt.-% of a hindered amine light stabilizer (HALS) having a number average molecular weight Mn of 1500 to 4000 g/mol; and—optionally up to 5 wt.-% wax, wherein the silane crosslinking catalyst is free of tin, carboxylic acid(s) and sulphonic acid(s), all weight percentages with respect to the total weight of the silane crosslinking catalyst.

Abstract: The present invention relates to a cross-linkable polyolefin composition comprising a first olefin polymer (A) comprising a first comonomer comprising epoxy groups, and a second olefin polymer (B) comprising a second comonomer comprising carboxylic acid groups and/or precursor thereof.

Abstract: The present invention relates to an ethylene polymer composition comprising: (A) an ethylene polymer comprising epoxy-groups, and (B) a cross-linking agent comprising: (B1) an organo-metallic Lewis acid, and at least one of: (B2) a compound comprising at least one amino group; and (B3) a compound comprising at least one hydroxyl group.

Abstract: The present invention provides a polyolefin composition, said composition comprising a terpolymer comprising a cross-linkable polyolefin comprising hydrolysable silane groups and a polar comonomer, the polyolefin composition further comprising a cross-linking catalyst and a silicon containing compound. The polar comonomer Is present in an amount of 5-35 wt %.