Abstract: A pre-coated steel strip is provided. The steel strip includes a strip of base steel having a length, a width, a first side, and a second side. The length of the strip is at least 100 m and the width is at least 600 mm. An aluminum or an aluminum alloy pre-coating is on at least part of at least one of the first or second sides of the strip of base steel. A thickness tp of the pre-coating is from 20 to 33 micrometers at every location on at least one of the first or second sides. Processes, coated stamped products and land motor vehicles are also provided.

Abstract: A pre-coated steel strip is provided. The steel strip includes a strip of base steel having a length, a width, a first side, and a second side. The length of the strip is at least 100 m and the width is at least 600 mm. An aluminum or an aluminum alloy pre-coating is on at least part of at least one of the first or second sides of the strip of base steel. A thickness tp of the pre-coating is from 20 to 33 micrometers at every location on at least one of the first or second sides. Processes, coated stamped products and land motor vehicles are also provided.

Abstract: A hot-rolled steel sheet having a tensile strength greater than 800 MPa and an elongation at break greater than 10% is provided. A composition of the steel includes, the contents being expressed by weight: 0.050%?C?0.090%, 1%?Mn?2%, 0.015%?Al?0.050%, 0.1%?Si?0.3%, 0.10%?Mo?0.40%, S?0.010%, P?0.025%, 0.003%?N?0.009%, 0.12%?V?0.22%, Ti?0.005%, Nb?0.020% and optionally, Cr?0.45%. A balance of the composition includes iron and inevitable impurities resulting from the smelting. A microstructure of the sheet or part includes, as a surface fraction, at least 80% upper bainite, and a remainder includes lower bainite, martensite and residual austenite. A sum of the martensite and residual austenite, as a surface fraction, is less than 5%.

Abstract: A pre-coated steel strip is provided. The steel strip includes a strip of base steel having a length, a width, a first side, and a second side. The length of the strip is at least 100 m and the width is at least 600 mm. An aluminum or an aluminum alloy pre-coating is on at least part of at least one of the first or second sides of the strip of base steel. A thickness tp of the pre-coating is from 20 to 33 micrometers at every location on at least one of the first or second sides. Processes, coated stamped products and land motor vehicles are also provided.

Abstract: A pre-coated steel strip is provided. The steel strip includes a strip of base steel having a length, a width, a first side, and a second side. The length of the strip is at least 100 m and the width is at least 600 mm. An aluminum or an aluminum alloy pre-coating is on at least part of at least one of the first or second sides of the strip of base steel. A thickness tp of the pre-coating is from 20 to 33 micrometers at every location on at least one of the first or second sides. Processes, coated stamped products and land motor vehicles are also provided.

Abstract: A pre-coated steel strip is provided. The steel strip includes a strip of base steel having a length, a width, a first side, and a second side. The length of the strip is at least 100 m and the width is at least 600 mm. An aluminum or an aluminum alloy pre-coating is on at least part of at least one of the first or second sides of the strip of base steel. A thickness tp of the pre-coating is from 20 to 33 micrometers at every location on at least one of the first or second sides. Processes, coated stamped products and land motor vehicles are also provided.

Abstract: A pre-coated steel strip is provided. The steel strip includesa strip of base steel having a length, a width, a first side, and a second side. The length of the strip is at least 100 m and the width is at least 600 mm. An aluminum or an aluminum alloy pre-coating is on at least part of at least one of the first or second sides of the strip of base steel. A thickness tp of the pre-coating is from 20 to 33 micrometers at every location on at least one of the first or second sides. Processes, coated stamped products and land motor vehicles are also provided.

Abstract: A pre-coated steel strip is provided. The steel strip includes a strip of base steel having a length, a width, a first side, and a second side. The length of the strip is at least 100 m and the width is at least 600 mm. An aluminum or an aluminum alloy pre-coating is on at least part of at least one of the first or second sides of the strip of base steel. A thickness tp of the pre-coating is from 20 to 33 micrometers at every location on at least one of the first or second sides. Processes, coated stamped products and land motor vehicles are also provided.

Abstract: A carbon steel sheet coated with a barrier pre-coating containing nickel and chromium in a weight ratio between 1.5 and 9, and a press hardening method for providing the carbon steel sheet coated with a barrier pre-coating comprising nickel and chromium are described.

Abstract: The invention relates to a hot-rolled steel sheet having a tensile strength greater than 800 MPa and an elongation at break greater than 10%, the composition of which comprises, the contents being expressed by weight: 0.050%?C?0.090%, 1%?Mn?2%, 0.015%?Al?0.050%, 0.1%?Si?0.3%, 0.10%?Mo?0.40%, S?0.010%, P?0.025%, 0.003%?N?0.009%, 0.12%?V?0.22%, Ti?0.005%, Nb?0.020% and, optionally, Cr?0.45%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the sheet or the part comprising, as a surface fraction, at least 80% upper bainite, the possible complement consisting of lower bainite, martensite and residual austenite, the sum of the martensite and residual austenite contents being less than 5%.

Abstract: A manufacturing process of a hot stamped coated part comprising the following successive steps, in this order: providing a hot rolled or cold rolled steel sheet comprising a steel substrate and an aluminium-silicon alloy precoating, the precoating containing more than 50% of free aluminium and having a thickness comprised between 15 and 50 micrometers, then cutting the steel sheet to obtain a precoated steel blank, then heating the blank under non protective atmosphere up to a temperature Ti comprised between Te?10° C. and Te, Te being the eutectic or solidus temperature of the precoating, then heating the blank from the temperature Ti up to a temperature Tm comprised between 840 and 950° C. under non protective atmosphere with a heating rate V comprised between 30° C./s and 90° C.

Abstract: A press hardened steel part is provided. The steel of the part has a chemical composition including, in weight: 0.062%?C?0.095%, 1.4%?Mn?1.9%, 0.2%?Si?0.5%, 0.020%?Al?0.070%, 0.02%?Cr?0.1%, wherein: 1.5%?(C+Mn+Si+Cr)?2.7%, 0.040%?Nb?0.060%, 3.4×N?Ti?8×N wherein: 0.044%?(Nb+Ti)?0.090%, 0.0005?B?0.004%, 0.001%?N?0.009%, 0.0005%?S?0.003%, 0.001%?P?0.020%, optionally: 0.0001%?Ca?0.003%, and the remainder being Fe and unavoidable impurities. The microstructure of the part includes, in a majority of the part, in surface fractions: less than 40% of bainite, less than 5% of austenite, less than 5% of ferrite, and a remainder being martensite. The martensite is fresh martensite and self-tempered martensite.

Abstract: The invention relates to a hot-rolled steel sheet having a tensile strength greater than 800 MPa and an elongation at break greater than 10%, the composition of which comprises, the contents being expressed by weight: 0.050%?C?0.090%, 1%?Mn?2%, 0.015%?Al?0.050%, 0.1%?Si?0.3%, 0.10%?Mo?0.40%, S?0.010%, P?0.025%, 0.003%?N?0.009%, 0.12%?V?0.22%, Ti?0.005%, Nb?0.020% and, optionally, Cr?0.45%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the sheet or the part comprising, as a surface fraction, at least 80% upper bainite, the possible complement consisting of lower bainite, martensite and residual austenite, the sum of the martensite and residual austenite contents being less than 5%.

Abstract: A hot-rolled steel sheet having a tensile strength greater than 800 MPa and an elongation at break greater than 10% is provided. A composition of the steel includes, the contents being expressed by weight: 0.050%?C?0.090%, 1%?Mn?2%, 0.015%?Al?0.050%, 0.1%?Si?0.3%, 0.10%?Mo?0.40%, S?0.010%, P?0.025%, 0.003%?N?0.009%, 0.12%?V?0.22%, Ti?0.005%, Nb?0.020% and optionally, Cr?0.45%. A balance of the composition includes iron and inevitable impurities resulting from the smelting. A microstructure of the sheet or part includes, as a surface fraction, at least 80% upper bainite, and a remainder includes lower bainite, martensite and residual austenite. A sum of the martensite and residual austenite, as a surface fraction, is less than 5%.

Abstract: A cold-rolled sheet is provided. The cold-rolled sheet includes a steel substrate with a carbon content C0 between 0.07% and 0.5%, expressed by weight, and a metal pre-coating on at least the two principal faces of the steel substrate. The substrate has a decarburized area on the surface of each of the two principal faces. The depth p50% of the decarburized area is between 6 and 30 micrometers, and p50% is the depth at which the carbon content is equal to 50% of the content C0. The sheet does not contain a layer of iron oxide between the substrate and the metal pre-coating.

Abstract: A cold-rolled sheet is provided. The cold-rolled sheet is annealed and pre-coated for the fabrication of press hardened parts, composed of a steel substrate for heat treatment with a carbon content C0 between 0.07% and 0.5%, expressed by weight, and a metal pre-coating on at least the two principal faces of the steel substrate. The substrate comprises a decarburized area on the surface of each of the two principal faces. The depth p50% of the decarburized area is between 6 and 30 micrometers, and p50% is the depth at which the carbon content is equal to 50% of the content C0. The sheet does not contain a layer of iron oxide between the substrate and the metal pre-coating. Processes are also provided.

Abstract: A cold-rolled sheet is provided. The cold-rolled sheet includes a steel substrate with a carbon content C0 between 0.07% and 0.5%, expressed by weight, and a metal pre-coating on at least the two principal faces of the steel substrate. The substrate has a decarburized area on the surface of each of the two principal faces. The depth p50% of the decarburized area is between 6 and 30 micrometers, and p50% is the depth at which the carbon content is equal to 50% of the content C0. The sheet does not contain a layer of iron oxide between the substrate and the metal pre-coating.

Abstract: A pre-coated steel strip is provided. The steel strip includes a strip of base steel having a length, a width, a first side, and a second side. The length of the strip is at least 100 m and the width is at least 600 mm. An aluminum or an aluminum alloy pre-coating is on at least part of at least one of the first or second sides of the strip of base steel. A thickness tp of the pre-coating is from 20 to 33 micrometers at every location on at least one of the first or second sides. Processes, coated stamped products and land motor vehicles are also provided.

Abstract: Coated steel having a well defined and uniform thickness is useful and advantageous for preparing products by hot stamping. Products prepared by hot stamping such a steel are particularly advantageous when subjected to a subsequent spot welding step.

Abstract: This invention relates to a cold-rolled sheet that is annealed and pre-coated for the fabrication of press hardened parts, composed of a steel substrate for heat treatment with a carbon content C0 between 0.07% and 0.5%, whereby this content is expressed by weight, and a metal pre-coating on at least the two principal faces of the steel substrate, characterized in that the substrate comprises a decarburized area on the surface of each of the two principal faces, whereby the depth p50% of the decarburized area is between 6 and 30 micrometers, whereby p50% is the depth at which the carbon content is equal to 50% of the content C0, and in that the sheet does not contain a layer of iron oxide between the substrate and the metal pre-coating.