Abstract: A photopolymerization accelerator composition improving color stability and controlling polymerization shrinkage stress of cured resin and/or the resulting composite paste thereby feature by tertiary twisted biphenyldiamine with the general formula I: R2 and R3 are each independently alkyl having from 1 to 5 carbon atoms; R and R1 are each independently hydrogen or halogen; alkyl, alkoxy, or alkylthio having from 1 to 18 carbon atoms; or phenyl and/or substituted phenyl alkoxy, or alkylthio having from 1 to 18 carbon atoms. It can be used in part with conventional photosensitizers and radically polymerizable monomers.

Abstract: A photopolymerization accelerator composition improving color stability and controlling polymerization shrinkage stress of cured resin and/or the resulting composite paste thereby feature by tertiary twisted biphenyldiamine with the general formula I: R2 and R3 are each independently alkyl having from 1 to 5 carbon atoms; R and R1 are each independently hydrogen or halogen; alkyl alkoxy, or alkylthio having from 1 to 18 carbon atoms; or phenyl and/or substituted phenyl alkoxy, or alkylthio having from 1 to 18 carbon atoms. It can be used in part with conventional photosensitizers and radically polymerizable monomers.

Abstract: A dental adhesive composition has an adhesive component and an activator component. The adhesive composition has a volatile organic solvent component, one or more polymerizable (meth)acrylate compounds optionally containing fillers, and a polymerization photoinitiator. The adhesive component may also be a substantially homogeneous mixture of one or more polymerizable (meth)acrylate compounds and an effective amount of a photoinitiator, without a solvent. The activator component includes an aromatic sulfinate salt and an activator component solvent. A method for adhering a restorative to a dental surface includes preparing the surface for restoration; applying a mixture of an adhesive component and an activator component to the prepared cavity, thereby forming a coated cavity surface; and, applying a direct or indirect dental restorative to the coated cavity surface.

Abstract: A photopolymerization accelerator composition improving color stability and controlling polymerization shrinkage stress of cured resin and/or the resulting composite paste thereby feature by tertiary twisted biphenyldiamine with the general formula I: R2 and R3 are each independently alkyl having from 1 to 5 carbon atoms; R and R1 are each independently hydrogen or halogen; alkyl, alkoxy, or alkylthio having from 1 to 18 carbon atoms; or phenyl and/or substituted phenyl alkoxy, or alkylthio having from 1 to 18 carbon atoms. It can be used in part with conventional photosensitizers and radically polymerizable monomers.

Abstract: A photopolymerizable and photocleavable (P&P) resin monomer is derived from a reactive photoresponsible moiety via various linkages to form photopolymerizable monomers and/or oligomers.

Abstract: A photopolymerizable and photocleavable (P&P) resin monomer is derived from a reactive photoresponsible moiety via various linkages to form photopolymerizable monomers and/or oligomers.

Abstract: Disclosed herein are low viscosity and low stress dental compositions comprising at least one low stress polymerizable resin and at least one filler. The dental compositions described herein have high depth of cure and self-leveling characteristics and are capable of bulk application.

Abstract: A self curing activator for chemical polymerization of the interface of a dental bonding agent and a self curing or dual curing dental cement or restorative, includes an aryl borate compound, a polymerizable monomer, an optional acidic compound, an amine compound which exhibits a catalytic action, an organic peroxide containing material, and a metal compound wherein said metal compound promotes the decomposition of the organic peroxide.

Abstract: A photopolymerizable and photocleavable (P&P) resin monomer is derived from a reactive photoresponsible moiety via various linkages to form photopolymerizable monomers and/or oligomers.

Abstract: A composition of macrocyclic oligomer with at least one polymerizable group, (meth)acrylate, for example.

Abstract: A self curing activator for chemical polymerization of the interface of a dental bonding agent and a self curing or dual curing dental cement or restorative, includes an aryl borate compound, a polymerizable monomer, an optional acidic compound, an amine compound which exhibits a catalytic action, an organic peroxide containing material, and a metal compound wherein said metal compound promotes the decomposition of the organic peroxide.

Abstract: The invention provides a dental method including forming a polishing member sufficient, when rotated, to polish a cut unpolished dental tooth surface to a surface roughness of less than 0.07 sRa ?m and, to polish an unpolished dental restorative material supported by a tooth in a patient's mouth to a surface roughness of less than 0.03 sRa ?m. The dental polishing material preferably includes elastomeric polymer impregnated with blocky synthetic diamonds. The synthetic diamonds effectively have particle sizes less than 50 microns. The synthetic diamonds are more than 50 percent by weight of the dental polishing material.

Abstract: A photopolymerizable and photocleavable (P&P) resin monomer is derived from a reactive photoresponsible moiety via various linkages to form photopolymerizable monomers and/or oligomers.

Abstract: A composition of macrocyclic oligomer with at least one (meth)acrylate polymerizable group. A method includes preparing an activated precursor of an oligomer at pseudo high-dilution conditions. A method also includes preparing an activated precursor of an oligomer by reacting the precursor with an activated coupling agent, wherein the precursor is condensable and polymerizable.

Abstract: A container enclosing an applicator and a dental composition including a volatile organic solvent. The container is sealed. The volatile organic solvent is effectively retained within the container, even after storage at about 43° C. for one week. Preferably the container is made of a copolymer of a cycloolefin and an open chain olefin.

Abstract: A composition of macrocyclic oligomer with at least one (meth)acrylate polymerizable group. A method includes preparing an activated precursor of an oligomer at pseudo high-dilution conditions. A method also includes preparing an activated precursor of an oligomer by reacting the precursor with an activated coupling agent, wherein the precursor is condensable and polymerizable.

Abstract: Disclosed herein are low viscosity and low stress dental compositions comprising at least one low stress polymerizable resin and at least one filler. The dental compositions described herein have high depth of cure and self-leveling characteristics and are capable of bulk application.

Abstract: The invention provides a container enclosing an applicator and a dental composition including a volatile organic solvent. The container is sealed. The volatile organic solvent is effectively retained within the container, even after storage at about 43° C. for one week. Preferably the container is made of a copolymer of a cycloolefin and an open chain olefin.

Abstract: A dental adhesive composition has an adhesive component and an activator component. The adhesive composition has a volatile organic solvent component, one or more polymerizable (meth)acrylate compounds optionally containing fillers, and a polymerization photoinitiator. The adhesive component may also be a substantially homogeneous mixture of one or more polymerizable (meth)acrylate compounds and an effective amount of a photoinitiator, without a solvent. The activator component includes an aromatic sulfinate salt and an activator component solvent. A method for adhering a restorative to a dental surface includes preparing the surface for restoration; applying a mixture of an adhesive component and an activator component to the prepared cavity, thereby forming a coated cavity surface; and, applying a direct or indirect dental restorative to the coated cavity surface.

Abstract: A composition of macrocyclic oligomer with at least one (meth)acrylate polymerizable group. A method includes preparing an activated precursor of an oligomer at pseudo high-dilution conditions. A method also includes preparing an activated precursor of an oligomer by reacting the precursor with an activated coupling agent, wherein the precursor is condensable and polymerizable.