Abstract: The present invention relates to heterophasic polypropylene compositions comprising a propylene homo- or copolymer forming a crystalline fraction as a matrix and an amorphous propylene ethylene elastomer as a soluble fraction dispersed in said matrix. The heterophasic polypropylene compositions further comprise an elastomeric ethylene/alpha-olefin random copolymer. The heterophasic polypropylene compositions have a well-balanced relation between stiffness and impact strength, low volatile and semi-volatile emissions and good processability.

Abstract: The present invention relates to a polymer composition comprising at least the following components: A) 70.0 to 95.0 wt.-% based on the overall weight of the polymer composition of a C2C3 random copolymer; whereby said C2C3 random copolymer has a melting point in the range of 110 to 140° C. determined by differential scanning calorimetry according to ISO 11357-3; a MFR2 (230° C., 2.16 kg) determined according to ISO 1133 in the range of 0.5 to 4.0 g/10 min; and a total C2-content in the range of 1 to 10 wt.-% based on the overall weight of the C2C3 random copolymer; B) 5.0 to 30.0 wt.-% based on the overall weight of the polymer composition of a LDPE; whereby said LDPE has a density determined according to ISO 1183 in the range of 915 to 922 kg/m3; and a MFR2 (190° C., 2.16 kg) determined according to ISO 1133 in the range of 0.9 to 20.0 g/10 min; with the proviso that the weight proportions of components A) and B) add up to 100 wt.-%.

Abstract: New C2C3 random copolymers, which combine low sealing initiation temperature (SIT), high hot-tack, low C6-solubles, good optical properties and an improved stiffness/impact balance, which are particularly suited for preparing blown films. The present invention is furthermore related to the manufacture of said copolymers and to their use, as well as to the blown films comprising such C2C3 random copolymers.

Abstract: The present invention relates to a heterophasic polypropylene composition with an improved property profile, e.g. improved balance of toughness, softness and haze, comprising a heterophasic propylene copolymer and a copolymer of propylene and 1-hexene.

Abstract: The present invention is directed to a polyolefin composition (C) containing a heterophasic propylene copolymer (TERHECO) and a styrenic thermoplastic (sTPE), wherein the heterophasic propylene copolymer (TERHECO) consists of units derived from propylene, ethylene and 1-hexene. Further the present invention is directed to articles made from the polyolefin composition (C) as well as to the production of sterilized articles.

Abstract: The invention relates to a process for producing a polypropylene composition by sequential polymerization said polypropylene composition having low sealing initiation temperature (SIT) and high melting point (Tm), presenting thus a broad sealing window.

Abstract: Multilayer film of at least three layers, one core layer and at least one sealing layer wherein the sealing layer comprises a linear low density polyethylene having a density in the range of 0.915 to 0.925 g/cm3, and the core layer comprises a propylene 1-hexene copolymer, said copolymer has an 1-hexene content in the range of 2.0 to 5.0 wt.-% and a xylene soluble fraction in the range of 0.3 to 15.0 wt.-%.

Abstract: The present invention relates to a propylene polymer composition comprising a long chain branched propylene polymer, wherein said propylene polymer composition has a) a xylene hot insolubles (XHU) fraction in an amount of less than 1.0%, based on the total weight amount of the propylene polymer composition, b) a melting temperature Tm of less than 160° C., c) a crystallization temperature Tc of at least 115° C., and d) a F30 melt strength of from 5.0 to less than 30.0 cN, a process for producing said propylene polymer composition by reactive modification of a propylene polymer in the presence of a peroxide, an article comprising said propylene polymer composition and the use of said propylene polymer composition for producing an article.

Abstract: The invention is related to film comprising a polypropylene composition showing improved coefficiency of friction as well as optical properties.

Abstract: Multilayer film comprising at least a skin layer, a core layer and an inner layer, whereby the inner layer comprises a single site catalyst derived (SSC) random propylene ethylene copolymer having—a melting temperature (Tm) from 120° C. to 144° C., —a content of units derived from ethylene in an amount of 1.5 to 6.0 wt.-%, —the melting temperature (Tm) fulfilling the following equation Tm<156° C.?[5.2×C2 content in wt.-%] ° C. wherein C2 content stands for the content of units derived from ethylene; and—a xylene cold soluble content (ISO 16152, 1st ED, 2005-07-01; 25° C.) of preferably below 30 wt.-% wherein the multilayer film is free of phthalic acid esters as well as decomposition products thereof.

Abstract: The invention relates to a process for producing a polypropylene composition by sequential polymerization said polypropylene composition having low sealing initiation temperature (SIT) and high melting point (Tm), presenting thus a broad sealing window.

Abstract: New C2C3 random copolymer composition, which shows improved sealing behaviour due to low sealing initiation temperature (SIT) and high hot tack force. In addition, the inventive composition shows an excellent sterilization behaviour, i.e. retention of low haze level after sterilization. The present invention is furthermore related to the manufacture of said copolymer composition and to its use.

Abstract: A heterophasic polyolefin composition comprising 55 to 95 wt.-% based on the total weight of the heterophasic polyolefin composition of a propylene butene random copolymer (A) having an MFR2 (230° C.) of 0.3 to 100.0 g/10 min and a butene content of 1.5 to 8.0 wt.-%, wherein the propylene butene random copolymer is obtained by a process using a single site catalyst (I) and 5 to 45 wt.-% based on the total weight of the heterophasic polyolefin composition of a copolymer of ethylene (B) having a density in the range of 910 to 935 kg/m3 and an MFR2 (190° C.) of 0.5 to 10 g/10 min, wherein the copolymer of ethylene (B) is obtained by a process using a single site catalyst (II).

Abstract: New C2C3 random copolymer (RACO), which shows improved sealing behaviour due to low sealing initiation temperature (SIT) and high hot tack force. In addition, the inventive C2C3 random copolymer (RACO) shows an excellent sterilization behaviour, i.e. retention of low haze level after sterilization. The present invention is furthermore related to the manufacture of said C2C3 random copolymer (RACO) and to its use.

Abstract: The present invention relates to a propylene polymer composition comprising a long chain branched propylene polymer, wherein said propylene polymer composition has a) a crystallization temperature Tc of less than 115° C., b) a melting temperature Tm of less than 155° C. c) a F30 melt strength of from 5.0 to less than 30.0 cN, and d) a V30 melting extensibility of more than 190 mm/s, a process for producing said propylene polymer composition by reactive modification of a propylene polymer in the presence of a peroxide, an article comprising said propylene polymer composition, the use of said propylene polymer composition for producing an article.

Abstract: New bimodal propylene terpolymer, which combines low sealing initiation temperature (SIT), high melting temperature, good processability and good optical properties, like low haze, its use and articles made therefrom.

Abstract: The present invention is directed to a polyolefin composition (C) containing a heterophasic propylene copolymer (TERHECO) and a styrenic thermoplastic (sTPE), wherein the heterophasic propylene copolymer (TERHECO) consists of units derived from propylene, ethylene and 1-hexene. Further the present invention is directed to articles made from the polyolefin composition (C) as well as to the production of sterilized articles.

Abstract: New C2C3 random copolymers, which combine low sealing initiation temperature (SIT), high hot-tack, low C6-solubles, good optical properties and an improved stiffness/impact balance, which are particularly suited for preparing blown films. The present invention is furthermore related to the manufacture of said copolymers and to their use, as well as to the blown films comprising such C2C3 random copolymers.

Abstract: The present invention is directed to a polypropylene composition (P) comprising a copolymer (C) of propylene and 1-hexene comprising a first random propylene copolymer (A) of propylene and a 1-hexene, and a second random propylene copolymer (B) of propylene and 1-hexene having a higher 1-hexene content than the first random propylene copolymer (A) as well as a plastomer (PL) being an elastomeric copolymer of ethylene and at least one C4 to C10 ?-olefin. Further, the present invention is directed to an article comprising said polypropylene composition (P) and the use of said polypropylene composition (P) as a sealing layer in a multi-layer film.

Abstract: Polypropylene composition comprising a heterophasic polypropylene (HECO) and a bimodal metallocene linear low-density polyethylene (mLLDPE), as well as articles obtained from said polypropylene composition. The present invention is further related to the use of a bimodal metallocene linear low-density polyethylene (mLLDPE) as modifier for heterophasic polypropylenes (HECOs) to improve impact strength and optics.