Abstract: A superhydrophobic polypropylene porous film, including a polypropylene porous film substrate, titanium dioxide layers and a surface modifier layer, is disclosed. The titanium dioxide layers are deposited on the surface of the polypropylene porous film substrate by atomic deposition technology; a surface modifier is coated on the titanium dioxide layers; hydrophobic bonds are formed between the titanium dioxide layers and the surface modifier layer; the superhydrophobic polypropylene porous film has a water contact angle greater than 150 degrees, a rolling angle less than 10 degrees, an aperture of 0.1-0.4 ?m, a porosity of 50%-80%, a tensile strength of 30-50 MPa, and an elongation at break of 10%-30%.

Abstract: A large-particle spherical salt with a particle size of 400-950 ?m and a sphericity of 0.5-1.0 is disclosed, which overcomes the existing difficulty in this field for larger particle size as well as higher sphericity. A preparation method of the large-particle spherical salt is also disclosed, wherein in one preparation process, 2% of gum arabic (based on the mass percentage of solute sodium chloride in a sodium chloride saturated solution) is added, and under conditions of an evaporating temperature of 60° C. a stirring rate of 350 rpm, and an evaporating time of 8 hours, a large-particle spherical salt with a particle size of 921.593 ?m and an average sphericity of 0.904 is successfully prepared. The large-particle spherical salt prepared by the method has a uniform particle size distribution and good appearance, can be combined with other substances, adding some extra value to the salt. Meanwhile, the large-particle spherical salt prepared by the method has a high safety grade (e.g.

Abstract: A superhydrophobic polypropylene porous film, including a polypropylene porous film substrate, titanium dioxide layers and a surface modifier layer, is disclosed. The titanium dioxide layers are deposited on the surface of the polypropylene porous film substrate by atomic deposition technology; a surface modifier is coated on the titanium dioxide layers; hydrophobic bonds are formed between the titanium dioxide layers and the surface modifier layer; the superhydrophobic polypropylene porous film has a water contact angle greater than 150 degrees, a rolling angle less than 10 degrees, an aperture of 0.1-0.4 ?m, a porosity of 50%-80%, a tensile strength of 30-50 MPa, and an elongation at break of 10%-30%.

Abstract: A large-particle spherical salt with a particle size of 400-950 ?m and a sphericity of 0.5-1.0 is disclosed, which overcomes the existing difficulty in this field for larger particle size as well as higher sphericity. A preparation method of the large-particle spherical salt is also disclosed, wherein in one preparation process, 2% of gum arabic (based on the mass percentage of solute sodium chloride in a sodium chloride saturated solution) is added, and under conditions of an evaporating temperature of 60° C. a stirring rate of 350 rpm, and an evaporating time of 8 hours, a large-particle spherical salt with a particle size of 921.593 ?m and an average sphericity of 0.904 is successfully prepared. The large-particle spherical salt prepared by the method has a uniform particle size distribution and good appearance, can be combined with other substances, adding some extra value to the salt. Meanwhile, the large-particle spherical salt prepared by the method has a high safety grade (e.g.