Abstract: A glass or glass powder is fused from a starting mixture containing approximately 38 wt % to 48 wt % SO2, 15 wt % to 19 wt % Al2O3, 4.5 wt % to 11 wt % TiO2, 0 wt % to 1.5 wt % Na2O, 0 wt % to 1.5 wt % K2O and 23 wt % to 30 wt % CaO. In addition, a glass powder mixture includes two glass powders, a carbon black powder and an organic binder, the first glass powder having a mean particle size of approximately 150 &mgr;m to 250 &mgr;m, the second glass powder having a mean particle size of less than approximately 100 &mgr;m, which may be 10 &mgr;m to 70 &mgr;m. The glass or glass powder mixture is suitable for producing a glass ceramic, such as that used as a resistor seal and/or a gas-tight glass ceramic solder in a spark plug.

Abstract: A glass, in particular a glass powder, is fused from a starting mixture containing 38 wt % to 48 wt % SiO2, 15 wt % to 19 wt % Al2O3, 4.5 wt % to 11 wt % TiO2, 0 wt % to 1.5 wt % Na2O, 0 wt % to 1.5 wt % K2O and 23 wt % to 30 wt % CaO. In addition, a glass powder mixture contains a first such glass powder having a mean particle size of 150 &mgr;m to 250 &mgr;m and a second such glass powder having a mean particle size of less than 100 &mgr;m, in particular from 10 &mgr;m to 70 &mgr;m, as well as carbon black powder and an organic binder. This glass or glass powder mixture is especially suitable for producing a glass ceramic, in particular in the form of a resistor seal and/or a gas-tight glass ceramic solder in a spark plug.

Abstract: The invention relates to inorganic-organic compound substances useful for biomedical purposes. The object of the invention is to develop inorganic-organic compound materials which overcome the disadvantages of the state of art, wherein inorganic-organic compound substances for biomedical purposes possess to a large extent specifically adjustable characteristics. Inorganic initial substances form a new solid chemical compound with organic initial substances. The inorganic initial component consists of a biocompatible silicate glass and/or a silicate glass ceramic of the system SiO.sub.2 -Al.sub.2 O.sub.3 -MgO-Na.sub.2 O/K.sub.2 O-F.sup.-, and/or a bioactive phosphate silicate glass and/or a phosphate silicate glass ceramic of the system SiO.sub.2 -Al.sub.2 O.sub.3 -MgO-Na.sub.2 O/K.sub.2 O-CaO-P.sub.2 O.sub.5 F.sup.- and/or of the system SiO.sub.2 -MgO-K.sub.2 O-F.sup.- -CaO-P.sub.2 O.sub.5, and/or a bioactive phosphate glass and/or a phosphate glass ceramic of the system P.sub.2 O.sub.5 -Al.sub.2 O.sub.