Abstract: A process for preparing a body having an osseointegrative topography formed on its surface. The process includes the steps of providing a primary body made of a titanium-zirconium alloy containing 13 to 17 wt-% of zirconium, sandblasting the primary body, and etching the sandblasted primary body with an etching solution including hydrochloric acid, sulfuric acid and water at a temperature of above 80° C. to obtain the body, said etching being performed for a duration of 350 seconds at least.

Abstract: A dental implant having a surface made of a ceramic material. At least a part of the surface includes recesses and cavities formed by removal of discrete grains having an average grain size from 0.1 ?m to 0.6 ?m and/or agglomerates of these grains from the ceramic material.

Abstract: A process for providing a topography to the surface of a dental implant, the surface being made of a ceramic material having yttria-stabilized zirconia, the process including: providing a macroscopic roughness to the surface of the dental implant by a mechanical process and/or injection molding technique; and etching at least a part of the roughened surface, wherein etching is carried out using an etching solution having hydrofluoric acid at a temperature of 70° C. at least, such that discrete grains or agglomerates of grains are removed from the yttria-stabilized zirconia, thereby forming recesses and cavities in the roughened surface is disclosed.

Abstract: A process for preparing a body having an osseointegrative topography formed on its surface. The process includes the steps of providing a primary body made of a titanium-zirconium alloy containing 13 to 17 wt-% of zirconium, sandblasting the primary body, and etching the sandblasted primary body with an etching solution including hydrochloric acid, sulfuric acid and water at a temperature of above 80° C. to obtain the body, said etching being performed for a duration of 350 seconds at least.

Abstract: A process for providing a topography to the surface of a dental implant, said surface being made of a ceramic material. At least a part of the surface of the dental implant is etched with an etching solution comprising hydrofluoric acid at a temperature of at least 70° C. Thereby, discrete grains or agglomerates of grains are removed from the ceramic material.