Abstract: The invention provides a method for reacting a variety of protective entities to form covalent bonds with nylon, which entities can be applied directly in the dyebath with the dyes that are used to dye the nylon without blocking such dyes or interfering with their color yield. Such protective entities include stain-blockers, chlorine resist agents, fire retardants, UV absorbers, antimicrobial agents, fume fade protectors, soil-resist agents and anti-stats. According to this method, a protective entity is reacted with a moiety having the capability of forming a covalent bond with a nylon fiber to create a modified protective entity that is adapted to form a covalent bond with a nylon fiber. The modified protective entity is added to a dyebath containing one or more dyes selected from the group consisting of fiber reactive dyes, acid dyes, acid-premetalized dyes and disperse dyes. The dyebath is applied to nylon fiber at a pH within the range of about 0.5 to about 6.

Abstract: The invention provides a method for reacting a variety of protective entities to form covalent bonds with nylon, which entities can be applied directly in the dyebath with the dyes that are used to dye the nylon without blocking such dyes or interfering with their color yield. Such protective entities include stain-blockers, chlorine resist agents, fire retardants, UV absorbers, antimicrobial agents, fume fade protectors, soil-resist agents and anti-stats. According to this method, a protective entity is reacted with a moiety having the capability of forming a covalent bond with a nylon fiber to create a modified protective entity that is adapted to form a covalent bond with a nylon fiber. The modified protective entity is added to a dyebath containing one or more dyes selected from the group consisting of fiber reactive dyes, acid dyes, acid-premetalized dyes and disperse dyes. The dyebath is applied to nylon fiber at a pH within the range of about 0.5 to about 6.

Abstract: A method of dyeing nylon, particularly cationic dyeable Type 6 and 66 nylon and light dyeable Type 66 nylon, so that the dyed fiber will resist taking on further dye and will have a high degree of wash and bleed fastness when the dyed fiber is subjected to a further high temperature aqueous dye bath. The method includes providing a bifunctional dye solution having a very low pH, i.e. no higher than 1.5. The dye is applied to the fiber with a degree of wet pick-up exceeding 100% by weight of the fiber. The fiber is then steamed, washed, and dried, and contacted by an alkaline solution, such as a trisodium phosphate solution. Thereafter, the fiber is autoclaved. Such a dyed nylon fiber can be combined with an undyed nylon fiber to produce a textile product.