Abstract: The invention is directed to starting glass compositions for veneer ceramics for dental restorations of framework ceramics comprising yttrium-stabilized zirconium dioxide. It is the object of the invention to make possible a translucent veneer ceramic which has high flexural strength as well as excellent adhesion to the framework ceramic of yttrium-stabilized zirconium dioxide. According to the invention, this object is met in a starting glass for veneer ceramics for dental restorations made of yttrium-stabilized zirconium dioxide which is produced from the following components: a) SiO2 58.0-74.0 percent by weight b) Al2O3 4.0-19.0 percent by weight c) Li2O 5.0-17.0 percent by weight d) Na2O 4.0-12.0 percent by weight e) ZrO2 0.5-6.0 percent by weight.

Abstract: The invention is directed to starting glass compositions for veneer ceramics for dental restorations of framework ceramics comprising yttrium-stabilized zirconium dioxide. It is the object of the invention to make possible a translucent veneer ceramic which has high flexural strength as well as excellent adhesion to the framework ceramic of yttrium-stabilized zirconium dioxide. According to the invention, this object is met in a starting glass for veneer ceramics for dental restorations made of yttrium-stabilized zirconium dioxide which is produced from the following components: a) SiO2 58.0-74.0 percent by weight b) Al2O3 4.0-19.0 percent by weight c) Li2O 5.0-17.0 percent by weight d) Na2O 4.0-12.0 percent by weight e) ZrO2 0.5-6.0 percent by weight.

Abstract: The invention is directed to veneer ceramics for dental restorations of framework ceramics comprising yttrium-stabilized zirconium dioxide. It is the object of the invention to make possible a translucent veneer ceramic which has high flexural strength as well as excellent adhesion to the framework ceramic of yttrium-stabilized zirconium dioxide. According to the invention, this object is met in a veneer ceramic for dental restorations made of yttrium-stabilized zirconium dioxide which is produced from the following components: a) SiO2 58.0-74.0 percent by weight b) Al2O3 4.0-19.0 percent by weight c) Li2O 5.0-17.0 percent by weight d) Na2O 4.0-12.0 percent by weight e) ZrO2 0.5-6.0 percent by weight.

Abstract: The invention is directed to veneer ceramics for dental restorations of framework ceramics comprising yttrium-stabilized zirconium dioxide. It is the object of the invention to make possible a translucent veneer ceramic which has high flexural strength as well as excellent adhesion to the framework ceramic of yttrium-stabilized zirconium dioxide. According to the invention, this object is met in a veneer ceramic for dental restorations made of yttrium-stabilized zirconium dioxide which is produced from the following components: a) SiO2 58.0-74.0 percent by weight b) Al2O3 4.0-19.0 percent by weight c) Li2O 5.0-17.0 percent by weight d) Na2O 4.0-12.0 percent by weight e) ZrO2 0.5-6.0 percent by weight.

Abstract: The invention is directed to veneer ceramics for dental restorations of framework ceramics comprising yttrium-stabilized zirconium dioxide. It is the object of the invention to make possible a translucent veneer ceramic which has high flexural strength as well as excellent adhesion to the framework ceramic of yttrium-stabilized zirconium dioxide. According to the invention, this object is met in a veneer ceramic for dental restorations made of yttrium-stabilized zirconium dioxide which is produced from the following components: a) SiO2 58.0-74.0 percent by weight b) Al2O3 ?4.0-19.0 percent by weight c) Li2O ?5.0-17.0 percent by weight d) Na2O ?4.0-12.0 percent by weight e) ZrO2 ?0.5-6.0 percent by weight.

Abstract: A veneering ceramic for dental restorations made of yttrium-stabilized zirconium dioxide comprises, in mass percent: SiO2 55.0-72.5; Nb2O5 6.0-19.8; B2O3 1.0-9.0; Al2O3 1.2-6.0; Li2O 5.0-16.5; Na2O 1.4-11.0; ZrO2 0.5-4.0, or comprises: SiO2 58.0-68.0; Nb2O5 10.0-19.8; Al2O3 1.2-6.0; Li2O 8.0-16.5; Na2O 1.4-8.0; ZrO2 0.5-4.0.

Abstract: The invention is directed to veneer ceramics for dental restorations of framework ceramics comprising yttrium-stabilized zirconium dioxide. It is the object of the invention to make possible a translucent veneer ceramic which has high flexural strength as well as excellent adhesion to the framework ceramic of yttrium-stabilized zirconium dioxide. According to the invention, this object is met in a veneer ceramic for dental restorations made of yttrium-stabilized zirconium dioxide which is produced from the following components: a) SiO2 58.0-74.0 percent by weight b) Al2O3 ?4.0-19.0 percent by weight c) Li2O ?5.0-17.0 percent by weight d) Na2O ?4.0-12.0 percent by weight e) ZrO2 ?0.5-6.0 percent by weight.