Abstract: A soda-lime-silica glass for solar collector cover plates and solar mirrors has less than 0.010 weight percent total iron as Fe2O3, a redox ratio of less than 0.350, less than 0.0025 weight percent CeO2, and spectral properties that include a visible transmission, and a total solar infrared transmittance, of greater than 90% at a thickness of 5.5 millimeters, and reduced solarization. In one non-limiting embodiment of invention, the glass is made by heating a pool of molten soda-lime-silica with a mixture of combustion air and fuel gas having an air firing ratio of greater than 11, or an oxygen firing ratio of greater than 2.31. In another non-limiting embodiment of the invention, streams of oxygen bubbles are moved through a pool of molten glass. In both embodiments, the oxygen oxidizes ferrous iron to ferric iron to reduce the redox ratio.

Abstract: A soda-lime-silica glass for solar collector cover plates and solar mirrors has less than 0.010 weight percent total iron as Fe2O3, a redox ratio of less than 0.350, less than 0.0025 weight percent CeO2, and spectral properties that include a visible transmission, and a total solar infrared transmittance, of greater than 90% at a thickness of 5.5 millimeters, and reduced solarization. In one non-limiting embodiment of invention, the glass is made by heating a pool of molten soda-lime-silica with a mixture of combustion air and fuel gas having an air firing ratio of greater than 11, or an oxygen firing ratio of greater than 2.31. In another non-limiting embodiment of the invention, streams of oxygen bubbles are moved through a pool of molten glass. In both embodiments, the oxygen oxidizes ferrous iron to ferric iron to reduce the redox ratio.