Abstract: An iron-based powder metallurgical composition is provided comprising an iron or iron-based powder and composite lubricant particles, with the composite lubricant particles comprising a core of 10-60% by weight of at least one primary fatty acid amide having more than 18 and not more than 24 carbon atoms and 40-90% by weight of at least one fatty acid bisamide, with the core having nanoparticles of at least one metal oxide adhered thereon. Further provided is a particulate composite lubricant as well as a method of preparing such lubricant.

Abstract: The invention concerns powder compositions consisting of electrically insulated particles of a soft magnetic material of an iron or iron-based powder and 0.1-2% by weight of a lubricant selected from the group consisting of fatty acid amides having 14-22 C atoms. Optionally a thermoplastic binder such as polyphenylene sulphide may be included in the composition. The invention also concerns a method for the preparation of soft magnetic composite components.

Abstract: An iron-based powder metallurgical composition is provided comprising an iron or iron-based powder and a particulate composite lubricant, the composite lubricant comprising particles having a core comprising a solid organic lubricant having fine carbon particles adhered thereon. A particulate composite lubricant and a method for producing the same also are provided.

Abstract: The invention concerns powder compositions consisting of electrically insulated particles of a soft magnetic material of an iron or iron-based powder and 0.1-2% by weight of a lubricant selected from the group consisting of fatty acid amides having 14-22 C atoms. Optionally a thermoplastic binder such as polyphenylene sulphide may be included in the composition. The invention also concerns a method for the preparation of soft magnetic composite components.

Abstract: The invention concerns a powder metal composition comprising an iron based powder and a lubricant and/or binder comprising at least one secondary amide of the general formula: R1—NH—CO—R2, wherein R1 and R2 are the same or different, straight or branched, saturated or unsaturated aliphatic hydrocarbon groups. The invention further concerns a method of making green bodies of the powder metal composition according to the invention, a method of producing a bonded iron-based powder composition, as well as the use of the at least one secondary amide as a lubricating and/or binding agent for iron based powders and the use as a die wall lubricant.

Abstract: The invention concerns an improved segregation-resistant and dust-resistant metallurgical composition for making compacted parts, comprising at least about 80 percent by weight of an iron or iron-based powder; at least one alloying powder; and (c) about 0.05 to about 2 percent by weight of a binding/lubricating combination of polyethylene wax and ethylene bis-stearamide, the polyethylene wax having a weight average molecular weight below about 1000 and a melting point below that of ethylene bis-stearamide, and being present in amount between 10 and 90% by weight of the binding/lubricating combination.

Abstract: The invention concerns a method of improving the dynamic properties of compacted and sintered products having a density between 6.8 and 7.6 g/cm3, preferably between 7.0 and 7.4 g/cm3. According to this method an iron based powder, graphite and a solid particular lubricant having a vaporizing temperature less the sintering temperature, preferably less than about 800° C. is compacted and sintered and the maximum particle size of the lubricant is selected so that the largest pores of a compacted and sintered product prepared from the composition are equal to or less than the largest pores obtained in a compacted and sintered product prepared from the composition without lubricant. The invention also concerns composition of an iron based powder, graphite and a solid particular lubricant having a vaporizing temperature less the sintering temperature, preferably less than about 800° C. and a maximum particle size less than about 0.