Abstract: The inventions discloses a method for reducing fouling on the surface of a ceramic membrane or filter with a recalcitrant filtration cake thereon that is non-responsive to regular back-flushing or other physical means of removal, where the ceramic membrane or filter is subjected to steam fast-flushing by injecting steam directly in feed channel of the ceramic membrane or filter while back-flushing the ceramic membrane or filter at the same time to heat and remove fouled layer on the ceramic membrane or filter while cooling a selective layer of the ceramic membrane or filter to avoid thermal shocking of the ceramic membrane or filter, the surface is cleaned with the ceramic membrane or filter being stationary.

Abstract: The present invention relates to modified ceramic membranes for the treatment of water. The invention discloses a modified ceramic membrane, comprising: a ceramic membrane, and an outer surface of said ceramic membrane is grafted by a hydrophilic organosilane, wherein said organosilane is selected from the group consisting of: CH30(C2H40)x(CH2)ySi(OCH3)3, where x is >4 and y is >0; CH30(C2H40)x(CH2)ySi(OCH2CH3)3, where x is >4 and y is >0; (CH30)3Si(CH2)yO(C2H40)x(CH2)ySi(OCH3)3, N where x is >4 and y is >0; and (CH3CH20)3Si(CH2)yO(C2H40)x(CH2)ySi(OCH2CI-13)3, where x is >4 and y is >0.

Abstract: The present invention relates to modified ceramic membranes for the treatment of water. The invention discloses a modified ceramic membrane, comprising: a ceramic membrane, and an outer surface of said ceramic membrane is grafted by a hydrophilic organosilane, wherein said organosilane is selected from the group consisting of: CH30(C2H40)x(CH2)ySi(OCH3)3, where x is >4 and y is >0; CH30(C2H40)x(CH2)ySi(OCH2CH3)3, where x is >4 and y is>0; (CH30)3Si(CH2)yO(C2H40)x(CH2)ySi(OCH3)3, N where x is >4 and y is >0; and (CH3CH20)3Si(CH2)yO(C2H40)x(CH2)ySi(OCH2CI-13)3, where x is >4 and y is >0.

Abstract: The removal of arsenic, from aqueous liquids by adsorption on alumina, is facilitated by selecting the alumina adsorbent to have a particle size below about 200 micrometers, forming a slurry of the alumina and aqueous liquid and agitating the slurry. It has been found that alumina can be selected to have a particle size sufficiently small, or preferably a combination of both particle size sufficiently small and pore size and number sufficiently large, to achieve 50 ppb or less arsenic within about 2 hours treatment. The alumina with adsorbed arsenic is separated from the slurry by steps preferably comprising microfiltration. A precipitation pretreatment can be combined with the slurry treatment e.g. to handle more concentrated solutions.