Abstract: The present invention is related to hierarchical composite wear component comprising a reinforced part, said reinforced part comprising a reinforcement of a triply periodic minimal surface ceramic lattice structure, said structure comprising multiple cell units, said cell units comprising voids and micro-porous ceramic cell walls, the micro-pores of the cell walls comprising a sinter metal or a cast metal, the ceramic lattice structure being embedded in a bicontinuous structure with a cast metal matrix.

Abstract: The disclosure relates to sintered ceramic grains comprising 3-55 wt. % alumina, 40-95 wt. % zirconia and 1-30 wt. % of one or more other inorganic components. The invention further relates to a method for preparing ceramic grains according to the invention, comprising: making a slurry comprising alumina, zirconia; making droplets of the slurry; introducing the droplets in a liquid gelling-reaction medium wherein the droplets are gellified; drying the gellified deformed droplets.

Abstract: A hierarchical composite wear component may have a reinforcement in the most exposed part to wear, the reinforcement including a three-dimensionally interconnected network of periodically alternating millimetric ceramic-metal composite granules with millimetric interstices. The ceramic-metal composite granules have at least 52 vol %, preferably at least 61 vol %, more preferably at least 70 vol % of micrometric particles of titanium carbide embedded in a first metal matrix. The ceramic-metal composite granules have a density of at least 4.8 g/cm3. The three-dimensionally interconnected network of ceramic-metal composite granules with its millimetric interstices is embedded in the second metal matrix. The reinforcement has on average at least 23 vol %, more preferably at least 28 vol %, most preferably at least 30 vol % of titanium carbide, the first metal matrix being different from the second metal matrix, the second metal matrix including a ferrous cast alloy.

Abstract: The disclosure herein relates to a method for preparing ceramic grains comprising: making a slurry comprising inorganic particles and a gelling agent; making droplets of the slurry; introducing the droplets in a liquid gelling-reaction medium wherein the droplets are gellified; deforming the droplets before, during or after gellification; drying the gellified deformed droplets, thereby obtaining dried grains and sintering the dried grains, thereby obtaining the ceramic grains. The disclosure herein further relates to ceramic grains obtainable by a disclosed method.

Abstract: The disclosure relates to sintered ceramic grains comprising 3-55 wt. % alumina, 40-95 wt. % zirconia and 1-30 wt. % of one or more other inorganic components. The invention further relates to a method for preparing ceramic grains according to the invention, comprising: making a slurry comprising alumina, zirconia; making droplets of the slurry; introducing the droplets in a liquid gelling-reaction medium wherein the droplets are gellified; drying the gellified deformed droplets.

Abstract: The present invention relates to grinding balls made of fritted ceramic comprising a compound of alumina silicate (?Al2O3.?SiO2) and in particular mullite (3Al2O3.2SiO2), zirconia (ZrO2) and alumina (Al2O3).

Abstract: The present invention relates to grinding balls made of fritted ceramic comprising a compound of alumina silicate (?Al2O3.?SiO2) and in particular mullite (3Al2O3.2SiO2), zirconia (ZrO2) and alumina (Al2O3).