Abstract: The invention is a method of plating a nonmetallic substrate comprising the steps of depositing an adhesion enhancing film on the substrate, treating the adhesion enhancing film to make the film catalytic, and forming an outer coating and passivating plate on the adhesion enhancing film. The resulting plated, nonmetallic substrates may comprise any number of materials used as an inner substrate such as compounds of oxide, nitride, phosphide, carbide, glass, ceramic, and mixtures thereof. In use, the resulting substrate may find application in any number of data storage and retrieval application.

Abstract: A disk substrate fabricated front an inner substrate having a specific stiffness greater than about 7.6 Mpsi/gm/cc and an encapsulating layer deposited over the inner substrate. The inner substrate may include materials such as alumina, silicon carbide, beryllium, boron carbide, aluminum, and mixtures thereof. The encapsulating layer may be made from aluminum, magnesium, copper, zinc, and mixtures thereof. The disk substrate may additionally comprise a finishing layer deposited on the encapsulating layer fabricate from a material such as nickel or an alloy thereof.

Abstract: The invention is a method of plating a nonmetallic substrate comprising the steps of depositing an adhesion enhancing film on the substrate, treating the adhesion enhancing film to make the film catalytic, and forming an outer coating and passivating plate on the adhesion enhancing film. The resulting plated, nonmetallic substrates may comprise any number of materials used as an inner substrate such as compounds of oxide, nitride, phosphide, carbide, glass, ceramic, and mixtures thereof. In use, the resulting substrate may find application in any number of data storage and retrieval application.

Abstract: An edge strengthened substrate of a data storage disk and a method for fabricating same is disclosed. A strengthening agent is preferably applied to selected portions of a disk-shaped glass substrate to increase the overall strength of the glass substrate. In one embodiment, a strengthening agent is preferably applied along an inner diameter portion of a disk-shaped glass substrate. A binder is preferably mixed with the strengthening agent to limit the mobility of the strengthening agent to the selected inner diameter portion of the substrate during the strengthening process. The glass substrate is then heated to a diffusion temperature for a sufficient duration of time to permit diffusion of the strengthening agent into the glass substrate. Selective application of a strengthening agent to an outer diameter portion of the glass substrate may be performed to further strengthen the glass substrate.