Abstract: A reaction bonded ceramic body that has 50% to 60%, by weight, boron carbide, and 20% to 30%, by weight, silicon carbide. The reaction bonded ceramic body has least a portion of the boron carbide reacted with silicon to become siliconized boron carbide. Also, a method of making a reaction bonded ceramic material. The method may include the steps of forming a green body from a mixture of boron carbide, carbon, and an organic binder, and contacting the green body with a liquid infiltrant comprising silicon. The infiltrant has a temperature of about 1625° C. to about 1700° C. Furthermore, a method of making a reaction bonded boron carbide ceramic body. The method includes the steps of forming a green body from a mixture of boron carbide, carbon, and an organic binder. The weight ratio of boron carbide to carbon in the green body may be about 5:5 to 1 or more.

Abstract: Exemplary silicon carbide ceramic bodies having inclusions therein are produced according to the invention. An exemplary ceramic body includes silicon carbide in major amounts and unreacted particles of an additive in minor amounts which are bonded to the matrix. The particles are dispersed throughout the silicon carbide, and are preferably selected from one or more of the group consisting of boron nitride, aluminum nitride and titanium diboride.

Abstract: A silicon carbide ceramic body having a high degree of lubricity as a result of large graphite inclusions in the body. The graphite inclusions have an average size of at least about 100 micrometers. The graphite-loaded silicon carbide component is preferably formed by spray drying graphite particles independent of the silicon carbide, blending the graphite agglomerates and silicon carbide to form a raw batch, forming the raw batch into a green body, and sintering the green body to produce a graphite-loaded silicon carbide ceramic body having good density and good strength.

Abstract: A silicon carbide ceramic body having a high degree of lubricity as a result of large graphite inclusions in the body. The graphite inclusions have an average size of at least about 100 micrometers. The graphite-loaded silicon carbide component is preferably formed by spray drying graphite particles independent of the silicon carbide, blending the graphite agglomerates and silicon carbide to form a raw batch, forming the raw batch into a green body, and sintering the green body to produce a graphite-loaded silicon carbide ceramic body having good density and good strength.