Abstract: Inner and outer layers of a braided body portion of an intravascular catheter as well as a soft tip portion are formed from different proportioned blends of nylon and copolymer of ester linked polyethylene and polyamide to produce optimum mechanical properties in the catheter. One or more surfaces of the catheter are coated with a hydrogel containing a copolymer of polyurethane and polyvinylpyrrolidone to provide improved lubricity and antithrombogenicity.

Abstract: A sheet formed from a uniform blend of from about 80 to 97% by weight of polyethylene terephthalate having an intrinsic viscosity of above about 0.9 and a melt viscosity at 525.degree. F. of above about 10,000 poises and correspondingly from about 20 to 3% by weight of a polycarbonate resin having an intrinsic viscosity of about 0.4 to 0.6 and a melt viscosity at 500.degree. F. of less than 50,000 poises; said sheet having a haze value as determined by ASTM D-1003 of less than about 2% and being essentially amorphous and non-oriented. Also disclosed is a process for forming a sheet which comprises uniformly blending the composition, extruding the composition into a sheet at a temperature between about 490.degree. to 530.degree. F. and rapidly cooling the sheet by contact with at least one cooling surface maintained at a surface temperature in the range of about 50.degree. to 160.degree. F. for a period of time not exceeding about 15 seconds.

Abstract: A sheet formed from a uniform blend of from about 80 to 97% by weight of polyethylene terephthalate having an intrinsic viscosity of above about 0.9 and a melt viscosity at 525.degree. F. of above about 10,000 poises and correspondingly from about 20 to 3% by weight of a polycarbonate resin having an intrinsic viscosity of about 0.4 to 0.6 and a melt viscosity at 500.degree. F. of less than 50,000 poises; said sheet having a haze value as determined by ASTM D-1003 of less than about 2% and being essentially amorphous and non-oriented. Also disclosed is a process for forming a sheet which comprises uniformly blending the composition, extruding the composition into a sheet at a temperature between about 490.degree. to 530.degree. F. and rapidly cooling the sheet by contact with at least one cooling surface maintained at a surface temperature in the range of about 50.degree. to 160.degree. F. for a period of time not exceeding about 15 seconds.

Abstract: This invention provides a film or sheet capable of being thermoformed into a shaped article and being formed from a blend of about 60 to 85 parts by weight of a polyethylene terephthalate having an intrinsic viscosity of at least about 0.90, about 15 to 40 parts by weight of a polycarbonate and about 5 to 20 parts by weight of a non-acidic silica filler, such as novaculite, the polyethylene terephthalate portion of the film or sheet having a degree of crystallinity in the range of about 20 to 40%. The present invention also provides compositions for forming such films and sheets and shaped articles thermoformed from such films or sheets, such as cook-in-trays. This invention also provides a process of forming such films or sheets.

Abstract: This invention provides a film or sheet capable of being thermoformed into a shaped article and being formed from a blend of about 60 to 85 parts by weight of a polyethylene terephthalate having an intrinsic viscosity of at least about 0.90, about 15 to 40 parts by weight of a polycarbonate and about 5 to 20 parts by weight of a non-acidic silica filler, such as novaculite, the polyethylene terephthalate portion of the film or sheet having a degree of crystallinity in the range of about 20 to 40%. The present invention also provides compositions for forming such films and sheets and shaped articles thermoformed from such films or sheets, such as cook-in-trays. This invention also provides a process of forming such films or sheets.

Abstract: This invention provides a film or sheet capable of being thermoformed into a shaped article and being formed from a blend of about 60 to 85 parts by weight of a polyethylene terephthalate polymer having an intrinsic viscosity of at least about 0.90 and correspondingly about 40 to 15 parts by weight of a polycarbonate polymer, the polyethylene terephthalate portion of the film or sheet having a degree of crystallinity in the range of about 20 to 40%. The film is essentially non-oriented. The present invention also provides shaped articles thermoformed from such film or sheet, such as cook-in-trays. Moreover, this invention provides a process of forming such film or sheet which comprises the steps of blending about 60 to 85 parts by weight of a polyethylene terephthalate polymer having an intrinsic viscosity of at least about 0.90 with correspondingly about 40 to 15 parts by weight of a polycarbonate resin, extruding the resultant blend at a temperature of above about 500.degree.

Abstract: This invention provides a film or sheet capable of being thermoformed into a shaped article and being formed from a blend of about 60 to 85 parts by weight of a polyethylene terephthalate polymer having an intrinsic viscosity of at least about 0.90 and correspondingly about 40 to 15 parts by weight of a polycarbonate polymer, the polyethylene terephthalate portion of the film or sheet having a degree of crystallinity in the range of about 20 to 40%. The film is essentially non-oriented. The present invention also provides shaped articles thermoformed from such film or sheet, such as cook-in-trays. Moreover, this invention provides a process of forming such film or sheet which comprises the steps of blending about 60 to 85 parts by weight of a polyethylene terephthalate polymer having an intrinsic viscosity of at least about 0.90 with correspondingly about 40 to 15 parts by weight of a polycarbonate resin, extruding the resultant blend at a temperature of above about 500.degree.