Abstract: Providing a core ball wherein a junction melting temperature and a low alpha dose are set for suppressing a soft error generation and solving a mounting problem. A metallic powder as a core is a sphere. A pure degree of a Cu ball of the metallic powder is equal to or higher than 99.9% but equal to or less than 99.995%. A contained amount of one of Pb and Bi or a total contained amount of Pb and Bi is equal to or higher than 1 ppm. A sphericity of the Cu ball is equal to or higher than 0.95. A solder plating film for coating the Cu ball comprises Sn—Bi based alloy. U contained in the solder plating film is equal to or less than 5 ppb and Th is equal to or less than 5 ppb. An alpha dose of the core ball is equal to or less than 0.0200 cph/cm2.

Abstract: A Cu core ball suppresses a soft error and its alpha dose is low. Its surface roughness does not affect a mounting process. A pure degree of the Cu ball as an internal ball is equal to or larger than 99.9% and equal to or less than 95%. A total contained amount of Pb and/or Bi in impurity contained in the Cu ball is equal to or larger than 1 ppm. Its sphericity is equal to or higher than 0.95. A solder plating film coated on the Cu ball is a Sn solder plating film or a solder plating film comprising a lead free solder alloy whose primary component is Sn. In the solder plating film, a contained amount of U is equal to or less than 5 ppb and that of Th is equal to or less than 5 ppb. A total alpha dose of the Cu ball and the solder plating film is equal to or less than 0.0200 cph/cm2. An arithmetic average roughness of the Cu core ball is equal to or less than 0.3 ?m.

Abstract: A Sn—Ag—Cu based lead-free solder ball which does not undergo yellowing of its surface when formed into a solder bump on an electrode of an electronic part such as a BGA package. The solder ball has excellent wettability and does not form voids at the time of soldering, even when it has a minute diameter such as 0.04-0.5 mm. It has a composition comprising 1.0-4.0 mass % of Ag, 0.05-2.0 mass % of Cu, 0.0005-0.005 mass % of P, and a remainder of Sn.

Abstract: A lead-free solder includes 0.05-5 mass % of Ag, 0.01-0.5 mass % of Cu, at least one of P, Ge, Ga, Al, and Si in a total amount of 0.001-0.05 mass %, and a remainder of Sn. One or more of a transition element for improving resistance to heat cycles, a melting point lowering element such as Bi, In, or Zn, and an element for improving impact resistance such as Sb may be added.

Abstract: A Sn—Ag—Cu based lead-free solder ball which does not undergo yellowing of its surface when formed into a solder bump on an electrode of an electronic part such as a BGA package. The solder ball has excellent wettability and does not form voids at the time of soldering, even when it has a minute diameter such as 0.04-0.5 mm. It has a composition comprising 1.0-4.0 mass % of Ag, 0.05-2.0 mass % of Cu, 0.0005-0.005 mass % of P, and a remainder of Sn.

Abstract: A solder which can form a soldered joint of good bonding strength on a Ni layer containing a small amount of P formed from electroless Ni plating with a P-containing plating solution comprises 60–64 mass % of Sn, 0.002–0.01 mass % of P, 0.04–0.3 mass % of Cu, and a remainder of Pb. The solder is particularly suitable for forming a solder bump on a Cu electrode which has been coated with Ni by electroless plating.

Abstract: A lead-free solder includes 0.05-5 mass % of Ag, 0.01-0.5 mass % of Cu, at least one of P, Ge, Ga, Al, and Si in a total amount of 0.001-0.05 mass %, and a remainder of Sn. One or more of a transition element for improving resistance to heat cycles, a melting point lowering element such as Bi, In, or Zn, and an element for improving impact resistance such as Sb may be added.

Abstract: A solder which can form a soldered joint of good bonding strength on a Ni layer containing a small amount of P formed from electroless Ni plating with a P-containing plating solution comprises 60-64 mass % of Sn, 0.002-0.01 mass % of P, 0.04-0.3 mass % of Cu, and a remainder of Pb. The solder is particularly suitable for forming a solder bump on a Cu electrode which has been coated with Ni by electroless plating.

Abstract: Solder spheres which can avoid blackening during transportation have a substantially uniform coating of a lubricant on the surfaces thereof. They are produced by dipping freshly prepared solder spheres in a lubricant solution with a concentration of from 10 ppm to 1000 ppm followed by collection of the spheres and drying. The lubricant is preferably selected from an aliphatic hydrocarbon lubricant, a higher fatty alcohol or acid lubricant, a fatty acid amide lubricant, a metal soap lubricant, a fatty acid ester lubricant, a fluoroplastic lubricant, a silicone lubricant, and a combination thereof.

Abstract: Solder spheres which can avoid blackening during transportation have a substantially uniform coating of a lubricant on the surfaces thereof. They are produced by dipping freshly prepared solder spheres in a lubricant solution with a concentration of from 10 ppm to 1000 ppm followed by collection of the spheres and drying. The lubricant is preferably selected from an aliphatic hydrocarbon lubricant, a higher fatty alcohol or acid lubricant, a fatty acid amide lubricant, a metal soap lubricant, a fatty acid ester lubricant, a fluoroplastic lubricant, a silicone lubricant, and a combination thereof.