Abstract: A carburized component with improved fatigue strength has a base steel containing, by mass %, C: 0.15-0.25%, Si: 0.03-0.50%, Mn: more than 0.60% and not more than 1.5%, P?0.015%, S: 0.006-0.030%, Cr: 0.05-2.0%, Al?0.10%, N?0.03%, and O?0.0020%, and optionally at least one element selected from Mo, Cu, Ni, B, Ti, Nb and V, the balance being Fe and impurities. A surface hardened layer portion satisfies: (a) average carbon concentration in the region from the outermost surface to a point of 0.2 mm depth of 0.35-0.60 mass %, (b) surface roughness Rz?15 ?m, and (c) ?r(0)??800 MPa, ?r(100)??800 MPa, and residual stress intensity index Ir?80000, wherein Ir is calculated by [Ir=?|?r(y)|dy], where y ?m is the depth from the outermost surface and ?r(y) is the residual stress for the points from the outermost surface to a depth of 100 ?m with the range of y from 0 to 100 (?m).

Abstract: A carburized component with improved fatigue strength has a base steel containing, by mass %, C: 0.15-0.25%, Si: 0.03-0.50%, Mn: more than 0.60% and not more than 1.5%, P?0.015%, S: 0.006-0.030%, Cr: 0.05-2.0%, Al?0.10%, N?0.03%, and O?0.0020%, and optionally at least one element selected from Mo, Cu, Ni, B, Ti, Nb and V, the balance being Fe and impurities. A surface hardened layer portion satisfies: (a) average carbon concentration in the region from the outermost surface to a point of 0.2 mm depth of 0.35-0.60 mass %, (b) surface roughness Rz?15 ?m, and (c) ?r(0)?-800 MPa, ?r(100)?-800 MPa, and residual stress intensity index Ir?80000, wherein Ir is calculated by [Ir=?|?r(y)|dy], where y ?m is the depth from the outermost surface and ?r(y) is the residual stress for the points from the outermost surface to a depth of 100 ?m with the range of y from 0 to 100 (?m).

Abstract: The steel wire rod contains oxides which comprises, on the weight % basis, SiO2, 70% or more; CaO+Al2O3, less than 20%; and ZrO2, 0.1 to 10% in the average composition of oxides of 2 &mgr;m or more in width on a longitudinal section thereof. This wire rod is excellent in cold workability such as drawability, and steel wires which have high fatigue strength can be produced from this wire rod as stock steel.