Abstract: Provided are a reagent for transparentizing a carbohydrate- or protein-containing material, the reagent including a compound selected from the group consisting of a benzene carboxylic acid compound, a hydroxybenzene compound, a benzene sulfonic acid compound, a homosulfamine compound, and a benzenesulfohydroxamic acid compound; and a method for transparentizing said material, including processing the carbohydrate- or protein-containing material in said reagent.

Abstract: Described are fuel parts comprising a crystalline polyamide resin having a terminal amino group concentration>a terminal carboxyl group concentration and excellent in fuel resistance at their weld portion, which fuel parts are suited for use as various parts to be attached to fuel tanks of automobiles and the like, and a process for producing the fuel parts.

Abstract: Described are fuel parts comprising a crystalline polyamide resin having a terminal amino group concentration>a terminal carboxyl group concentration and excellent in fuel resistance at their weld portion, which fuel parts are suited for use as various parts to be attached to fuel tanks of automobiles and the like, and a process for producing the fuel parts.

Abstract: A polypropylene resin composition comprising an isotactic polypropylene component, a rubber component, and an inorganic filler component, wherein (a) the melt flow rate, according to ASTM D1238, is 20 g/10 min or more, (b) the flexural modulus, according to ASTM D790, is 2300 MPa or more, (c) the Izod impact strength, according to ASTM D256, is 180 J/m or more at 23.degree. C. and 45 J/m or more at -30.degree. C., (d) the heat deformation temperature, according to ASTM D648, is 130.degree. C. or more, and (e) there is a diffraction peak unique to polypropylene of space group P21/c in the diffraction pattern measured by the wide angle X-ray diffraction method in an injection molded article of the composition formed under a quenching condition.

Abstract: A polyamide resin composition comprising: (A) 100 parts by weight of at least one member selected from a polyamide-11 resin and a polyamide-12 resin; optionally (B) from 3 to 30 parts by weight of a modified polyolefin resin; and (C) from 3 to 25 parts by weight of a plasticizer mixture comprising a plasticizer (C1) and a plasticizer (C2). The modified polyolefin resin (B) is either a modified polyolefin (B1) which is a copolymer of an olefin comprising at least one of ethylene and propylene, with an .alpha.,.beta.-unsaturated carboxylic acid or a derivative thereof, or a modified polyolefin (B2) which is a graft polymer obtained by grafting an .alpha.,.beta.-unsaturated carboxylic acid or a derivative thereof onto a copolymer of an olefin comprising at least one of ethylene and propylene. The plasticizer (C1) has a solidifying point of -40.degree. C.