Abstract: A method for processing lithium ion battery scrap includes a leaching step of leaching lithium ion battery scrap and subjecting the resulting leached solution to solid-liquid separation to obtain a first separated solution; an iron removal step of adding an oxidizing agent to the first separated solution and adjusting a pH of the first separated solution in a range of from 3.0 to 4.0, then performing solid-liquid separation and removing iron in the first separated solution to obtain a second separated solution; and an aluminum removal step of neutralizing the second separated solution to a pH range of from 4.0 to 6.0, then performing solid-liquid separation and removing aluminum in the second separated solution to obtain a third separated solution.

Abstract: A method for processing lithium ion battery scrap according to this invention includes a leaching step of leaching lithium ion battery scrap to obtain a leached solution; an aluminum removal step of neutralizing the leached solution to a pH range of from 4.0 to 6.0, then performing solid-liquid separation and removing aluminum in the leached solution to obtain a first separated solution; and an iron removal step of adding an oxidizing agent to the first separated solution and adjusting the pH in a range of from 3.0 to 5.0, then performing solid-liquid separation and removing iron in the first separated solution to obtain a second separated solution.

Abstract: The present invention provides a method for removing iron from an iron-containing solution containing an iron ion, comprising adding a lithium ion battery cathode material containing manganese to an acidic sulfuric acid solution to obtain a cathode material-containing solution, and then precipitating a manganese ion as manganese dioxide in a mixed solution obtained by mixing the iron-containing solution with the cathode material-containing solution while precipitating the iron ion contained in the iron-containing solution as a solid.

Abstract: A method for processing lithium ion battery scrap includes a leaching step of leaching lithium ion battery scrap and subjecting the resulting leached solution to solid-liquid separation to obtain a first separated solution; an iron removal step of adding an oxidizing agent to the first separated solution and adjusting a pH of the first separated solution in a range of from 3.0 to 4.0, then performing solid-liquid separation and removing iron in the first separated solution to obtain a second separated solution; and an aluminum removal step of neutralizing the second separated solution to a pH range of from 4.0 to 6.0, then performing solid-liquid separation and removing aluminum in the second separated solution to obtain a third separated solution.

Abstract: A method for processing lithium ion battery scrap according to this invention includes a leaching step of leaching lithium ion battery scrap to obtain a leached solution; an aluminum removal step of neutralizing the leached solution to a pH range of from 4.0 to 6.0, then performing solid-liquid separation and removing aluminum in the leached solution to obtain a first separated solution; and an iron removal step of adding an oxidizing agent to the first separated solution and adjusting the pH in a range of from 3.0 to 5.0, then performing solid-liquid separation and removing iron in the first separated solution to obtain a second separated solution.

Abstract: The present invention provides a method for removing iron from an iron-containing solution containing an iron ion, comprising adding a lithium ion battery cathode material containing manganese to an acidic sulfuric acid solution to obtain a cathode material-containing solution, and then precipitating a manganese ion as manganese dioxide in a mixed solution obtained by mixing the iron-containing solution with the cathode material-containing solution while precipitating the iron ion contained in the iron-containing solution as a solid.