Abstract: A thermoplastic elastomer composition including 100 parts by mass of a block copolymer containing a polymer block (X) having an aromatic vinyl compound as a main component and a polymer block (Y) having a conjugated diene compound as a main component, or a hydrogenated product thereof (A); 1 to 400 parts by mass of an ethylene/?-olefin copolymer (B) satisfying the following requirements (b-1) to (b-3); and 0 to 200 parts by mass of a polyolefin-based resin (C) satisfying the following requirement (c-1), (b-1) a kinematic viscosity at 100° C. is 5 to 5,000 mm2/s and a kinematic viscosity at 40° C. is 50 to 100,000 mm2/s, (b-2) a weight-average molecular weight (Mw) determined by gel permeation chromatography (GPC) is 1,000 to 30,000, (b-3) a content ratio of ethylene structural units is 15 to 85 mol %, and (c-1) MFR (230° C. and 2.16 kg) is 0.1 to 500 g/10 min.

Abstract: A water dispersion composition containing an ethylene·?-olefin copolymer acid-modified product (B) in a range of 0.01 to 50% by mass, wherein the ethylene·?-olefin copolymer acid-modified product (B) is an acid-modified product of an ethylene·?-olefin copolymer (A) satisfying requirements (A1) to (A6) as specified herein and also satisfies the requirements (B1) to (B5) as specified herein.

Abstract: A masterbatch of a liquid additive is provided, the resin composition for the masterbatch comprising (a) a block copolymer or a hydrogenated product thereof, the block copolymer containing a polymer block having a vinyl aromatic compound as a main component and a polymer block having a conjugated diene compound as a main component, and 40 to 100 parts by mass of a polyolefinic resin and 100 to 150 parts by mass of an ethylene·?-olefin copolymer with respect to 100 parts by mass of the (a) component, wherein the kinematic viscosity at 100° C. is 10 to 5,000 mm2/s; the ethylene molar content is in the range of 30 to 85 mol %; and the molecular weight distribution (Mw/Mn) for the molecular weight measured by gel permeation chromatography (GPC) with reference to polystyrene is not more than 2.5.

Abstract: A resin composition, a shaped article, a fiber, a film and a sheet. The resin composition includes two or more kinds of polyolefin resins (A), and 0.05 to 10 mass % of an ?-olefin (co)polymer (B) satisfying requirements (b-1) to (b-3): (b-1) A methyl group index is 40 to 60%. The methyl group index is a ratio of an integral of a peak observed in a range of 0.50 to 1.15 ppm to an integral of peaks observed in a range of 0.50 to 2.20 ppm in a 1H-NMR spectrum of a solution of the (co)polymer (B) in deuterated chloroform, positions of the peaks being calculated relative to a solvent peak at 7.24 ppm assigned to CHCl3 in deuterated chloroform as a reference. (b-2) A weight average molecular weight determined by GPC is 1,500 to 20,000. (b-3) No melting point is observed from ?100 to 150° C. in DSC.

Abstract: A lubricant oil composition for automotive gears includes a lubricant base oil including a mineral oil having a kinematic viscosity at 100° C. of 2.0 to 6.5 mm2/s, a viscosity index of not less than 105 and a pour point of not more than ?10° C., and/or a synthetic oil having a kinematic viscosity at 100° C. of 1.0 to 6.5 mm2/s, a viscosity index of not less than 120 and a pour point of not more than ?30° C.; and an ethylene/?-olefin copolymer having an ethylene content of 55 to 85 mol %, a kinematic viscosity at 100° C. of 10 to 200 mm2/s, a molecular weight distribution of not more than 2.2, and a melting point in the range of ?30° C. to ?60° C. The lubricant oil composition for automotive gears has a kinematic viscosity at 100° C. of 4.0 to 9.0 mm2/s.

Abstract: A masterbatch of a liquid additive is provided, the resin composition for the masterbatch comprising (a) a block copolymer or a hydrogenated product thereof, the block copolymer containing a polymer block having a vinyl aromatic compound as a main component and a polymer block having a conjugated diene compound as a main component, and 40 to 100 parts by mass of a polyolefinic resin and 100 to 150 parts by mass of an ethylene.?-olefin copolymer with respect to 100 parts by mass of the (a) component, wherein the kinematic viscosity at 100° C. is 10 to 5,000 mm2/s; the ethylene molar content is in the range of 30 to 85 mol %; and the molecular weight distribution (Mw/Mn) for the molecular weight measured by gel permeation chromatography (GPC) with reference to polystyrene is not more than 2.5.

Abstract: A lubricant oil composition for automotive gears includes a lubricant base oil including a mineral oil having a kinematic viscosity at 100° C. of 2.0 to 6.5 mm2/s, a viscosity index of not less than 105 and a pour point of not more than ?10° C., and/or a synthetic oil having a kinematic viscosity at 100° C. of 1.0 to 6.5 mm2/s, a viscosity index of not less than 120 and a pour point of not more than ?30° C.; and an ethylene/?-olefin copolymer having an ethylene content of 55 to 85 mol %, a kinematic viscosity at 100° C. of 10 to 200 mm2/s, a molecular weight distribution of not more than 2.2, and a melting point in the range of ?30° C. to ?60° C. The lubricant oil composition for automotive gears has a kinematic viscosity at 100° C. of 4.0 to 9.0 mm2/s.

Abstract: Provided are a viscosity modifier for lubricating oils for obtaining an additive composition for lubricating oils having excellent fluidity in a wide temperature range from low temperature to high temperature; and said additive composition for lubricating oils. Further provided are a viscosity modifier for lubricating oils for obtaining a lubricating oil composition capable of reducing viscosity in good balance in a wide temperature range from low temperature to high temperature; and said lubricating oil composition. The viscosity modifier for lubricating oils includes an ethylene ?-olefin copolymer (A) which includes 30 to 50 mole % of structural units derived from at least one ?-olefin selected from ?-olefins having 4 and 5 carbon atoms and 50 to 70 mole % of structural units derived from ethylene (with the proviso that the total of all structural units of said copolymer is 100 mole %) and which satisfies specific requirements (a), (b), and (c).

Abstract: Provided are a viscosity modifier for lubricating oils for obtaining an additive composition for lubricating oils having excellent fluidity in a wide temperature range from low temperature to high temperature; and said additive composition for lubricating oils. Further provided are a viscosity modifier for lubricating oils for obtaining a lubricating oil composition capable of reducing viscosity in good balance in a wide temperature range from low temperature to high temperature; and said lubricating oil composition. The viscosity modifier for lubricating oils includes an ethylene ?-olefin copolymer (A) which includes 30 to 50 mole % of structural units derived from at least one ?-olefin selected from ?-olefins having 4 and 5 carbon atoms and 50 to 70 mole % of structural units derived from ethylene (with the proviso that the total of all structural units of said copolymer is 100 mole %) and which satisfies specific requirements (a), (b), and (c).

Abstract: [Object] Disclosed is to provide a process for producing a molded article of polyethylene excellent in mechanical properties while the productivity at the time of T-die molding is improved, and a process for producing a secondary molded article by vacuum molding of the molded article with high formability. [Means to Solve the Problems] A process for producing a molded article by T-die molding of a mixture comprising a polyolefinic resin and a polyethylene wax, the polyethylene wax having a density of 880 to 980 (kg/m3) as measured by a density gradient tube method in accordance with JIS K7112 and a number average molecular weight (Mn) of 500 to 4,000 in terms of polyethylene as determined by gel permeation chromatography (GPC) and satisfying the relationship shown by the following expression (I): B?0.

Abstract: [Object]Disclosed is to provide a process for producing a film by using a raw material comprising a polyethylene having a density of 900 to 980 kg/m3 or a polypropylene, whereby improving the productivity at the time of producing the film by a stretch molding. Further the film is obtained without impairing the optical characteristics and mechanical characteristics, which are intrinsic characteristics of polyethylene or polypropylene. [Solving Means]A process for producing a film by a stretch molding of a mixture comprising a polyethylene and a polyethylene wax, the polyethylene having a density of 900 to 980 kg/m3 and an MI of 0.01 to 100 g/10-minutes as measured at 190° C. and a testing load of 21.18 N in accordance with JIS K7210 or a polypropylene, and the polyethylene wax having a density of 890 to 980 kg/m3 and a number-average molecular weight (Mn) of 500 to 4,000 as measured by the gel permeation chromatography (GPC) and satisfying the relationship shown by the following equation (I). B?0.

Abstract: A phosphorous epoxy resin of the invention being obtainable by reacting an organophosphorus compound, a trifunctional epoxy resin and a bifunctional epoxy resin optionally together with a bifunctional phenol compound. A flame-resistant highly thermally stable epoxy resin composition is also provided, which contains the above phosphorous epoxy resin. A cured product with excellent flame resistance and thermal stability can be obtained from the phosphorous epoxy resin, which cured product is useful as a prepreg or a laminate.

Abstract: An epoxy resin composition which exhibits a low dielectric constant and a low dielectric dissipation factor as well as an excellent working susceptibility after its curing is provided. The epoxy resin composition contains at least one member selected from a novolak resin (A) prepared by condensing formalin and an alkylphenol compound; and an epoxy resin (B) prepared by glycidylating said novolak resin (A) with an epihalohydrin.

Abstract: A heat-resistant, flame-retardant epoxy resin composition is provided by combining or reating members selected from a polyfunctional epoxy resin, a bisphenol type epoxy resin, a highly halogenated bisphenol type epoxy resin, a low halogenated bisphenol type epoxy resin, and a halogenated bisphenol. The composition is suitable as a laminate useful for printed circuit boards.