Abstract: A method for producing a heat-resistant roll, and a roll produced by the method, the method including: fabricating a roll part comprising 5 wt % or more of a clay mineral; grinding the roll surface of the roll part; conducting a surface treatment in which the ground roll surface is smoothed in a moisturized state; and forming a coating film of a clay mineral on the surface-treated roll surface.

Abstract: A heating device 10 including a heat-generating member 20 and a support member 30 that supports the heat-generating member 20 and comprises bio-soluble inorganic fibers, wherein the bio-soluble inorganic fibers do not contact directly the heat-generating member 20 or contact of the bio-soluble inorganic fibers with the heat-generating member 20 is reduced.

Abstract: A heat storage member includes a honeycomb structure having a plurality of cells, each of which is filled with capsules and a heat conductive filler. Each capsule contains a heat storage material. The heat storage member is prepared by bringing a starting material that is a mixture of the capsules into contact with the honeycomb structure to cover at least one surface of the opening of the cells of the honeycomb structure, subjecting the same to uniaxial pressure molding under the pressure of 4 MPa to 10 MPa, and filling each cell with the starting material.

Abstract: A base material for a disk roll, the base material including: 5 to 9 wt % of ceramic fibers, 20 to 40 wt % of kibushi clay, 2 to 20 wt % of bentonite and 40 to 60 wt % of mica.

Abstract: A wet blanket obtained by impregnating a blanket including bio-soluble inorganic fibers with a colloidal silica liquid. A cured blanket obtained by curing the wet blanket.

Abstract: A method for producing a heat-resistant roll including: a roll part fabricating step for fabricating a roll part comprising 5 wt % or more of a clay mineral; a grinding step for grinding the roll surface of the roll part; a surface treatment step for conducting a surface treatment in which the ground roll surface is smoothed in a moisturized state; and a clay coating film forming step for forming a coating film of a clay mineral on the surface-treated roll surface.

Abstract: A base material for a disk roll including ceramic fibers, an inorganic binder and scaly silica.

Abstract: A base material for a disk roll including ceramic fibers, an inorganic binder and scaly silica.

Abstract: A base material for a disk roll including ceramic fibers, an inorganic binder and scaly silica.

Abstract: A base material for a disk roll, the base material including: 5 to 9 wt % of ceramic fibers, 20 to 40 wt % of kibushi clay, 2 to 20 wt % of bentonite and 40 to 60 wt % of mica.

Abstract: A heating device 10 including a heat-generating member 20 and a support member 30 that supports the heat-generating member 20 and comprises bio-soluble inorganic fibers, wherein the bio-soluble inorganic fibers do not contact directly the heat-generating member 20 or contact of the bio-soluble inorganic fibers with the heat-generating member 20 is reduced.

Abstract: A disk roll includes a shaft, and a plurality of disks that are fitted to the shaft, the plurality of disks fitted having been fired, having a density of more than 1.20 g/cm3 and 1.50 g/cm3 or less, and including 20 to 50 wt % of ceramic wool, 5 to 30 wt % of kibushi clay, 2 to 20 wt % of bentonite, and 20 to 45 wt % of a filler, the filler being selected from mica, alumina, wollastonite, cordierite, and calcined kaolin.

Abstract: An inorganic fibrous shaped product including organic fiber that includes at least biosoluble inorganic fiber having the following composition and an organic thickener, and including no colloidal silica: [Composition] SiO2: 70 to 82 wt %; CaO: 10 to 29 wt %; MgO: 1 wt % or less; Al2O3: less than 5 wt %; and the total of SiO2, CaO, MgO and Al2O3 exceeds 98 wt %.

Abstract: Inorganic fiber paper including bio-soluble inorganic fibers which have been subjected to a heat treatment and a binder. A method for producing inorganic fiber paper including: the first step of subjecting amorphous bio-soluble inorganic fibers to a heat treatment; and the second step of making paper comprising the heat-treated bio-soluble inorganic fibers and a binder. Equipment for heating and/or thermal insulation which includes the inorganic fiber paper.

Abstract: A paste-like unshaped composition including inorganic fibers that have the following composition ratio and are not coated with a coating layer; an inorganic binder; and a solvent, wherein the composition further optionally comprises inorganic powder, the ratio of the inorganic fibers and the inorganic powder is 100:0 to 10:90, the composition comprises no pH adjuster and no organic fibers, and when the inorganic powder is contained, the inorganic powder does not contain a needle-like crystal structure, [Composition ratio of inorganic fibers] SiO2 66 to 82 wt %; CaO 10 to 34 wt %; MgO 3 wt % or less; Al2O3 5 wt % or less; and the total of SiO2, CaO, MgO and Al2O3 is 98 wt % or more.

Abstract: Inorganic fiber having the following composition ratio and comprising 40 wt % or less of shots each having a diameter of 45 ?m or more: [Composition ratio of inorganic fiber] SiO2 66 to 82 wt %; CaO 10 to 34 wt %; MgO 0 to 3 wt %; Al2O3 0 to 5 wt %; and the total of SiO2, CaO, MgO and Al2O3 is 98 wt % or more.

Abstract: An inorganic fiber including biosoluble fiber and a cationic surfactant adhering to the biosoluble fiber. An inorganic fiber including biosoluble fiber and a surfactant adhering to the biosoluble fiber, wherein the amount of the surfactant is 0.01 to 2 wt %, based on 100 wt % of the whole inorganic fiber comprising the surfactant adhered thereto.

Abstract: An adhesive for inorganic fibers including SiO2, CaO and Al2O3 within a range excluding the range I defined by the following points A, 8, 18, 19 and 20 in the SiO2—Al2O3—CaO state diagram shown in FIG. 1, and including no zeolite. Point A: SiO2 (0%), Al2O3 (100%), CaO (0%): Point 8: SiO2 (20.8%), Al2O3 (79.2%), CaO (0%): Point 18: SiO2 (46.3%), Al2O3 (35.8%), CaO (17.9%): Point 19: SiO2 (31.5%), Al2O3 (53.6%), CaO (14.9%): Point 20: SiO2 (25.2%), Al2O3 (57.5%), CaO (17.3%).

Abstract: A base material for a disk roll including ceramic fibers, an inorganic binder and scaly silica.

Abstract: An inorganic fiber block obtained by stacking blanket-like products each including inorganic fibers, wherein the composition of the inorganic fibers have the following composition: SiO2: 66 to 82 mass %, CaO:10 to 34 mass %, MgO: 0 to 3 mass %, Al2O3: 0 to 5 mass %, and the total of SiO2, CaO, MgO and Al2O3 is 99 mass % or more.