Abstract: Films of thermoplastic poly(arylene ether imidazole)s (PAEI)s are used as surface modifiers for neat resin panels and composite resin panels. The PAEI polymer contains imidazole groups along the backbone which co-cure, i.e., react chemically, with epoxies or bismaleimides during processing and thereby provide excellent adhesion between the PAEI film and an epoxy or bismaleimide neat resin or composite resin facesheet. The film provides good adhesion and a smooth surface to the finished part and acts as a release agent from the mold. The as-processed integral structures have very smooth (specular) surfaces, and since the film releases readily from a glass mold, no release agent is necessary. The PAEI film is thermally stable, resistant to electron radiation, and adheres tenaciously to the facesheet. The film maintains good adhesion even after thermal cycling from room temperature to .about. -196.degree. C.

Abstract: An aqueous process was developed to prepare a consolidated composite laminate from an aqueous slurry. An aqueous poly(amic acid) surfactant solution was prepared by dissolving a poly(amic acid) powder in an aqueous ammonia solution. A polymeric powder was added to this solution to form a slurry. The slurry was deposited on carbon fiber to form a prepreg which was dried and stacked to form a composite laminate. The composite laminate was consolidated using pressure and was heated to form the polymeric matrix. The resulting composite laminate exhibited high fracture toughness and excellent consolidation.