Abstract: A chemimechanical pulp for use in the manufacture of paper or paperboard products where a high drainability, bulky pulp is desired. The pulp has a long fiber content of between 60 and 75%, a fine-material content of at most 14%, a shive content of less than 0.5%, is refined to a freeness of 600 ml CSF at the lowest, and has a tensile index of at least 10 kNm/kg. A method for producing such a pulp comprises: a) impregnating chips with a lignin softening chemical; b) preheating the chips; c) refining the chips to papermaking pulp; wherein the chips are impregnated and heated over a total time period of at most 4 minutes; a) using a hot impregnating liquid having a temperature of at least 130.degree. C.

Abstract: The invention relates to a product easy to disintegrate, containing cellulose-containing fiber material, which has such a strength, that it can be reeled up or handled in sheet shape for storage and transport, without the addition of chemicals, which increase the bonding strength between the fibers. The product is characterized in that it has a density of 550-1000 kg/m.sup.3, a bursting index of 0.15-0.50 MN/kg and a grammage of 300-1500 gm.sup.2, and that the product has a dry solids content of 70-95%.

Abstract: A method is disclosed for delignification of ligno-cellulose containing fiber material comprising mixing an oxygen-containing gas with the cellulose fiber material so as to atomize the gas and form a foam of the gas and the cellulose fiber material, and without an intervening oxidation step, subjecting the foam to upwardly flowing, substantially non-pressurized, alkali extraction. The alkali extraction step is conducted at a temperature of from about 40.degree. to about 80.degree. C. and at a pH, ligno cellulose containing fiber concentration and oxygen containing gas concentration sufficient to provide a bleached, delignified cellulose fiber without bleaching the lignin substance extracted from the material and to suppress lignin condensation reaction during the extraction.