Abstract: A method for producing aluminum oxide is provided. The method uses an aluminum-oxide-forming agent containing a partially hydrolyzed aluminum alkyl compound containing an aluminum trialkyl or a mixture thereof, and a solvent. It is thus possible to produce an aluminum oxide thin film or aluminum oxide particles on or in a substrate that is not resistant to polar solvents. A method of producing a polyolefin-based polymer nanocomposite containing zinc oxide particles or aluminum oxide particles using a solution containing a partially hydrolyzed zinc alkyl or a solution containing a partially hydrolyzed aluminum alkyl is also provided. The polyolefin-based polymer nanocomposite contains a polyolefin substrate and zinc oxide particles or aluminum oxide particles, and does not contain a dispersant. The zinc oxide particles or aluminum oxide particles have an average particle size of less than 100 nm.

Abstract: A method for producing aluminum oxide is provided. The method uses an aluminum-oxide-forming agent containing a partially hydrolyzed aluminum alkyl compound containing an aluminum trialkyl or a mixture thereof, and a solvent. It is thus possible to produce an aluminum oxide thin film or aluminum oxide particles on or in a substrate that is not resistant to polar solvents. A method of producing a polyolefin-based polymer nanocomposite containing zinc oxide particles or aluminum oxide particles using a solution containing a partially hydrolyzed zinc alkyl or a solution containing a partially hydrolyzed aluminum alkyl is also provided. The polyolefin-based polymer nanocomposite contains a polyolefin substrate and zinc oxide particles or aluminum oxide particles, and does not contain a dispersant. The zinc oxide particles or aluminum oxide particles have an average particle size of less than 100 nm.

Abstract: A method for producing aluminum oxide is provided. The method uses an aluminum-oxide-forming agent containing a partially hydrolyzed aluminum alkyl compound containing an aluminum trialkyl or a mixture thereof, and a solvent. It is thus possible to produce an aluminum oxide thin film or aluminum oxide particles on or in a substrate that is not resistant to polar solvents. A method of producing a polyolefin-based polymer nanocomposite containing zinc oxide particles or aluminum oxide particles using a solution containing a partially hydrolyzed zinc alkyl or a solution containing a partially hydrolyzed aluminum alkyl is also provided. The polyolefin-based polymer nanocomposite contains a polyolefin substrate and zinc oxide particles or aluminum oxide particles, and does not contain a dispersant. The zinc oxide particles or aluminum oxide particles have an average particle size of less than 100 nm.

Abstract: A method for producing aluminum oxide is provided. The method uses an aluminum-oxide-forming agent containing a partially hydrolyzed aluminum alkyl compound containing an aluminum trialkyl or a mixture thereof, and a solvent. It is thus possible to produce an aluminum oxide thin film or aluminum oxide particles on or in a substrate that is not resistant to polar solvents. A method of producing a polyolefin-based polymer nanocomposite containing zinc oxide particles or aluminum oxide particles using a solution containing a partially hydrolyzed zinc alkyl or a solution containing a partially hydrolyzed aluminum alkyl is also provided. The polyolefin-based polymer nanocomposite contains a polyolefin substrate and zinc oxide particles or aluminum oxide particles, and does not contain a dispersant. The zinc oxide particles or aluminum oxide particles have an average particle size of less than 100 nm.

Abstract: A method for producing aluminum oxide is provided. The method uses an aluminum-oxide-forming agent containing a partially hydrolyzed aluminum alkyl compound containing an aluminum trialkyl or a mixture thereof, and a solvent. It is thus possible to produce an aluminum oxide thin film or aluminum oxide particles on or in a substrate that is not resistant to polar solvents. A method of producing a polyolefin-based polymer nanocomposite containing zinc oxide particles or aluminum oxide particles using a solution containing a partially hydrolyzed zinc alkyl or a solution containing a partially hydrolyzed aluminum alkyl is also provided. The polyolefin-based polymer nanocomposite contains a polyolefin substrate and zinc oxide particles or aluminum oxide particles, and does not contain a dispersant. The zinc oxide particles or aluminum oxide particles have an average particle size of less than 100 nm.

Abstract: The present invention relates to a protein composition formed of dry matter of a dispersion in which a protein is dispersed in a stabilizer solution, in which the stabilizer includes at least one type selected from the group consisting of a catechol-based stabilizer, 6-hydroxy-2,5,7,8-tetramethylchroman-2-carboxylic acid, 2,6-di-tert-butyl-p-cresol, 2-tert-butyl-4-methoxyphenol, and 6,6?-di-tert-butyl-4,4?-butylidenedi-m-cresol.

Abstract: A main object is to provide a biaxially stretched polypropylene film for capacitors that has high voltage resistance at high temperatures and excellent dielectric breakdown properties and that can be formed into an ultrathin film. Furthermore, a capacitor obtained by using the biaxially stretched polypropylene film for capacitors described above is provided. The biaxially stretched polypropylene film for capacitors, includes a polypropylene resin, and the film has a spacing value of (040) face of ?-crystal measured by X-ray diffraction of 0.525 to 0.530 nm.

Abstract: The present invention relates to a protein composition formed of dry matter of a dispersion in which a protein is dispersed in a stabilizer solution, in which the stabilizer includes at least one type selected from the group consisting of a catechol-based stabilizer, 6-hydroxy-2,5,7,8-tetramethylchroman-2-carboxylic acid, 2,6-di-tert-butyl-p-cresol, 2-tert-butyl-4-methoxyphenol, and 6,6?-di-tert-butyl-4,4?-butylidenedi-m-cresol.

Abstract: A method for producing aluminum oxide is provided. The method uses an aluminum-oxide-forming agent containing a partially hydrolyzed aluminum alkyl compound containing an aluminum trialkyl or a mixture thereof, and a solvent. It is thus possible to produce an aluminum oxide thin film or aluminum oxide particles on or in a substrate that is not resistant to polar solvents. A method of producing a polyolefin-based polymer nanocomposite containing zinc oxide particles or aluminum oxide particles using a solution containing a partially hydrolyzed zinc alkyl or a solution containing a partially hydrolyzed aluminum alkyl is also provided. The polyolefin-based polymer nanocomposite contains a polyolefin substrate and zinc oxide particles or aluminum oxide particles, and does not contain a dispersant. The zinc oxide particles or aluminum oxide particles have an average particle size of less than 100 nm.

Abstract: A main object is to provide a biaxially stretched polypropylene film for capacitors that has high voltage resistance at high temperatures and excellent dielectric breakdown properties and that can be formed into an ultrathin film. Furthermore, a capacitor obtained by using the biaxially stretched polypropylene film for capacitors described above is provided. The biaxially stretched polypropylene film for capacitors, includes a polypropylene resin, and the film has a spacing value of (040) face of ?-crystal measured by X-ray diffraction of 0.525 to 0.530 nm.