Abstract: A method and an apparatus for compacting a CIGS thin film in a non-vacuum environment are provided. According to the present invention, a substrate having a CIGS light absorbing layer configured thereon is processed with a soft baking process. Then, a pneumatic cylinder is employed for providing a pressure for driving a roller which is fixed to a holder. The holder is connected to the pneumatic cylinder. The roller is driven to downwardly apply a pressing force onto the CIGS light absorbing layer. The substrate is then moved back and forth to compact the CIGS light absorbing layer uniformly.

Abstract: A method for preparing a CIGS ink without a surfactant or a binder is provided. In accordance with the method of the present invention, an initial CIGS mixture powder is obtained by mixing two component powder, three component powder or four component powder of copper, indium, gallium, and selenium in predetermined proportions. Then additional selenide powder is added and mixed into the initial CIGS mixture powder to form a final CIGS mixture powder. Then, a certain proportion of solvent is added into the final CIGS mixture powder, and the mixture powder is then stirred to obtain a CIGS ink in a predetermined copper/indium/gallium/selenium ratio as desired.

Abstract: A method for fabricating a cadmium sulfide thin film, in which the chemical bath including the sulfur-containing compounds and the cadmium-containing compounds is adjusted to alkaline by adding aqueous ammonia, followed by adding the buffer salts while stirring and heating, and then the glass substrate is immersed in the chemical bath such that when the immersing time is increased, the thickness of cadmium sulfide thin film will be increased, and the cadmium sulfide thin film obtained does not have a dual structure, and thereby the obtained cadmium sulfide thin film can have excellent adhesion to the glass substrate, and thereby the quality of cadmium sulfide thin film can be improved.

Abstract: A vanish, a heat-dissipation prepreg, and the manufacturing method thereof are disclosed. The vanish has a curing agent with structure as indicated in formula (1). The vanish based on this curing agent will improve thermal stability and peel strength. Glass fabric cloth is dipped into the vanish having the curing agent to form a heat-dissipation prepreg with better thermal stability and peel strength. Furthermore, the curing agent has polarity so that inorganic powders are uniformly distributed in the prepreg. Therefore, the dissipation efficiency of the heat-dissipation prepreg is improved.