Abstract: Disclosed are individualized, crosslinked fibers, and processes for making such fibers, and absorbent structures containing the fibers. The individualized, crosslinked fibers have a polymeric polyacrylic acid crosslinking agent reacted with the fibers in the form of intrafiber crosslink bonds. Preferably, the crosslinking agent is a copolymer of acrylic acid and maleic acid and preferably, between about 1.0 weight % and about 10.0 weight % of the crosslinking agent reacts with the individualized fibers to form the intrafiber crosslink bonds. The individualized, crosslinked fibers are useful in a variety of absorbent structure applications. The absorbent structures may also contain hydrogel-forming material.

Abstract: A process for making individualized, crosslinked fibers having low levels of residual crosslinking agent. The fibers are made by contacting the fibers with a crosslinking agent; reacting the crosslinking agent with the fibers to form intrafiber crosslink bonds in the substantial absence of interfiber bonds; and washing the fibers with an alkaline solution.

Abstract: Individualized, crosslinked fiber, and process for making such fibers. The individualized, crosslinked fibers have between about 0.5 mole % and about 3.5 mole % crosslinking agent, calculated on a cellulose anhydroglucose molar basis, reacted with fibers in the form of intrafiber crosslink bonds, wherein the crosslinking agent is selected from the group consisting of C.sub.2 -C.sub.8 dialdehydes, C.sub.2 -C.sub.8 dialdehyde acid analogues having at least one aldehyde functionality, and oligomers of such C.sub.2 -C.sub.8 dialdehydes, and dialdehyde acid analogues. Preferably, the crosslinking agent is glutaraldehyde, and between about 0.75 mole % and about 2.5 mole % crosslinking agent react to form the intrafiber crosslink bonds. The individualized crosslinked fibers are useful in a variety of absorbent structure applications.

Abstract: Absorbent structures containing individualized, crosslinked fibers. The individualized, crosslinked fibers preferably have between about 0.5 mole % and about 3.5 mole % crosslinking agent, calculated on a cellulose anhydroglucose molar basis, reacted with the fibers in the form of intrafiber crosslink bonds, wherein the crosslinking agent is selected from the group consisting of C.sub.2 -C.sub.8 dialdehydes, C.sub.2 -C.sub.8 dialdehyde acid analogues having at least one aldehyde functionality, and oligomers of such C.sub.2 -C.sub.8 dialdehydes and dialdehyde acid analogues. More preferably, the crosslinking agent is glutaraldehyde, and between about 0.75 mole % and about 2.5 mole % crosslinking agent react to form the intrafiber crosslink bonds. Also preferably, the absorbent structures have actual dry densities greater than their corresponding equilibrium wet densities, and expand upon wetting. The absorbent structures may also contain hydrogel-forming material.