Abstract: A process for coating electrically conductive substrates by (1) applying an electrocoat film to an electrically conductive substrate and curing it to give an electrocoat and then (2) applying a layer of a pulverulent coating material to the electrocoat and curing it to give a powder coat or alternatively (1) applying an electrocoat film to an electrically conductive substrate and drying it without fully curing it, (2) applying a layer of a pulverulent coating material to the dried electrocoat film(s) and (3) jointly curing the dried electrocoat film and the layer of the pulverulent coating material to give the electrocoat and the powder coat wherein the pulverulent coating material comprises (A) at least one epoxy resin having a melting point, melting range or glass transition temperature>30° C., (B) at least one carboxyl-containing polyester resin having a melting point, melting range or glass transition temperature>30° C.

Abstract: Powder coating materials which comprise high-functionality, highly branched or hyperbranched polycarbonates based on dialkyl or diaryl carbonates or on phosgene, diphosgene or triphosgene and on aliphatic, aliphatic/aromatic or aromatic diols or polyols.

Abstract: A process for coating electrically conductive substrates by (1) applying an electrocoat film to an electrically conductive substrate and curing it to give an electrocoat and then (2) applying a layer of a pulverulent coating material to the electrocoat and curing it to give a powder coat or alternatively (1) applying an electrocoat film to an electrically conductive substrate and drying it without fully curing it, (2) applying a layer of a pulverulent coating material to the dried electrocoat film(s) and (3) jointly curing the dried electrocoat film and the layer of the pulverulent coating material to give the electrocoat and the powder coat wherein the pulverulent coating material comprises (A) at least one epoxy resin having a melting point, melting range or glass transition temperature >30° C., (B) at least one carboxyl-containing polyester resin having a melting point, melting range or glass transition temperature >30° C.

Abstract: A powder coating material comprising, based on the coating material, (A) from 40 to 65% by weight of at least one solid epoxy resin which is polyfunctional in respect of thermal crosslinking by way of the epoxide groups and has an epoxide equivalent weight of from 380 to 420 g/equ., an ICI melt viscosity at 150° C. of from 2800 to 5000 mPas, and a softening point of from 95 to 105° C., (B) from 15 to 35% by weight of at least one solid, linear epoxy resin based on bisphenol A, AD and/or F, having a functionality in respect of thermal crosslinking by way of the epoxide groups of not more than 2, (C) from 15 to 30% by weight of an inorganic filler and (D) from 1 to 10% by weight of at least one hardener; and its use for producing functional coatings for substrates for high long-term service temperatures.

Abstract: The invention relates to three-layer metal pipe coating compositions based on a powder primer, on a thermoplastic hard adhesive and on a polyolefin cladding. The powder primer contains epoxidized novolak resins, phenolic crosslinking agents and fillers based on crystalline silicic acid modifications. The invention likewise relates to a process for the exterior coating of metal pipes by a three-layer method, in which the powder primer described is applied to the metal pipe, a thermoplastic hard adhesive is applied to the powder primer, and subsequently a polyolefin cladding is applied.

Abstract: Powder coating, process for the exterior coating of metal pipes, and use of the powder coating for the single-layer exterior coating of metal pipes. The powder coating comprises epoxy resins, phenolic crosslinking agents, catalysts, fillers and additives. The fillers used are crystalline silicic acids modified with glycidyl groups. The invention also relates to a process for the exterior coating of metal pipes and to use of the coatings for a single layer exterior coating of metal pipes.