Abstract: The invention relates to a foamable mixture which contains at least one alkoxysilane-terminated prepolymer and which can be produced of a) at least one alkoxysilane that was functionalized with isocyanate groups and that can be produced of at least one hydroxyfunctional and/or aminofunctional alkoxysilane and at least one diisocyanate or polyisocyanate, and b) at least one compound that contains at least one OH group, and at least one blowing agent, characterized in that the foamable mixture has a dynamic viscosity of 100 to 25,000 mPas, preferably 500 to 10,000 mPas, at 23° C. The invention further relates to a method for producing said foamable mixture. The foamable mixtures according to the invention are suitable for sealing, insulating and mounting joints, roof surfaces, windows and doors or for filling hollow spaces.

Abstract: The invention relates to a foamable mixture which contains at least one alkoxysilane-terminated prepolymer and which can be produced of a) at least one alkoxysilane that was functionalized with isocyanate groups and that can be produced of at least one hydroxyfunctional and/or aminofunctional alkoxysilane and at least one diisocyanate or polyisocyanate, and b) at least one compound that contains at least one OH group, and at least one blowing agent, characterized in that the foamable mixture has a dynamic viscosity of 100 to 25,000 mPas, preferably 500 to 10,000 mPas, at 23° C. The invention further relates to a method for producing said foamable mixture. The foamable mixtures according to the invention are suitable for sealing, insulating and mounting joints, roof surfaces, windows and doors or for filling hollow spaces.

Abstract: A process for the production of compounds which contain at least one urea group and at least one silyl goup. The process involves reacting a compound containing at least one amino group and a carbamate compound. The compounds produced by this process are useful as surface coating compositions, foams, and adhesives.

Abstract: A binder which is a graft polymer bearing at least two alkoxysilyl groups of the formula —Si(R1)m(OR2)3-m in which R1 and R2 are independently linear or branched alkyl groups containing 1 to 6 carbon atoms and m is an integer of 0 to 2. The graft polymer has graft branches on a graft base. The graft polymer contains at least 0.5% by weight, based on the graft base, of graft branches.

Abstract: A process for the production of compounds which contain at least one urea group and at least one silyl group. The process involves reacting a compound containing at least one amino group and a carbamate compound. The compounds produced by this process are useful as surface coating compositions, foams and adhesives.

Abstract: A process for the production of compounds which contain at least one urea group and at least one silyl group. The process involves reacting a compound containing at least one amino group and a carbamate compound. The compounds produced by this process are useful as surface coating compositions, foams and adhesives.

Abstract: A composition useful for the production of foam plastics from disposable pressurized containers is provided. The composition comprises at least one polyisocyanate or isocyanate prepolymer, at least one catalyst for the reaction of the isocyanate group with the OH group, at least one blowing agent and at least one foam stabilizer. One day at the latest after application from said disposable pressurized container, the residue of said composition left in the pressurized container has a diisocyanate monomer content of less than 5.0% by weight, based on the residual contents of the emptied container.

Abstract: A binder which is a graft polymer bearing at least two alkoxysilyl groups of the formula

Abstract: Described is an NCO-group-containing polyurethane prepolymer madefrom polyisocanyates and polyols derived from natural oils. The invention is characterized in that the polyol is obtained by transesterification in the presence of basic lithium compounds. Together with a tertiary amine used to accelerate the moisture curing, the storage stability is thus increased considerably. Up to 4.0 mmol of the lithium compound is used per kilogram of polyol, and 0.1 to 2.0% by wt. of the amine, relative to the total weight of the composition, is used as the accelerator. The polyurethane prepolymer is suitable not only for the production of adhesives but also for the production of foamed materials, in particular those dispensed from throw-away pressure vessels.

Abstract: A composition for producing light plaster contains as main constitutive elements particles of plaster in anhydride or hemihydrate form and at least one foaming agent. The composition is characterized in that the foaming agent generates gas after a delay of 1 minute to 24 hours and constitutes 0.1 to 50% by weight of the total dry mixture. Also disclosed is the use of said composition to produce in-situ cellular plastic and low density plaster moldings.

Abstract: The invention relates to isocyanate-terminated polyurethane prepolymers containing a stoichiometric excess of an isocyanate component comprised of one or more aromatic isocyanates containing on average from 2 to 4 isocyanate groups per molecule and a polyol component comprised of an oleochemical polyol prepared by epoxidation of a triglyceride containing olefinic unsaturation and subsequent ring opening with an alcohol. In use, accelerators, flameproofing agents, blowing agents and, optionally, liquefying agents, dyes and/or stabilizers, are included. The oleochemical polyol does not contain any free epoxide groups and is obtained by complete ring opening of epoxidized triglycerides of a fatty acid mixture containing at least partly olefinically unsaturated fatty acids with one or more C.sub.1 -C.sub.12 alcohols and partial conversion by alcoholysis or transesterification of the triglyceride derivatives to alkyl ester polyols containing from 1 to 12 carbon atoms in the alkyl radical.