Abstract: Disclosed are aqueous coating compositions comprising at least one hydroxyl-containing compound (A), at least one compound (B) having isocyanate groups and also having hydrolyzable silane groups, and at least one catalyst (C) wherein the compound (B) has 10 mol % to less than 90 mol % of at least one structural unit (I) —N(X—SiR?x(OR?)3-x)n(X?—SiR?y(OR?)3-y)m??(I) Where R?=hydrogen, alkyl or cycloalkyl, X, X?=linear and/or branched alkylene or cycloalkylene radical having 1 to 20 carbon atoms, R?=alkyl, cycloalkyl, aryl or aralkyl, n=0 to 2, m=0 to 2, m+n=2, and x, y=0 to 2, and more than 10 to 90 mol % of at least one structural unit (II) —Z—(X—SiR?x(OR?)3-x) (II), where Z=—NH—, —NR—, —O— or —S—, where R=alkyl, cycloalkyl, aryl or aralkyl, and x, X, R? and R? have the definition indicated for formula (I).

Abstract: Disclosed are coating compositions comprising at least one hydroxyl-containing compound (A) and at least one isocyanato-containing compound (B), wherein one or more of the constituents of the coating composition comprise between 2.5 and 97.5 mol %, based on the entirety of structural units (I) and (II), of at least one structural unit of the formula (I) —N(X—SiR?x(OR?)3-x)n(X?—SiR?y(OR?)3-y)m??(I) and between 2.5 and 97.5 mol %, based on the entirety of structural units (I) and (II), of at least one structural unit of the formula (II) —Z—(X—SiR?x(OR?)3-x)??(II).

Abstract: The present invention relates to a coating composition comprising (a) at least one hydroxyl-containing compound (A), (b) at least one compound (B) having free and/or blocked isocyanate groups, and (c) at least one catalyst (C) for the crosslinking of silane groups, one or more constituents of the coating composition containing hydrolyzable silane groups, wherein the coating composition contains a water scavenger as further constituent (D).

Abstract: The invention relates to the use of partly silanized compounds based on polyisocyanate as crosslinking agents with heightened refractive index in curable coating compositions, more particularly in clearcoat materials for automotive finishing. The invention likewise relates to a coating composition which comprises these compounds as crosslinking agents, and to the use of the coating composition to produce a coating.

Abstract: Disclosed are aqueous coating compositions comprising at least one hydroxyl-containing compound (A), at least one compound (B) having isocyanate groups and also having hydrolyzable silane groups, and at least one catalyst (C) wherein the compound (B) has 10 mol % to less than 90 mol % of at least one structural unit (I) —N(X—SiR?x(OR?)3-x)n(X?—SiR?y(OR?)3-y)m??(I) Where R?=hydrogen, alkyl or cycloalkyl, X, X?=linear and/or branched alkylene or cycloalkylene radical having 1 to 20 carbon atoms, R?=alkyl, cycloalkyl, aryl or aralkyl, n=0 to 2, m=0 to 2, m+n=2, and x, y=0 to 2, and more than 10 to 90 mol % of at least one structural unit (II) —Z—(X—SiR?x(OR?)3-x) (II), where Z=—NH—, —NR—, —O— or —S—, where R=alkyl, cycloalkyl, aryl or aralkyl, and x, X, R? and R? have the definition indicated for formula (I).

Abstract: Disclosed are coating compositions comprising (a) at least one hydroxyl-containing compound (A), (b) at least one compound (B) having isocyanate groups, and (c) at least one catalyst (D) for the crosslinking of silane groups, said catalyst (D) comprising phosphorus. It is an aspect of the disclosed coating compositions that (i) one or more constituents of the coating composition contain hydrolyzable silane groups and (ii) the coating composition can be finally cured to a coating which has statistically distributed regions of an Si—O—Si network.

Abstract: The invention relates to the use of partly silanized compounds based on polyisocyanate as crosslinking agents with heightened refractive index in curable coating compositions, more particularly in clearcoat materials for automotive finishing. The invention likewise relates to a coating composition which comprises these compounds as crosslinking agents, and to the use of the coating composition to produce a coating.

Abstract: Hydrolysates and/or condensates of epoxy- and silane-functional oligomers and polymers, prepared by hydrolyzing and/or condensing at least one oligomer and/or polymer (A) containing at least one epoxide group (a1) and at least one hydrolyzable silane group (a2); and also (meth)acrylate copolymers (A) containing lateral and/or terminal epoxide groups (a1) and lateral and/or terminal hydrolyzable silane groups (a2), in a molar ratio (a1): (a2) of from 15:1 to 1: 1.5, processes for preparing them, and their use.

Abstract: Disclosed herein is a silane-functional mixture, comprising at least one phosphonic diester (A), at least one diphosphonic diester (A), or at least one phosphonic diester and one diphosphonic diester (A), and at least one compound (B) comprising at least two condensable silane groups.

Abstract: The present invention relates to a coating composition comprising (a) at least one hydroxyl-containing compound (A), (b) at least one compound (B) having free and/or blocked isocyanate groups, and (c) at least one catalyst (C) for the crosslinking of silane groups, ?one or more constituents of the coating composition containing hydrolyzable silane groups, wherein the coating composition contains a water scavenger as further constituent (D).

Abstract: Disclosed are coating compositions comprising (a) at least one hydroxyl-containing compound (A), (b) at least one compound (B) having isocyanate groups, and (c) at least one catalyst (D) for the crosslinking of silane groups, said catalyst (D) comprising phosphorus. It is an aspect of the disclosed coating compositions that (i) one or more constituents of the coating composition contain hydrolyzable silane groups and (ii) the coating composition can be finally cured to a coating which has statistically distributed regions of an Si—O—Si network.

Abstract: Hydrolysates and/or condensates of epoxy- and silane-functional oligomers and polymers, prepared by hydrolyzing and/or condensing at least one oligomer and/or polymer (A) containing at least one epoxide group (a1) and at least one hydrolyzable silane group (a2); and also (meth)acrylate copolymers (A) containing lateral and/or terminal epoxide groups (a1) and lateral and/or terminal hydrolyzable silane groups (a2), in a molar ratio (a1):(a2) of from 1.5:1 to 1:1.5, processes for preparing them, and their use.

Abstract: Disclosed are coating compositions comprising at least one hydroxyl-containing compound (A) and at least one isocyanato-containing compound (B), wherein one or more of the constituents of the coating composition comprise between 2.5 and 97.5 mol %, based on the entirety of structural units (I) and (II), of at least one structural unit of the formula (I) —N(X—SiR?x(OR?)3-x)n(X?—SiR?y(OR?)3-y)m ??(I) and between 2.5 and 97.5 mol %, based on the entirety of structural units (I) and (II), of at least one structural unit of the formula (II) —Z—(X—SiR?x(OR?)3-x) ??(II).

Abstract: Disclosed are coating compositions comprising (a) at least one hydroxyl-containing compound (A), (b) at least one compound (B) having free and/or blocked isocyanate groups, and (c) at least one catalyst (D) for the crosslinking of silane groups, where (i) one or more constituents of the coating composition contain hydrolyzable silane groups and (iii) the coating composition can be finally cured to a coating which has statistically distributed regions of an Si—O—Si network. The finally cured coating obtained from the coating composition has a post-crosslinking index (PCI) of less than 2, wherein (PCI) is defined as the ratio of the storage modulus E?(200) at 200° C. to the minimum of the storage modulus E?(min) at a temperature above the measured glass transition temperature Tg.

Abstract: An aqueous dispersion with a pH of from 2 to 7, comprising (A) at least one swellable polymer or oligomer containing anionic and/or potentially anionic functional groups, (B) surface-modified, cationically stabilized, inorganic nanoparticles of at least one kind, and (C) at least one amphiphile; and its use for producing highly scratch-resistant coatings, moldings, and self-supporting films.

Abstract: Disclosed herein is a silane-functional mixture, comprising at least one phosphonic diester (A), at least one diphosphonic diester (A), or at least one phosphonic diester and one diphosphonic diester (A), and at least one compound (B) comprising at least two condensable silane groups.

Abstract: Transparent coatings with a thickness of at least 30 ?m, a relative elastic resilience to DIN 55676 of at least 70%, and a scratch resistance corresponding to a score of not more than 2 in the steel wool scratch test to DIN 1041 after 10 double strokes; process for producing them, and their use.

Abstract: A method of characterizing surface structures using a chemically curable impression material to take an impression of at least one site of the undamaged surface of an article and of a surface of an article damaged by mechanical and/or chemical exposure and/or by exposure to radiation and/or heat, and/or of a surface of a test specimen mounted on the surface of an article, said test specimen surface being damaged by mechanical and/or chemical exposure and/or by exposure to radiation and/or heat, curing the impression material to produce a negative of the damage pattern, and using image analysis to determine the extent of the surface structures and/or the extent of the surface damage within the damage pattern on the basis of light-microscope pictures of the negative. Use of the method for the preparation, modification and/or development of new and/or existing materials.

Abstract: Autocatalyzed, thermally curable compositions free from external catalysts and comprising condensates of silanes which contain at least one of hydrolyzable atoms and hydrolyzable groups and processes for preparing them, and their use for producing thermally cured compositions.

Abstract: Transparent coatings with a thickness of at least 30 ?m, a relative elastic resilience to DIN 55676 of at least 70%, and a scratch resistance corresponding to a score of not more than 2 in the steel wool scratch test to DIN 1041 after 10 double strokes; process for producing them, and their use.