Abstract: A method of feeding a pulverulent batch material into a furnace in the manufacture of glass. The pulverulent batch material is fed from a first bulk batch feeder at a first batch feed rate, and from a second trim batch feeder at a second trim batch feed rate. The trim batch feed rate is equal to or less than 10% of the total batch feed rate. The use of trim electrodes and trim burners is also disclosed.

Abstract: Feed materials are melted in a first vessel to form a glass melt at a first temperature T1, the glass melt containing at least one fining agent. The molten glass is next cooled to a second temperature T2 less than T1 in a second vessel wherein an oxygen-comprising gas is not actively added (e.g. bubbled) into the melt during the duration of the time the melt is at T2. The molten glass is thereafter heated to a third temperature T3 greater than T1 and subsequently formed into a glass article.

Abstract: Feed materials are melted in a furnace to form a glass melt in a first vessel, transferred through a first refractory metal connecting tube to a second vessel for conditioning, then transferred through a second refractory metal connecting tube to a third vessel where the glass melt is fined. A gas is bubbled into the glass melt through an injection tube disposed in the first connecting tube, optionally in the second connecting tube, and optionally in both connecting tubes. The gas may be used to mix the melt and/or recharge a fining agent with oxygen.

Abstract: A method of feeding a pulverulent batch material into a furnace in the manufacture of glass. The pulverulent batch material is fed from a first bulk batch feeder at a first batch feed rate, and from a second trim batch feeder at a second trim batch feed rate. The trim batch feed rate is equal to or less than 10% of the total batch feed rate. The use of trim electrodes and trim burners is also disclosed.

Abstract: A method of forming a glass melt including heating a glass feed material in a first melting furnace to form a glass melt, flowing the glass melt into a second melting furnace through a refractory metal connecting tube, and further heating the glass melt in the second melting furnace. The refractory metal connecting tube is heated to prevent the molten glass from excessive cooling, and to ensure that the glass melt entering the second melting furnace is equal to or greater than the temperature of the glass melt in the second melting furnace. An apparatus for performing the method is also disclosed.