Abstract: Methods of forming UV-absorbent transparent coatings and transparent substrates coated with the same allow for a relatively lower temperature cross-linkage reaction between a UV-absorbent compound and an epoxy-alkoxysilane. More specifically, UV-absorbent coatings on transparent substrates are formed by prepolymerizing a mixture consisting essentially of a benzophenone, an epoxy alkoxysilane and an organic catalyst at a temperature of between about 40° C. to about 130° C. and for a time sufficient such that between about 30% to about 70% of the epoxy alkoxysilane has been converted to a ring-opened oligomer or polymer. Such prepolymerized mixture may then be hydrolyzed and coated onto the surface of a transparent substrate, and thereafter cured at a temperature of less than about 200° C. for a time sufficient to cross-link the hydrolyzed alkoxysilane with itself and the glass surface.

Abstract: Methods of forming UV-absorbent transparent coatings and transparent substrates coated with the same allow for a relatively lower temperature cross-linkage reaction between a UV-absorbent compound and an epoxy-alkoxysilane. More specifically, UV-absorbent coatings on transparent substrates are formed by prepolymerizing a mixture consisting essentially of a benzophenone, an epoxy alkoxysilane and an organic catalyst at a temperature of between about 40° C. to about 130° C. and for a time sufficient such that between about 30% to about 70% of the epoxy alkoxysilane has been converted to a ring-opened oligomer or polymer. Such prepolymerized mixture may then be hydrolyzed and coated onto the surface of a transparent substrate, and thereafter cured at a temperature of less than about 200° C. for a time sufficient to cross-link the hydrolyzed alkoxysilane with itself and the glass surface.

Abstract: A vacuum insulating glass (IG) unit and method of manufacturing the same. A peripheral or edge seal of a vacuum IG unit is formed utilizing microwave energy in order to enable tempered glass sheets of the IG unit to retain a significant portion of their original temper strength. In certain exemplary embodiments, the edge seal may be formed of solder glass.