Abstract: The present disclosure discloses a preparation method of pressed Scandia-doped dispenser cathode using microwave sintering. Embodiments of the present disclosure include dissolving some nitrates and ammonium metatungstate with deionized water to prepare a homogeneous solution. Precursor powder with uniform size is obtained by spray drying, the precursor powder is decomposed, and two-step reduction may be proceeded to form doped tungsten powder with uniform element distribution. The cathode is prepared by one-time microwave sintering. One-time forming of cathode sintering is realized, and sintering shrinkage and sintering time are reduced significantly. The method has excellent repeatability, and the cathode has a homogeneous structure and excellent emission performance at 950° C.

Abstract: The present disclosure discloses a preparation method of pressed Scandia-doped dispenser cathode using microwave sintering. Embodiments of the present disclosure include dissolving some nitrates and ammonium metatungstate with deionized water to prepare a homogeneous solution. Precursor powder with uniform size is obtained by spray drying, the precursor powder is decomposed, and two-step reduction may be proceeded to form doped tungsten powder with uniform element distribution. The cathode is prepared by one-time microwave sintering. One-time forming of cathode sintering is realized, and sintering shrinkage and sintering time are reduced significantly. The method has excellent repeatability, and the cathode has a homogeneous structure and excellent emission performance at 950° C.

Abstract: In a method of manufacturing a pressed scandate dispenser cathode, firstly, scandium nitrate, barium nitrate, calcium nitrate, aluminum nitrate and ammonium metatungstate (AMT) are dissolved in de-ionized water, respectively, and then mixed with a solution of a cross-link agent such as citric acid and H2O2. After water bathing, the mixed aqueous solution turns into gel, and the powders are obtained after the gel calcination. Secondly, the calcined powders are reduced by hydrogen. Finally, the reduced powders are pressed into shapes and then sintered in the furnace with the atmosphere of hydrogen or by Spark Plasma Sintering (SPS 3.202-MK-V) in vacuum.

Abstract: In a method of manufacturing a pressed scandate dispenser cathode, firstly, scandium nitrate, barium nitrate, calcium nitrate, aluminum nitrate and ammonium metatungstate (AMT) are dissolved in de-ionized water, respectively, and then mixed with a solution of a cross-link agent such as citric acid and H2O2. After water bathing, the mixed aqueous solution turns into gel, and the powders are obtained after the gel calcination. Secondly, the calcined powders are reduced by hydrogen. Finally, the reduced powders are pressed into shapes and then sintered in the furnace with the atmosphere of hydrogen or by Spark Plasma Sintering (SPS 3.202-MK-V) in vacuum.