Abstract: Desirable methods for larger scale silver nanoplate synthesis are described along with methods for applying a noble metal coating onto the silver nanoplates to form coated silver nanoplates with a desirable absorption spectrum. The silver nanoplates are suitable for use in coatings for altering the hue of a transparent film. The hue adjustment can be particularly desirable for transparent conductive films.

Abstract: Fusing nanowire inks are described that can also comprise a hydrophilic polymer binder, such as a cellulose based binder. The fusing nanowire inks can be deposited onto a substrate surface and dried to drive the fusing process. Transparent conductive films can be formed with desirable properties.

Abstract: Metal nanowires, such as silver nanowires coated on a substrate were sintered together to form fused metal nanowire networks that have greatly improved conductivity while maintaining good transparency and low haze. The method of forming such a fused metal nanowire networks are disclosed that involves exposure of metal nanowires to various fusing agents on a short timescale. The resulting sintered network can have a core-shell structure in which metal halide forms the shell. Additionally, effective methods are described for forming patterned structure with areas of sintered metal nanowire network with high conductivity and areas of un-sintered metal nanowires with low conductivity. The corresponding patterned films are also described.

Abstract: Metal nanowires, such as silver nanowires coated on a substrate were sintered together to form fused metal nanowire networks that have greatly improved conductivity while maintaining good transparency and low haze. The method of forming such a fused metal nanowire networks are disclosed that involves exposure of metal nanowires to various fusing agents on a short timescale. The resulting sintered network can have a core-shell structure in which metal halide forms the shell. Additionally, effective methods are described for forming patterned structure with areas of sintered metal nanowire network with high conductivity and areas of un-sintered metal nanowires with low conductivity. The corresponding patterned films are also described.

Abstract: Highly uniform and thin silver nanowires are described having average diameters below 20 nm and a small standard deviation of the diameters. The silver nanowires have a high aspect ratio. The silver nanowires can be characterized by a small number of nanowires having a diameter greater than 18 nm as well as with a blue shifted narrow absorption spectrum in a dilute solution. Methods are described to allow for the synthesis of the narrow uniform silver nanowires. Transparent conductive films formed from the thin, uniform silver nanowires can have very low levels of haze and low values of ?L*, the diffusive luminosity, such that the transparent conductive films can provide little alteration of the appearance of a black background.

Abstract: Highly uniform and thin silver nanowires are described having average diameters below 20 nm and a small standard deviation of the diameters. The silver nanowires have a high aspect ratio. The silver nanowires can be characterized by a small number of nanowires having a diameter greater than 18 nm as well as with a blue shifted narrow absorption spectrum in a dilute solution. Methods are described to allow for the synthesis of the narrow uniform silver nanowires. Transparent conductive films formed from the thin, uniform silver nanowires can have very low levels of haze and low values of ?L*, the diffusive luminosity, such that the transparent conductive films can provide little alteration of the appearance of a black background.

Abstract: Highly uniform and thin silver nanowires are described having average diameters below 20 nm and a small standard deviation of the diameters. The silver nanowires have a high aspect ratio. The silver nanowires can be characterized by a small number of nanowires having a diameter greater than 18 nm as well as with a blue shifted narrow absorption spectrum in a dilute solution. Methods are described to allow for the synthesis of the narrow uniform silver nanowires. Transparent conductive films formed from the thin, uniform silver nanowires can have very low levels of haze and low values of ?L*, the diffusive luminosity, such that the transparent conductive films can provide little alteration of the appearance of a black background.

Abstract: Highly uniform and thin silver nanowires are described having average diameters below 20 nm and a small standard deviation of the diameters. The silver nanowires have a high aspect ratio. The silver nanowires can be characterized by a small number of nanowires having a diameter greater than 18 nm as well as with a blue shifted narrow absorption spectrum in a dilute solution. Methods are described to allow for the synthesis of the narrow uniform silver nanowires. Transparent conductive films formed from the thin, uniform silver nanowires can have very low levels of haze and low values of ?L*, the diffusive luminosity, such that the transparent conductive films can provide little alteration of the appearance of a black background.

Abstract: Highly uniform and thin silver nanowires are described having average diameters below 20 nm and a small standard deviation of the diameters. The silver nanowires have a high aspect ratio. The silver nanowires can be characterized by a small number of nanowires having a diameter greater than 18 nm as well as with a blue shifted narrow absorption spectrum in a dilute solution. Methods are described to allow for the synthesis of the narrow uniform silver nanowires. Transparent conductive films formed from the thin, uniform silver nanowires can have very low levels of haze and low values of ?L*, the diffusive luminosity, such that the transparent conductive films can provide little alteration of the appearance of a black background.

Abstract: Highly uniform and thin silver nanowires are described having average diameters below 20 nm and a small standard deviation of the diameters. The silver nanowires have a high aspect ratio. The silver nanowires can be characterized by a small number of nanowires having a diameter greater than 18 nm as well as with a blue shifted narrow absorption spectrum in a dilute solution. Methods are described to allow for the synthesis of the narrow uniform silver nanowires. Transparent conductive films formed from the thin, uniform silver nanowires can have very low levels of haze and low values of ?L*, the diffusive luminosity, such that the transparent conductive films can provide little alteration of the appearance of a black background.

Abstract: Desirable methods for larger scale silver nanoplate synthesis are described along with methods for applying a noble metal coating onto the silver nanoplates to form coated silver nanoplates with a desirable absorption spectrum. The silver nanoplates are suitable for use in coatings for altering the hue of a transparent film. The hue adjustment can be particularly desirable for transparent conductive films.

Abstract: Fusing nanowire inks are described that can also comprise a hydrophilic polymer binder, such as a cellulose based binder. The fusing nanowire inks can be deposited onto a substrate surface and dried to drive the fusing process. Transparent conductive films can be formed with desirable properties.

Abstract: Desirable methods for larger scale silver nanoplate synthesis are described along with methods for applying a noble metal coating onto the silver nanoplates to form coated silver nanoplates with a desirable absorption spectrum. The silver nanoplates are suitable for use in coatings for altering the hue of a transparent film. The hue adjustment can be particularly desirable for transparent conductive films.

Abstract: A method of forming a transparent electrically conductive film including depositing a dispersion of metal nanowires onto a substrate surface, delivering a solution including a fusing agent in a solvent onto the substrate surface, and drying the substrate surface after depositing the metal nanowires and delivering the fusing agent solution to fuse at least some of the metal nanowires into the transparent electrically conductive film comprising a fused metal nanowire network.

Abstract: Fusing nanowire inks are described that can also comprise a hydrophilic polymer binder, such as a cellulose based binder. The fusing nanowire inks can be deposited onto a substrate surface and dried to drive the fusing process. Transparent conductive films can be formed with desirable properties.

Abstract: Reduction/oxidation reagents have been found to be effective to chemically cure a sparse metal nanowire film into a fused metal nanostructured network through evidently a ripening type process. The resulting fused network can provide desirable low sheet resistances while maintaining good optical transparency. The transparent conductive films can be effectively applied as a single conductive ink or through sequential forming of a metal nanowire film with the subsequent addition of a fusing agent. The fused metal nanowire films can be effectively patterned, and the patterned films can be useful in devices, such as touch sensors.

Abstract: Metal nanowires, such as silver nanowires coated on a substrate were fused together to form fused metal nanowire networks that have greatly improved conductivity while maintaining good transparency. Materials formed form the fused metal nanowire networks described herein can have a transparency to visible light of at least about 85% and a sheet resistance of no more than about 100 Ohms/square or a transparency to visible light of at least about 90% and a sheet resistance of no more than about 250 Ohms/square. The method of forming such a fused metal nanowire networks are disclosed that involves exposure of metal nanowires to various fusing agents on a short timescale. When formed into a film, materials comprising the metal nanowire network demonstrate low sheet resistance while maintaining desirably high levels of optical transparency, making them suitable for transparent electrode formation.

Abstract: Reduction/oxidation reagents have been found to be effective to chemically cure a sparse metal nanowire film into a fused metal nanostructured network through evidently a ripening type process. The resulting fused network can provide desirable low sheet resistances while maintaining good optical transparency. The transparent conductive films can be effectively applied as a single conductive ink or through sequential forming of a metal nanowire film with the subsequent addition of a fusing agent. The fused metal nanowire films can be effectively patterned, and the patterned films can be useful in devices, such as touch sensors.

Abstract: Metal nanowires, such as silver nanowires coated on a substrate were sintered together to form fused metal nanowire networks that have greatly improved conductivity while maintaining good transparency and low haze. The method of forming such a fused metal nanowire networks are disclosed that involves exposure of metal nanowires to various fusing agents on a short timescale. The resulting sintered network can have a core-shell structure in which metal halide forms the shell. Additionally, effective methods are described for forming patterned structure with areas of sintered metal nanowire network with high conductivity and areas of un-sintered metal nanowires with low conductivity. The corresponding patterned films are also described.

Abstract: Metal salt based stabilizers are described that are effective to improve stability of sparse metal conductive films formed with metal nanowires, especially silver nanowires. Specifically, vanadium (+5) compositions can be effectively placed in coatings to provide desirable stabilization under accelerated wear testing conditions. Sparse metal conductive films can comprise fused metal nanostructured networks. Cobalt (+2) compounds can be incorporated as stabilization agents within nanowire inks to provide a high degree of stabilization without significantly interfering with the fusing process.