Abstract: A shear testing system and method of thermo-seepage-mechanical field and engineering disturbance coupling under deep and complex condition are provided. The shear testing system can be used in conjunction with an axial pressure application device to simplify the structure, save costs, and facilitate a triaxial confining pressure—temperature—axial pressure—torsional shear coupled test on a rock specimen. The shear testing system can achieve the following three purposes. First, the shear testing system can convert an axial pressure into a torsional shear force through a transmission mechanism of a power conversion assembly. Second, the shear testing system can apply an axial pressure to the rock specimen fixed between two specimen fixing heads, through a pressure shaft of an axial pressure mechanism. Third, the shear testing system can apply a triaxial confining pressure and a temperature field to the rock specimen.

Abstract: A tantalum powder, a tantalum powder compact, a tantalum powder sintered body, a tantalum anode, an electrolytic capacitor and a preparation method for tantalum powder. The tantalum powder contains boron element, and the tantalum powder has a specific surface area of greater than or equal to 4 m2/g; the ratio of the boron content of the tantalum powder to the specific surface area of the tantalum powder is 2˜16; the boron content is measured in weight ppm, and the specific surface area is measured in m2/g; Powder that can pass through a ?-mesh screen in the tantalum powder accounts for over 85% of the total weight of the tantalum powder, where ?=150˜170; and the tantalum powder with high CV has a low leakage current and dielectric loss, and good moldability.

Abstract: A tantalum powder, a tantalum powder compact, a tantalum powder sintered body, a tantalum anode, an electrolytic capacitor and a preparation method for tantalum powder. The tantalum powder contains boron element, and the tantalum powder has a specific surface area of greater than or equal to 4 m2/g; the ratio of the boron content of the tantalum powder to the specific surface area of the tantalum powder is 2˜16; the boron content is measured in weight ppm, and the specific surface area is measured in m2/g; Powder that can pass through a ?-mesh screen in the tantalum powder accounts for over 85% of the total weight of the tantalum powder, where ?=150˜170; and the tantalum powder with high CV has a low leakage current and dielectric loss, and good moldability.

Abstract: The invention relates to the rare metal smelting field, and particularly, the present invention relates to a tantalum powder for preparing capacitors and a process for preparing the tantalum powder, and to a sintered anode prepared from the tantalum powder. As to the tantalum powder as provided by the invention, its primary tantalum powder has a BET of from 3.0 to 4.5 m2/g. After the secondary agglomeration, the tantalum powder has a large particle size. The tantalum powder has an average Fisher sub-sieve size (FSSS) of 1.2 to 3.0 ?m wherein as measured with a standard sieve mesh, more than 75% of tantalum powder has a +325-mesh, and a particle size distribution D50 of more than 60 ?m, that is, the secondary particle size is high. A resultant capacitor anode prepared by sintering the tantalum powder of the invention at 1200° C. for 20 minutes and then being energized at the voltage of 20 V has the specific capacitance of from 140,000 to 180,000 ?FV/g and the residual current of less than 1.0 nA/?FV.

Abstract: The invention relates to the rare metal smelting field, and particularly, the present invention relates to a tantalum powder for preparing capacitors and a process for preparing the tantalum powder, and to a sintered anode prepared from the tantalum powder. As to the tantalum powder as provided by the invention, its primary tantalum powder has a BET of from 3.0 to 4.5 m2/g. After the secondary agglomeration, the tantalum powder has a large particle size. The tantalum powder has an average Fisher sub-sieve size (FSSS) of 1.2 to 3.0 ?m wherein as measured with a standard sieve mesh, more than 75% of tantalum powder has a +325-mesh, and a particle size distribution D50 of more than 60 ?m, that is, the secondary particle size is high. A resultant capacitor anode prepared by sintering the tantalum powder of the invention at 1200° C. for 20 minutes and then being energized at the voltage of 20 V has the specific capacitance of from 140,000 to 180,000 ?FV/g and the residual current of less than 1.0 nA/?FV.