Abstract: A resin-coated Al—Zn alloy coated steel sheet is excellent in formability, resistance to chromium dissolution, corrosion resistance, alkali resistance, and paintability, and produced by the following method. That is, a silane coupling agent having amino group, chromium ion and at least one alcohol selected from the group consisting of trihydric alcohol and dihydric alcohol having the number of carbon of 2 to 3 are compounded into an acrylic polymer resin emulsion including carboxyl group and glycidyl group, and having an acid value of 10 to 60. A pH of the resultant mixture is adjusted within a range of 7 to 9 to obtain a chromate containing resin composition. The chromate containing resin composition is applied on an Al—Zn alloy coated steel sheet as a substrate, and then dried to obtain a resin film on the substrate. A compounding amount of the silane coupling agent is within a range of 0.5 to 3.0 wt % with respect to a resin solid component of the acrylic polymer resin emulsion.

Abstract: An acidic substitutional plating bath for zinciferous surfaces, particularly zinciferous metal-plated steel sheet, with which sludge production and equipment corrosion are inhibited and which has an improved heavy metal ion deposition efficiency is provided by an aqueous composition that has a pH of 2 to 4.5 and that contains 1.5 to 40 g/L of at least one heavy metal ion selected from nickel, iron, and cobalt; 0.5 to 10 g/L of phosphate ions; 1 to 250 g/L of sulfate ion; and 1 to 20 g/L of organic acid.