Abstract: A method for fabricating a sintered duplex nuclear fuel pellet includes the steps of: preparing a first powder composed of a material selected from the group consisting of UO2 and UO2—Er2O3, and a second powder composed of UO2—Gd2O3 and a sintering additive; producing a duplex compact consisting of an annular outer portion composed of the first powder and a cylindrical inner portion composed of the second powder; and sintering the duplex compact under a reducing gas atmosphere, wherein the sintering additive contains manganese of 0.001% to 2% by weight based on the total weight of the cylindrical inner portion.

Abstract: There is provided a method of producing U3O8 powder having large surface area and small particle size by oxidizing defective UO2 pellets and manufacturing nuclear fuel pellets which are stable in a pore structure and high in density through the use of a mixture comprising UO2 powder and U3O8 powder. The method includes producing an U308 powder having a surface area of at least 1 m2/g by oxidizing defective UO2 pellets at a temperature of 300 to 370? in such a way that a maximum weight increase rate per 1 g of the UO2 pellets is up to 0.06 wt %/min; producing a mixed powder by mixing the U3O8 powder with an UO2 powder by 2 to 15 wt %; producing a compact by compression molding the mixed powder; and sintering the compact in a reducing gas atmosphere at a temperature of 1600 to 1800?. In addition, a small amount of an Al-compound may be added to the oxidized U3O8 powder before the U3O8 powder is mixed with the UO2 powder.

Abstract: A method of manufacturing an alumina-based ceramic includes sintering a powder compact of an iron-containing alumina powder in an atmosphere (N2, 95 N2-5 H2, H2) of a relatively low oxygen partial pressure, and annealing in an atmosphere (80 N2-20 O2, O2) higher in oxygen partial pressure than the sintering atmosphere to provide an alumina-based ceramic with a grain-boundary migration layer on a surface thereof. The resulting undulated grain boundaries on the surface layer suppress and deflect the crack propagation, thereby improving the short-crack toughness. The formation of a grain-boundary migration layer on the surface of an alumina-based ceramic brings about a great improvement in short-crack related properties, including durability and wear resistance.