Abstract: A nonwoven fabric structure according to the present invention is a nonwoven fabric structure comprising a long-fiber nonwoven fabric as a main constituent, wherein the nonwoven fabric structure has a basis weight of 250 to 2000 g/m2, a Frazier permeability of 0 to 20 cc/cm2·s, and an apparent density of 0.5 to 1.3 g/cm3, and therefore has excellent shaping properties and excellent mechanical strength properties.

Abstract: A hybrid cord 1 for rubber reinforcement comprises a strand 2 having higher elastic modulus, made of PBO fiber or the like, which is disposed at the center of the cord, and strands 3 having lower elastic modulus, made of glass fiber or the like, which are disposed therearound. The hybrid cord has enough strength and is excellent in flexural fatigue resistance, adhesion property relative to rubber, and dimensional stability. A rubber product employs this hybrid cord 1 for rubber reinforcement.

Abstract: The present invention relates to polybenzazole fibers or filaments, staple fibers, spun yarns, and woven or knitted fabrics containing in themselves an organic pigment having heat resistance as high as a thermal decomposition temperature of 200° C. or higher, and soluble in a mineral acid and having group(s) of —N? and/or NH— in the molecule, such as any of perinones and/or perylenes, any of phthalocyanines, any of quinacridones, and any of dioxazines, wherein they have a strength retention of 50% or higher when exposed to light from a xenon lamp for 100 hours and having a tensile strength retention of 85% or higher after exposed to an atmosphere of a temperature of 80° C. and a relative humidity of 80% for 700 hours. The polybenzazole fibers or filaments, staple fibers, spun yarns, and woven or knitted fabrics can be used for cords for reinforcing rubber, sheets and rods for reinforcing cement/concrete, composite materials, sail clothes, ropes, knife proof vests and bullet proof vests.

Abstract: The present invention relates to polybenzazole fibers or filaments, staple fibers, spun yarns, and woven or knitted fabrics containing in themselves an organic pigment having heat resistance as high as a thermal decomposition temperature of 200° C. or higher, and soluble in a mineral acid and having group(s) of —N=and/or NH— in the molecule, such as any of perinones and/or perylenes, any of phthalocyanines, any of quinacridones, and any of dioxazines, wherein they have a strength retention of 50% or higher when exposed to light from a xenon lamp for 100 hours and having a tensile strength retention of 85% or higher after exposed to an atmosphere of a temperature of 80° C. and a relative humidity of 80% for 700 hours. The polybenzazole fibers or filaments, staple fibers, spun yarns, and woven or knitted fabrics can be used for cords for reinforcing rubber, sheets and rods for reinforcing cement/concrete, composite materials, sail clothes, ropes, knife proof vests and bullet proof vests.

Abstract: There is provided a polybenzazole fiber or film containing a basic organic compound in the form of a monomer or a condensate, selected from the group consisting of guanidines, triazoles, quinazolines, piperidines, anilines, pyridines, cyanuric acids, and p-phenylenediamine, m-phenylenediamine and a mixture thereof. This fiber has characteristics in that the X-ray meridian diffraction half-width factor is 0.3°/GPa or less, that the elasticity decrement (Er) attributed to change of molecular orientation is 30 GPa or less, and that the breaking strength is 1 GPa or more. This fiber can be used in staple fiber, a spun yarn, a woven or knit fabric, a felt material, a composite material, a cord, a rod, a fibrous sheet, a knife proof vest or a bullet proof vest.

Abstract: A hybrid cord 1 for rubber reinforcement comprises a strand 2 having higher elastic modulus, made of PBO fiber or the like, which is disposed at the center of the cord, and strands 3 having lower elastic modulus, made of glass fiber or the like, which are disposed therearound. The hybrid cord has enough strength and is excellent in flexural fatigue resistance, adhesion property relative to rubber, and dimensional stability. A rubber product employs this hybrid cord 1 for rubber reinforcement.

Abstract: There is provided a cord of twisted polybenzazole fibers, which has a tenacity of 35 g/d or higher and an elastic modulus of 800 g/d or higher. The cord has not only remarkably improved fatigue resistance but also excellent mechanical characteristics at a high level that has not been achieved so far. Therefore, it can attain the weight reduction of composite materials, particularly in the field of reinforced rubber materials, and can also make a great contribution to the energy saving.