Method of electroplating and varying the resistance of a wafer

Abstract

An electroplating apparatus is provided with a metal target and a device for supporting a semiconductor wafer (or other workpiece) in an electroplating solution. The target (anode) may be located relatively far from the wafer surface (cathode) at the beginning of the plating process, until a sufficient amount of metal is plated. When an initial amount of metal is built up on the wafer surface, the target may be moved closer to the wafer for faster processing. The movement of the target may be controlled automatically according to one or more process parameters.

Description

FIELD OF THE INVENTION

The present invention relates to a system for electroplating the surfaces of semiconductor wafers and other workpieces. More particularly, the present invention relates to an electroplating apparatus and method that achieves improved performance with respect to thickness uniformity and rate of metal deposition.

BACKGROUND OF THE INVENTION

It is known to electroplate the surfaces of semiconductor wafers. It has been difficult, however, to obtain an electroplated layer of uniform thickness. It has been especially difficult to achieve the desired thickness uniformity at a high rate of metal deposition. Known systems for electroplating semiconductor products are described in U.S. Pat. No. 5,833,820 (Dubin), U.S. Pat. No. 5,670,034 (Lowery), U.S. Pat. No. 5,472,592 (Lowery), and U.S. Pat. No. 5,421,987 (Tzanavaras).

SUMMARY OF THE INVENTION

The present invention relates to an apparatus for electroplating a semiconductor product. The apparatus includes a support device for supporting the product in an electroplating solution, an electrical circuit for applying an electrical potential across the electroplating solution, and a control device for reducing the current distance to the product through the solution after an initial amount of conductive material is electroplated on the product surface. The semiconductor product may be, for example, a semiconductor wafer or clip. Integrated circuits may be formed in the product if desired.

According to one aspect of the invention, the support device includes conductive contacts. The contacts may be used to connect the product to the electrical circuit.

According to another aspect of the invention, the control device includes a mechanism for moving a metal target (anode) toward the electroplated product. In an alternative embodiment of the invention, the product may be moved toward the anode.

According to another aspect of the invention, a processor is used to operate the control device in response to data correlated to the electroplating process. The input data may be functionally related or correlated to elapsed electroplating time, the resistance of the product in the electroplating solution, the optical characteristics of the product, the surface capacitance of the product, etc.

The present invention also relates to a method of electroplating the surface of a semiconductor wafer. The method includes the steps of using an electrode to electroplate an initial amount of conductive material on the wafer surface, then changing the distance between the electrode and the wafer surface, and then using the electrode to electroplate an additional amount of material on the wafer surface. According to a preferred embodiment of the invention, at the start of the process, while the resistance of the wafer is significant, thickness uniformity is promoted by locating the target far from the wafer. Then, when the wafer resistance is reduced by the initial amount of electrodeposited metal, higher plating efficiency may be obtained by moving the target closer to the wafer.

According to another aspect of the invention, the wafer may be provided with a refractory seed layer. The seed layer contains metal and adheres to the semiconductor wafer material. The resistance of the seed layer is greater than that of the electrodeposited metal.

Thus, according to a preferred embodiment of the invention, a metal target (anode) is located relatively far from the wafer (cathode) at the beginning of the plating process, until a sufficient amount of metal is plated on the wafer surface. Once the metal is built up on the wafer surface, the target is moved closer to the wafer for faster processing.

As explained in more detail below, before the metal is built up on the wafer surface, the high resistance of the seed layer is a significant factor. The electrical potential near the contacts on the edges of the wafer is greater than the potential at the center of the wafer. Consequently, according to the invention, the target and the wafer are separated from each other to increase the resistance of the electroplating solution (the bath). A relatively high bath resistance mutes the significance of the potential difference in the radial direction of the wafer. Metal built up on the wafer surface has less resistance than the seed layer, such that the difference in potential across the surface of the wafer becomes less significant. Eventually, the target can be moved closer to the wafer (to reduce the bath resistance and increase the deposition rate) without impairing plating uniformity.

These and other features and advantages of the invention will become apparent from the following detailed description of preferred embodiments of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view of an electroplating apparatus constructed in accordance with a preferred embodiment of the present invention.

FIG. 2 is another cross-sectional view of the electroplating apparatus of FIG. 1, showing the apparatus at a subsequent stage of operation.

FIG. 3 is a cross-sectional view of an electroplating apparatus constructed in accordance with another preferred embodiment of the present invention.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

Referring now to the drawings, where like reference numerals designate like elements, there is shown in FIG. 1 an electroplating apparatus 10 constructed in accordance with a preferred embodiment of the present invention. The apparatus 10 has a tank 12 containing electroplating solution 14, a wafer support 16 for supporting a wafer 18 in the solution 14, and a metal target (anode) 20. The wafer support 16 may have metal clips 22, 24 for holding the wafer 18 in the desired position. An electrically conductive seed layer 26 may be formed on the wafer surface 28. The seed layer 26 may be electrically grounded through the clips 22, 24 and suitable wires 30.

In operation, voltage is applied to the target 20 by a control device 32. The electrical potential causes current to flow from the target 20, through the solution 14, through the seed layer 26, and through the clips 22, 24 to the grounding wires 30. The electroplating process causes a metal layer 34 (FIG. 2) to form on the seed layer 26. The process may be continued until the metal layer 34 achieves the desired thickness. The electroplated wafer 18 may then be removed from the tank 12 for further processing.

The rate at which metal 34 is deposited on the wafer surface 28 is proportional to the combined resistance of the solution 14 and the seed layer 26, as follows:
I=A/(R₁+R₂),
where I is the metal deposition rate, A is a constant, R₁ is the resistance of the solution 14, and R₂ is the resistance of the wafer 18. The solution resistance R₁ depends on (1) the distance D between the target 20 and the wafer surface 28 and (2) the conductivity of the solution 14. For any particular point on the wafer surface 28, the wafer resistance R₂ depends on (1) the distance from that point to the electrical contacts 22, 24 and (2) the conductivity of the wafer 18.

At the start of the electroplating process (that is, before any metal 34 is formed on the seed layer 26), the wafer resistance R₂ is a significant factor with respect to the deposition rate I. The resistance of the seed layer 26 may be substantial. Consequently, at the start of the process, the value of R₂ may vary substantially as a function of radial position on the wafer 18. That is, the value of R₂ would tend to increase as distance increases from the clips 22, 24. To mute the significance of the wafer resistance R₂ and to thereby improve the thickness uniformity of the initially deposited metal 34, the target 20 initially may be located relatively far from the wafer 18 (FIG. 1). As the conductive metal 34 is formed on the seed layer 26, the wafer resistance R₂ becomes much less significant relative to the solution resistance R₁. After the initial amount of metal 34 is formed on the wafer 18, the target may be moved closer to the wafer 18 to reduce the solution resistance R₁ and to increase the deposition rate I.

The target 20 may be moved by a suitable mechanism 36 controlled by the control device 32. In an alternative embodiment of the invention, shown in FIG. 3, the wafer 18 may be moved closer to the target 20. In another alternative embodiment, (not shown) more than one anode may be employed—one relatively far away from the wafer 18 to form the initial amount of metal on the wafer 18 and the other located relatively close to the wafer 18 to form the rest of the metal layer 34 at a relatively high deposition rate.

The control device 32 (FIG. 2) may be operated by a suitable microprocessor 38 or the like. Signals 40 may be input to the processor 38 representative of elapsed electroplating time, the measured resistance of the wafer 18, the optical characteristics (e.g. reflectivity) of the wafer 18, and/or the surface capacitance of the wafer 18. The input signals 40 may be generated by a suitable input device 42, such as a clock or a suitable measuring device. The resistance of the wafer 18 may be determined by measuring the voltage between the contacts 22, 24. The bulk resistance of the wafer 18 also may be determined off-line, for example, by a four-point probe device (not shown).

The processor 38 may have a look-up table and/or an algorithm that correlates elapsed electroplating time to metal thickness and/or deposition rate for known solutions 14 and target positions. Feedback signals 46 representative of the position of the target 20 (and/or the distance D between the target 20 and the wafer 18) may be provided to the processor 38 by the controller 32. The processor 38 may be programmed to send operating signals 44 to the controller 32 to automatically move the target 20 closer to the wafer 18 when a predetermined amount of metal 34 is formed on the seed layer 26.

The motion of the target 20 toward the wafer 18 may be continuous or gradual, and, the motion may be programmed to optimize plating efficiency while achieving the desired uniformity. In an alternative embodiment of the invention, the target 2Q may be moved in a stepwise fashion toward the wafer 18 at a predetermined time in the process or when a predetermined amount of metal 34 is determined to have been formed on the wafer 18.

In a preferred embodiment of the invention, the target 20 may be located about five centimeters from the wafer surface 28 in the start position (FIG. 1), and about one to two centimeters in the high efficiency plating position (FIG. 2). The present invention should not be limited, however, to the preferred embodiments described and illustrated in detail herein.

The solution 14 may be arranged to deposit copper, platinum, gold or another suitable material on the wafer 18. The seed layer 26 may be formed by a known chemical vapor deposition (CVD) process. The seed layer 26 may be, for example, a refractory and metal composite material that adheres to the wafer surface 28. The metal component of the seed layer 26 may be the same as or different than the plated metal material 34.

If desired, the tank 12 may be provided with a cascade structure (not shown) to ensure that fresh solution 14 is made available to the wafer (cathode) 18. Other suitable means, such as a diffuser or baffle plate, for agitating and flowing the solution 14 against the wafer 18 may be employed, if desired. Although the tank 12 is shown with only one support device 16, the invention may be employed with more than one support device 16 per tank 12. If desired, a number of wafers 18 may be electroplated in the same solution 14 simultaneously. Suitable electrodes 20, 22, 24 may be provided for each wafer 18.

The above descriptions and drawings are only illustrative of preferred embodiments which achieve the features and advantages of the present invention, and it is not intended that the present invention be limited thereto. Any modification of the present invention which comes within the spirit and scope of the following claims is considered part of the present invention.

Claims

1-50. (canceled)

51. A method of electroplating a wafer, said method comprising:

changing the resistance of said wafer while applying an electric potential across a first distance; and

subsequently, applying an electric potential to said wafer across a second distance, said first distance being greater than said second distance.

52. The method of claim 51, wherein the resistance of said wafer is reduced during said step of changing the resistance of said wafer.

53. The method of claim 51, further comprising partially forming at least one layer on said wafer to decrease said resistance of said wafer.

54. The method of claim 53, wherein the step of decreasing the resistance of said wafer further comprises moving said wafer from said first distance to said second distance.

55. A method of controlling the rate at which metal is deposited on a wafer surface, said method comprising:

placing a wafer in an electroplating solution at a predetermined distance from first and second electrical contacts;

forming a metal layer on at least a portion of said wafer, wherein said step of forming a metal layer changes the resistance of the wafer surface; and

subsequently, moving an electrode and/or said wafer in response to the change in said resistance of the wafer's surface.

56. A method of electroplating a surface of a semiconductor wafer, said wafer comprising the steps of:

using an electrode to electroplate an initial amount of material on said surface of said semiconductor wafer such that the variability of the resistance of said surface relative to a radial position of said wafer is reduced; and

subsequently, changing the distance between said electrode and said surface of said semiconductor wafer.

57. A method of varying the resistance of a wafer, said method comprising:

placing said wafer in an electroplating solution at a first distance from a first anode;

providing a second anode at a second distance from said wafer, wherein said first distance is greater than said second distance.

58. The method of claim 57, further comprising applying a first electric potential from said first anode to said wafer, wherein said wafer has a first resistance.

59. The method of claim 58, wherein said step of applying a first electric potential forms an initial amount of metal on said wafer at a first deposition rate changing said first resistance of said wafer to a second resistance.

60. The method of claim 59, wherein subsequently, after said first resistance of said wafer changes to said second resistance, a second electric potential is applied to said wafer from said second anode.

61. The method of claim 60, wherein said step of applying a second electric potential results in an additional amount of metal formed on said wafer.