Molybdenum alloy x-ray targets having uniform grain structure

The invention relates to a process for making a cross-directionally worked molybdenum plate, the process comprising: (a) reducing ammonium molybdate and forming molybdenum metal powder; (b) consolidating a molybdenum component comprised of molybdenum metal powder and an alloying element to a first workpiece, the alloying element being selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof; (c) thermally treating the first workpiece and subjecting the workpiece to thermo-mechanical forces in a first direction, and thereby forming a second workpiece; (d) thermally treating the second workpiece and subjecting the second workpiece to thermo-mechanical forces in a second direction that is different from the first direction; (e) subjecting the thermomechanically treated second workpiece to a recrystallization heat treatment step, and thereby forming a heat-treated crossdirectionally worked workpiece; and (f) subjecting the heat-treated, cross-directionally worked workpiece to a slicing step or a machining step, and thereby forming the cross-directionally worked molybdenum plate. The invention also relates to X-ray targets made from the process.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description
BACKGROUND OF THE INVENTION

X-ray producing devices are extremely valuable tools that are used in a wide variety of applications, both industrial and medical. For example, such equipment is commonly used in areas such as diagnostic and therapeutic radiology; semiconductor manufacture and fabrication; and materials analysis and testing.

While used in a number of different applications, the basic structure and operation of x-ray devices is similar. X-rays are produced when electrons are generated, accelerated to a high speed, and then stopped abruptly. Typically, this entire process takes place within a vacuum formed x-ray generating tube. An x-ray tube ordinarily includes three primary elements: a cathode assembly, which is the source of electrons; an anode, which is axially spaced apart from the cathode and oriented so as to receive electrons emitted by the cathode; and some mechanism for applying a high voltage for driving the electrons from the cathode to the anode. Usually, the cathode assembly is composed of a metallic cathode head having a cathode cup. Disposed within the cathode cup is a filament that, when heated via an electrical current, emits electrons.

The three x-ray tube elements are usually positioned within an evacuated glass tube and connected within an electrical circuit. The electrical circuit is connected so that the voltage generation element can apply a very high voltage (ranging from about ten thousand to in excess of hundreds of thousands of volts) between the anode and the cathode. This high voltage differential causes the electrons that are emitted from the cathode filament to accelerate at a very high velocity towards an x-ray “target” positioned on the anode in the form of a thin stream, or beam. The x-ray target includes a plate with a focal track. When the electrons strike the target surface, the kinetic energy of the striking electron beam is converted to electromagnetic waves of very high frequency, i.e., x-rays. The resulting x-rays emanate from the anode target surface, and are then collimated through a window formed in the x-ray device for penetration into an object, such as an area of a patient's body.

Unfortunately, known processes for making plates have limitations that have prevented artisans from develop a simple effective process for quickly effectively making plates useful in x-ray targets. A particularly limiting disadvantage of known single forging processes, for instance, is that such processes are wasteful and inefficient, making them costly and impractical to implement. Known processes make products have poor uniform grain size. Poor uniformity in grain size interferes with the performance of X-ray anodes. Also, known processes produce anodes having poor temperature properties.

For the foregoing reasons, there is a need to develop a process that produces x-ray targets having uniform properties.

For the foregoing reasons, there is a need to develop a process that produces x-ray targets having uniform properties.

SUMMARY OF THE INVENTION

The invention relates to a process for making a cross-directionally worked molybdenum plate. The plate is preferably used in an X-ray target so that the plate functions as an anode. The process involves (a) reducing ammonium molybdate and forming molybdenum metal powder; (b) consolidating a molybdenum component made of molybdenum metal powder and an alloying element to a first workpiece, the alloying element being selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof; (c) thermally treating the first workpiece and subjecting the workpiece to thermo-mechanical forces in a first direction, and thereby forming a second workpiece; (d) thermally treating the second workpiece and subjecting the second workpiece to thermo-mechanical forces in a second direction that is different from the first direction; (e) subjecting the thermomechanically treated second workpiece to a recrystallization heat treatment step, and thereby forming a heat-treated cross-directionally worked workpiece; and (f) subjecting the heat-treated, cross-directionally worked workpiece to a slicing step or a machining step, and thereby forming the cross-directionally worked molybdenum plate.

In one embodiment, the invention relates to a member made by such a process, in which the member includes a plate and a stem attached to the plate.

In one embodiment, the invention relates to a plate involving a cross-directionally worked molybdenum component selected from the group consisting of (i) a molybdenum component containing molybdenum and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (ii) a molybdenum component of molybdenum, niobium and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (iii) a molybdenum component of molybdenum, tungsten in an amount ranging from about 1 to about 30 wt. % and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof; in which the plate has a radial strength of at least about 60 ksi when the plate is exposed to a temperature of about 1600° C.

In another embodiment, the invention relates to an X-ray target: (a) a plate involving a cross-directionally worked molybdenum component selected from the group consisting of (i) a molybdenum component containing molybdenum and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (ii) a molybdenum component including molybdenum, niobium and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (iii) a molybdenum component including molybdenum, tungsten in an amount ranging from about 1 to about 30 wt. % and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof; in which the plate has a radial strength of at least about 60 ksi when the plate is exposed to a temperature of about 1600° C.; (b) a focal track located on a surface of the plate; and (c) a stem extending from the plate.

DESCRIPTION OF THE FIGURES

These and other features, aspects, and advantages of the present invention will become better understood with reference to the following description and appended claims, where:

FIG. 1 is a schematic showing how a billet/ingot can be extruded in accordance to the invention;

FIGS. 2 (a) and 2 (b) are a schematic showing how the first workpiece can be upset forged in accordance to the invention;

FIG. 3(a) is a view of the second workpiece generated during the upset forging operation with removal of centering disk affected material at A;

FIG. 3(b) is a view of the second workpiece formed from upset forging and a plate that can be sliced from the billet;

FIG. 4 is a side view showing a workpiece being subjected to hammer forging;

FIG. 5 shows the second workpiece formed from a workpiece that is subjected to hammer forging; and

FIG. 6 is a side view of a stem that can be attached to the plate made in accordance to the invention.

DESCRIPTION OF THE INVENTION

The cross-directionally worked molybdenum plate is generally made by a process that (a) reduces ammonium molybdate and forming molybdenum metal powder; (b) consolidates a molybdenum component made of molybdenum metal powder and an alloying element to a first workpiece, the alloying element being selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof; (c) thermally treats the first workpiece and subjecting the workpiece to thermo-mechanical forces in a first direction, and thereby forming a second workpiece; (d) thermally treats the second workpiece and subjecting the second workpiece to thermo-mechanical forces in a second direction that is different from the first direction; (e) subjects the thermomechanically treated second workpiece to a recrystallization heat treatment step, and thereby forming a heat-treated cross-directionally worked workpiece; and (f) subjects the heat-treated, cross-directionally worked workpiece to a slicing step or a machining step, and thereby forms the cross-directionally worked molybdenum plate.

The molybdenum metal powder is made by reducing ammonium molybdate by any suitable process. Generally, this is done through a conventional hydrogen reduction process. The process consolidates a molybdenum component including molybdenum metal powder and an alloying element to a first workpiece. In one embodiment, the molybdenum component is consolidated into the first workpiece by a powder metallurgical technique. Such a process generally involves the steps of cold isostatic pressing of the molybdenum metal powder and any alloying components into a “green” preform of the first workpiece. In another embodiment, the molybdenum component is consolidated into the first workpiece by a melt casting technique. Such a process may involve vacuum arc casting, ebeam melting, or plasma arc casting of an ingot. The alloying element is generally selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof. In one embodiment, the first workpiece further includes niobium in an amount that is less than about 3 wt. %, preferably from about 1 wt % to about 3 wt. %. In another embodiment, the alloying element is present in an amount that is about 1.2 wt. %, or less. In another embodiment, the alloying element is present in an amount ranging from about 1 wt. % to about 1.5 wt. %. In another embodiment, the first workpiece further includes tungsten in an amount ranging from about 1 to about 30wt.%.

The first workpiece is thermally treated and subjected to thermo-mechanical forces in a first direction, so that a second workpiece forms. The thermal treatment of the first workpiece is generally done at a temperature that is at least about 2100° F. (about 1148° C.) and preferably from about 2500° F. (about 1371° C.) to about 3000° F. (1648° C.).

The thermally treated first workpiece is subjected to any thermomechanical treatment, which when practiced in accordance to the invention, produces a plate that is useful in an X-ray target. In one embodiment, the first workpiece is a billet or an ingot and the first workpiece is thermo-mechanically treated by extruding the billet or the ingot to a ratio of reduction (Do:Df) in a cross-sectional area ranging from about 3:1 through about 4:1. More particularly, referring to FIG. 1, the billet/ingot is extruded along length “L” to a suitable ratio of reduction (Do:Df). The billet length can be vary and preferably is from about 14″ (about 36 cm) to about 32″ (about 82 cm).

The second workpiece is then thermally treated and subjected to thermo-mechanical forces in a second direction that is different from the first direction. In one embodiment, the second workpiece is subjected to upset forging. The thermal treatment of the first workpiece is generally done at a temperature that is at least about 2100° F. (about 1148° C.) and preferably from about 2500° F. (about 1371° C.) to about 3000° F. (1648° C.).

The thermally treated second workpiece is subjected to any thermo-mechanical treatment, which when practiced in accordance to the invention, produces a plate that is useful in an X-ray target. In one embodiment, the second workpiece is upset forged by a closed die forging process with a closed die that is dimensioned to form a plate. In another embodiment, the second workpiece is upset forged by an open die (pancake) forging process with an open die that is dimensioned to form a plate. In another embodiment, the closed die is further dimensioned to include a mold for a stem (shown in FIG. 6) so that the plate formed by the process further includes a stem. As such, the invention encompasses a member made by the process of the invention, in which the member has a plate and a stem attached to the plate.

Referring to FIGS. 2(a) and 2(b), FIG. 2(a) shows the first workpiece (10) at the start of the upset forging process in which the workpiece is placed in the press liner (12), between centering disks (14,16) and within an extrusion liner (19), such the moving centering disk (14) applies a main ram tonnage (18) against the stationary centering disk (16).

FIG. 2(b) depicts the end of the forming process in which the workpiece (10) has been subjected to thermo-mechanical forces thereby forming a forged workpiece (or forged billet (20)).

In another embodiment, as shown in FIGS. 4 and 5, the second workpiece is subjected to hammer-forging instead of upset forging. FIG. 4 shows a workpiece being subjected to hammer forging, and FIG. 5 shows the second workpiece formed from the first workpiece. In this embodiment, the ratio of Do cross-sectional area to Df cross-sectional area preferably ranges from 1:2.0 to 1:2.8.

The thermo-mechanically treated second workpiece is subjected to a recrystallization heat treatment step to form a fully annealed, cross-directionally worked workpiece. This is generally done by through conventional heat treatment methods.

The heat treatment is generally done at a temperature that is at least about 2100° F. (about 1148° C.) and preferably from about 2500° F. (about 1371° C.) to about 3000° F. (1648° C.).

The heat-treated, cross-directionally worked workpiece is then subjected to a slicing step or a machining step, and thereby the cross-directionally worked molybdenum plate forms. The material that does not form the billet during upset forging (the “affected material”) is removed by the centering disks (CD), as shown in FIGS. 3(a) and 4. A plate can be sliced from the billet per the orientation shown in the FIG. 3(b) Advantageously, the entire billet is useful for making plates.

The plate made by the process of the invention has any suitable dimension that enables the plate to be used in a sputtering target. In one preferred embodiment, the plate has a diameter ranging from about 6″ (about 15 cm) to about 14″ (about 36 cm) and a thickness/height ranging from about 0.5″ (about 1 cm) to about 2″ (about 5 cm). In another embodiment, the plate has a diameter ranging from about 1″ (about 2.54 cm) to about 14″ (about 36 cm) and a thickness/height ranging from about ¼″ (about 0.6 cm) to about 7″ (about 18 cm).

Advantageously, the plate made in accordance to the invention has high temperature properties. In one embodiment, the plate has a radial strength of at least about 60 ksi when the plate is exposed to a temperature of about 1600° C. When the alloying element includes lanthanum oxide, the plate made by the process of the invention has improved creep resistance, as compared to a plate made without lanthanum oxide. In one embodiment the plate further includes a stem.

As such, in a preferred embodiment of the invention, the invention provides a plate having a cross-directionally worked molybdenum component selected from the group consisting of (i) a molybdenum component containing molybdenum and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (ii) a molybdenum component including molybdenum, niobium and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (iii) a molybdenum component made of molybdenum, tungsten in an amount ranging from about 1 to about 30 wt. % and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof; in which the plate has a radial strength of at least about 60 ksi when the plate is exposed to a temperature of about 1600° C.

In one embodiment, the stem also includes a cross-directionally worked molybdenum component selected from the group consisting of (i) a molybdenum component containing molybdenum and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (ii) a molybdenum component involving molybdenum, niobium and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (iii) a molybdenum component including molybdenum, tungsten in an amount ranging from about 1 to about 30 wt. % and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof, in which the stem also has a strength of at least about 60 ksi when the stem is exposed to a temperature of about 1600° C.

Although the invention has been described in detail in the foregoing for the purpose of illustration, it is to be understood that such detail is solely for that purpose and that variations can be made therein by those skilled in the art without departing from the spirit and scope of the invention except as it may be limited by the claims.

Claims

1. A process for making a cross-directionally worked molybdenum plate, the process comprising:

(a) reducing ammonium molybdate and forming molybdenum metal powder;
(b) consolidating a molybdenum component comprised of molybdenum metal powder and an alloying element to a first workpiece, the alloying element being selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof;
(c) thermally treating the first workpiece and subjecting the workpiece to thermo-mechanical forces in a first direction, and thereby forming a second workpiece;
(d) thermally treating the second workpiece and subjecting the second workpiece to thermo-mechanical forces in a second direction that is different from the first direction;
(e) subjecting the thermomechanically treated second workpiece to a recrystallization heat treatment step, and thereby forming a heat-treated crossdirectionally worked workpiece; and
(f) subjecting the heat-treated, cross-directionally worked workpiece to a slicing step or a machining step, and thereby forming the cross-directionally worked molybdenum plate.

2. The process of claim 1, wherein the first workpiece further comprises niobium in an amount that is less than about 3 wt. %.

3. The process of claim 1, wherein the first workpiece further comprises tungsten in an amount ranging from about 1 to about 30 wt. %.

4. The process of claim 1, wherein the molybdenum component is consolidated into the first workpiece by a powder metallurgical technique.

5. The process of claim 1, wherein the molybdenum component is consolidated into the first workpiece by an arc casting technique.

6. The process of claim 5, wherein the arc casting technique is a vacuum arc casting technique.

7. The process of claim 1, wherein the first workpiece is a billet or an ingot and the first workpiece is thermo-mechanically treated by extruding the billet or the ingot to a ratio of reduction (Do:Df) in a cross-sectional area ranging from about 3:1 through about 4:1.

8. The process of claim 1, wherein in step (d), the second workpiece is subjected to upset forging.

9. The process of claim 8, wherein second workpiece is upset forged by a closed die forging process with a closed die that is dimensioned to form a plate.

10. The process of claim 8, wherein second workpiece is upset forged by an open die forging process with an open die that is dimensioned to form a plate.

11. The process of claim 9, wherein in step (d), the closed die is further dimensioned to include a mold for a stem so that the plate formed by the process in step (e) further comprises a stem.

12. A member made by the process of claim 11, wherein the member comprises a plate and a stem attached to the plate.

13. A plate made from the process of claim 1, wherein the plate is a cross-directionally worked plate having a uniform grain structure.

14. The process of claim 1, wherein the alloying element is present in an amount that is about 1.2 wt. %, or less.

15. The process of claim 1, wherein the alloying element is present in an amount ranging from about 1 wt. % to about 1.5 wt. %.

16. The process of claim 1, wherein the plate has a diameter ranging from about 1″ to about 14″ and a thickness/height ranging from about ¼″ to about 7″.

17. The process of claim 1, wherein the plate made by the process has a radial strength of at least about 60 ksi when the plate is exposed to a temperature of about 1600° C.

18. The process of claim 1, wherein the alloying element comprises lanthanum oxide, and the plate made by the process has improved creep resistance, as compared to a plate made without lanthanum oxide.

19. A plate comprising a cross-directionally worked molybdenum component selected from the group consisting of (i) a molybdenum component containing molybdenum and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (ii) a molybdenum component comprising molybdenum, niobium and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (iii) a molybdenum component comprising molybdenum, tungsten in an amount ranging from about 1 to about 30 wt. % and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof;

wherein the plate has a radial strength of at least about 60 ksi when the plate is exposed to a temperature of about 1600° C.

20. The plate of claim 19, wherein the plate further comprises a stem.

21. An X-ray target comprising:

(a) a plate comprising a cross-directionally worked molybdenum component selected from the group consisting of (i) a molybdenum component containing molybdenum and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (ii) a molybdenum component comprising molybdenum, niobium and an alloying-element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (iii) a molybdenum component comprising molybdenum, tungsten in an amount ranging from about 1 to about 30 wt. % and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof;
wherein the plate has a radial strength of at least about 60 ksi when the plate is exposed to a temperature of about 1600° C.;
(b) a focal track located on a surface of the plate; and
(c) a stem extending from the plate.

22. The target of claim 21, wherein the stem comprises a worked molybdenum component selected from the group consisting of (i) a molybdenum component containing molybdenum and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (ii) a molybdenum component comprising molybdenum, niobium and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof or (iii) a molybdenum component comprising molybdenum, tungsten in an amount ranging from about 1 to about 30 wt. % and an alloying element selected from the group consisting of titanium, zirconium, hafnium, carbon, lanthanum oxide, and combinations thereof,

wherein the stem also has a strength of at least about 60 ksi when the stem is exposed to a temperature of about 1600° C.
Patent History
Publication number: 20060151072
Type: Application
Filed: Apr 15, 2004
Publication Date: Jul 13, 2006
Inventors: James Daily (Marshall, MI), Brad Lemon (Battle Creek, MI), Joseph Hirt (Coldwater, MI), Prabhat Kumar (Framingham, MA), Gerhard Gille (Goslar)
Application Number: 10/553,841
Classifications
Current U.S. Class: 148/514.000; 148/423.000
International Classification: C22C 27/04 (20060101); C22F 1/18 (20060101);