PROTECTIVE SLEEVE FABRICATED WITH HYBRID YARN, HYBRID YARN, AND METHODS OF CONSTRUCTION THEREOF
A hybrid yarn filament used in construction of a sleeve for protecting elongate members against at least one of EMI, RFI or ESD, and methods of construction of the hybrid yarn filament. The hybrid yarn filament has a non-conductive filament and at least one conductive wire filament overlying an outer surface of the non-conductive filament. The hybrid yarn filament is arranged in electrical communication with itself or other hybrid yarn filaments to provide uniform shielding against EMI, RFI, and/or ESD.
This application is a divisional application of U.S. application Ser. No. 11/684,984, filed Mar. 12, 2007, which claims priority to U.S. Provisional Application Ser. No. 60/786,847, filed Mar. 29, 2006, both of which are incorporated herein by reference their entirety.
BACKGROUND OF THE INVENTION1. Technical Field
This invention relates generally to sleeves for protecting elongate members and more particularly to EMI/RFI/ESD shielding yarns and sleeves constructed therefrom.
2. Related Art
It is known that electromagnetic interference (EMI), radio frequency interference (RFI), and electrostatic discharge (ESD) can pose a potential problem to the proper functioning of electronic components caused by interference due to inductive coupling between nearby electrical conductors and propagating electromagnetic waves. Electronic systems generate electromagnetic energy due to the flow of current within a circuit. This electromagnetic energy can adversely affect the performance of surrounding electronic components, whether they are in direct communication within the circuit, or located nearby. For example, electrical currents in conductors associated with an electrical power system in an automobile may induce spurious signals in various electronic components, such as an electronic module. Such interference could downgrade the performance of the electronic module or other components in the vehicle, thereby causing the vehicle to act other than as desired. Similarly, inductive coupling between electrical wiring in relatively close relation to lines carrying data in a computer network or other communication system may have a corrupting effect on the data being transmitted over the network.
The adverse effects of EMI, RFI and ESD can be effectively eliminated by proper shielding and grounding of EMI, RFI and ESD sensitive components. For example, wires carrying control signals which may be subjected to unwanted interference from internally or externally generated EMI, RFI and ESD may be shielded by using a protective sleeve. Protective sleeves can be generally flat or cylindrical, wherein the sleeves are formed from electrically conductive and non-conductive constituents, with the conductive constituents typically being grounded via a drain wire interlaced with the yarns during manufacture of the sleeve. Known conductive constituents take the form of non-conductive fibers or filaments, such as nylon, coated with a conductive metal, such as silver. Other known conductive constituents are fabricated by impregnating a non-conductive resin with micro fibers of metal, such as stainless steel, copper or silver, or with micron size conductive powders of carbon, graphite, nickel, copper or silver, such that the micro fibers and/or powders are bonded in conductive communication.
While such RFI, EMI, and ESD sleeving made with coated conductive yarns is generally effective at eliminating electrical interference, the sleeving can be relatively expensive in manufacture, particularly when expensive coatings, such as silver, are used. In addition, conductive coatings can be worn off, leading to inefficiencies in conductive connections between the conductive constituents, thereby impacting the ability of the sleeving to provide optimal RFI, EMI, and/or ESD protection. Accordingly, RFI, EMI, ESD shielding which is more economical in manufacture, and more efficient in use, and more reliable against wear and having an increased useful life, is desired.
A sleeve manufactured from fabric according to the present invention overcomes or greatly minimizes at least those limitations of the prior art described above, thereby allowing components having potential adversarial effects on one another to function properly, even when near one another.
SUMMARY OF THE INVENTIONOne aspect of the invention includes a conductive hybrid yarn for constructing a fabric sleeve for protecting elongate members against at least one of EMI, RFI and/or ESD. The hybrid yarn has a non-conductive elongate filament, and at least one elongate continuous conductive wire filament overlying and extending outwardly from an outer surface of the non-conductive filament. Accordingly, the wire filament or filaments are able to establish electrical contact with one another. As such, with the wire filaments being continuous wire filaments arranged in electrical communication with one another, the sleeve is provided with optimal conductivity. Thus, effective and uniform EMI, RFI and/or ESD protection is provided to the elongate members housed within the sleeve.
Yet another aspect of the invention includes a method of constructing a conductive hybrid yarn used for forming a sleeve, wherein the sleeve provides protection to elongate members against at least one of EMI, RFI and/or ESD. The method includes providing a non-conductive elongate yarn filament and a continuous conductive wire filament, and then, overlying an outer surface of the non-conductive filament with the continuous conductive wire filament.
Accordingly, sleeves produced at least in part with hybrid yarn in accordance with the invention are useful for shielding elongate members from EMI, RFI and/or ESD, wherein the sleeves can be constructed having any desired shape, whether flat, cylindrical, box shaped, or otherwise. In addition, the sleeves can be made to accommodate virtually any package size by adjusting the fabricated width, height, and length in manufacture, and can be equipped with a variety of closure mechanisms. Further, the sleeves are at least somewhat flexible in 3-D without affecting their protective strength, conductivity, and thus shielding ability, thereby allowing the sleeves to bend, as needed, to best route the elongate members without affecting the EMI, RFI and/or ESD protection provided by the sleeves.
These and other features and advantages will become readily apparent to those skilled in the art in view of the following detailed description of the presently preferred embodiments and best mode, appended claims, and accompanying drawings, in which:
Referring in more detail to the drawings,
As shown in
To facilitate elimination of any unwanted interference, the sleeve 10 is preferably constructed with at least one, and preferably a pair of drain wires 20, 21 (
The non-conductive members 14 are preferably provided as multi-filamentary yarns, which provides the sleeve 10 with softer texture, enhanced drape, and enhanced noise dampening characteristics. Though, as mentioned, monofilaments could be used, if desired for the intended application. Depending on the application, the non-conductive members 14 can be formed from, by way of example and without limitation, polyester, nylon, polypropylene, polyethylene, acrylic, cotton, rayon, and fire retardant (FR) versions of all the aforementioned materials when extremely high temperature ratings are not required. If higher temperature ratings are desired along with FR capabilities, then the non-conductive members 14 could be constructed from, by way of example and without limitation, materials including m-Aramid (sold under names Nomex, Conex, Kermel, for example), p-Aramid (sold under names Kevlar, Twaron, Technora, for example), PEI (sold under name Ultem, for example), PPS, LCP, TPFE, and PEEK. When even higher temperature ratings are desired along with FR capabilities, the non-conductive members can include mineral yarns such as fiberglass, basalt, silica and ceramic, for example.
As mentioned, the continuous conductive wire filaments 16 can be either served with the non-conductive member 14 (
As shown in
The arrangement of the wire filaments 16, and their specific construction, whether having single, double, triple, or more conductive wires 16, used in constructing the hybrid yarn members 12, is selected to best maximize the shielding potential desired. In a woven fabric construction, it is generally preferred that the hybrid yarn members 12 traversing the warp direction of the sleeve 10 have at least two or more conductive wire filaments 16, as best shown in
An additional consideration given in the construction of the hybrid yarn members 12 is to best provide the hybrid yarns 12 in both the fill and warp directions with a generally similar denier. As such, given that each of the fill hybrid yarn members 12 preferably have a single conductive wire filament 16, the associated underlying nonconductive filaments 14 preferably have a larger denier in comparison to the nonconductive filaments 14 used in the warp hybrid yarn members 12, which, as mentioned, preferably have two or more conductive wire filaments 16. By providing the fill and warp hybrid yarns 12 with approximately the same denier, the resulting sleeve fabric has a smoother appearance and feel, thereby enhancing the abrasion resistance of the resulting sleeve 10.
For example, a fill hybrid yarn member 12 could have a single continuous strand of stainless steel wire filament 16, between about 20-100 μm in diameter, and in one example, about 50 μm in diameter (this diameter of wire in our examples equates to about 140 denier), twisted or served about non-conductive PET multifilament 14 of about 1100 denier, thereby resulting in the hybrid yarn member 12 being about 1240 denier, and a warp hybrid yarn member 12 could have two continuous strands of stainless steel wire filament 16, between about 20-100 μm in diameter, and in this example, about 50 μm in diameter, twisted or served about non-conductive PET multifilament 14 of about 970 denier, thereby resulting in the hybrid yarn member 12 being about 1250 denier. Thus, the resulting deniers of the warp and fill hybrid yarns 12 being approximately equal to one another.
In another example, a hybrid fill yarn member 12 could have a single continuous strand of stainless steel wire filament 16, between about 20-100 μm in diameter, and in this example, about 50 μm in diameter, twisted or served about non-conductive PET multifilament 14 of about 1100 denier, thereby resulting in the hybrid yarn member 12 being about 1240 denier, and a hybrid warp yarn member 12 could have three continuous strands of stainless steel wire filament 16, between about 20-100 μm in diameter, and in this example, about 50 μm in diameter, twisted or served about PET non-conductive multifilament 14 of about 830 denier, thereby resulting in the hybrid yarn member 12 being about 1250 denier. So, again, the resulting fill and warp direction hybrid yarns 12 are approximately the same denier.
In yet another example, a hybrid fill yarn member 12 could have a single continuous strand of stainless steel wire filament 16, between about 20-100 μm in diameter, and in this example, about 35 μm in diameter (this diameter of wire in our examples equates to about 70 denier), twisted or served about non-conductive m-Aramid multifilament 14 of about 530 denier, thereby resulting in the hybrid yarn member 12 being about 600 denier, and a hybrid warp yarn member 12 could have two continuous ends, between about 20-100 μm in diameter, and in this example, about 35 μm in diameter, of stainless steel wire filament 16 twisted or served about m-Aramid non-conductive multifilament 14 of about 460 denier, thereby resulting in the hybrid yarn member 12 being about 600 denier. Therefore, the resulting fill and warp hybrid yarns 12 are again approximately the same denier.
In yet a further example, a hybrid fill yarn member 12 could have a single continuous strand of stainless steel wire filament 16, between about 20-100 μm in diameter, and in this example, about 35 μm in diameter, twisted or served about non-conductive m-Aramid multifilament 14 of about 530 denier, thereby resulting in the hybrid yarn member 12 being about 600 denier, and a hybrid warp yarn member 12 could have three continuous strands of stainless steel wire filament 16, between about 20-100 μm in diameter, and in this example, about 35 μm in diameter, twisted or served about m-Aramid non-conductive multifilament 14 of about 390 denier, thereby resulting in the hybrid yarn member 12 being about 600 denier. Again, the resulting deniers of the hybrid fill and warp yarns 12 are approximately the same.
Accordingly, as the examples above demonstrate, without limitation, numerous constructions and arrangements of fill and warp hybrid yarns 12 are possible. Further, as mentioned, more warp conductive wire filaments 16 could be used to effectively increase the conductivity of the conductive hybrid yarn members 12, thereby enhancing the EMI, RFI and/or ESD shielding effectiveness, with the resulting deniers of the warp and fill hybrid yarn members 12 preferably remaining approximately equal to one another.
Another aspect of the invention includes a method of constructing the fabric sleeves 10 described above for protecting elongate members against at least one of EMI, RFI and/or ESD. The method includes providing at least one or more hybrid yarn members 12 each having a non-conductive elongate filament 14 and at least one elongate continuous conductive wire filament 16 overlying an outer surface of the non-conductive filament 14. Next, interlacing the hybrid yarn members 12 with one another, such as in warp and fill directions, for example to form a fabric, wherein the wire filaments 16 extending along the warp direction are brought into direct conductive electrical communication with the wire filaments 16 extending along the fill direction. It should be understood that the fabric sleeve can be constructed via weaving, knitting, crochet knitting, or braiding techniques. As such, it should be recognized that the method includes additional steps, as necessary, to arrive at the specific sleeve constructions described above, and desired. It should be further understood that if the resulting sleeve is braided, crocheted, or knitted using other than warp or weft knitting forms of knitting, that the use of warp and weft directions above may not apply to the sleeves constructed from these methods of construction. Regardless, it is to be understood that the hybrid yarn members 12 can be interlaced using virtually any textile construction method to form a protective sleeve In addition, the sleeves 10 constructed from the hybrid yarn members 12 can be constructed to conform to a multitude of widths, heights and lengths and configurations for use in a variety of applications.
Obviously, many modifications and variations of the present invention are possible in light of the above teachings. It is, therefore, to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described.
Claims
1. A conductive hybrid yarn filament for constructing a fabric sleeve for protecting elongate members against at least one of EMI, RFI or ESD, said hybrid yarn filament comprising:
- an elongate non-conductive filament; and
- an elongate continuous conductive wire filament overlying an outer surface of said non-conductive filament.
2. The conductive hybrid yarn filament of claim 1 wherein said wire filament is twisted with said non-conductive filament.
3. The conductive hybrid yarn filament of claim 1 wherein said wire filament is served about said non-conductive filament.
4. The conductive hybrid yarn filament of claim 1 further comprising at least two of said continuous conductive wire filaments overlying an outer surface of said non-conductive filament.
5. The conductive hybrid yarn filament of claim 4 wherein said at least two of said wire filaments are arranged in opposite helical direction to one another.
6. The conductive hybrid yarn filament of claim 1 further comprising at least three elongate continuous conductive wire filaments overlying an outer surface of said non-conductive filament.
7. The conductive hybrid yarn filament of claim 6 wherein at least one of said three wire filaments is arranged in an opposite helical direction to the remaining wire filaments.
8. The conductive hybrid yarn filament of claim 6 wherein at least one of said three wire filaments is arranged having a different helical angle than the remaining wire filaments.
9. The conductive hybrid yarn filament of claim 1 wherein said non-conductive filament is formed as a multifilament.
10. The conductive hybrid yarn filament of claim 1 wherein said non-conductive filament is formed from a heat-settable polymeric material.
11. The conductive hybrid yarn filament of claim 1 wherein said non-conductive filament includes a separate monofilament and a multifilament.
12. A method of constructing a flexible conductive hybrid yarn filament for a fabric sleeve, the method comprising the steps of:
- providing a non-conductive elongate filament;
- providing an elongate conductive wire filament; and
- overlying an outer surface of said non-conductive filament with said conductive wire filament.
13. The method of claim 12 further including twisting said conductive filament with said non-conductive filament so that said conductive filament and said non-conductive filament extend in helical paths.
14. The method of claim 12 further including serving said conductive filament about said non-conductive filament so that said conductive filament extends in a helical path and said non-conductive filament extends in a generally straight path.
15. The method of claim 12 further including providing at least two of said wire filaments and overlying the outer surface of said non-conductive filament with said at least two wire filaments.
16. The method of claim 15 further including arranging said at least two wire filaments in opposite helical directions to one another.
17. The method of claim 12 further including providing at least three wire filaments and overlying the outer surface of said non-conductive filament with said at least three wire filaments.
18. The method of claim 17 further including arranging at least one of said at least three wire filaments in an opposite helical direction to the remaining wire filaments.
19. The method of claim 17 further including arranging at least one of said at least three wire filaments having a different helical angle than the remaining wire filaments.
20. The method of claim 12 further including providing said non-conductive filament as a multifilament.
21. The method of claim 12 further including providing said non-conductive filament as a heat-settable polymeric material.
22. The method of claim 12 further including providing said non-conductive filament as a monofilament and a multifilament.
Type: Application
Filed: Jul 10, 2009
Publication Date: Nov 5, 2009
Inventor: Ming-Ming Chen (West Chester, PA)
Application Number: 12/500,812
International Classification: H05K 9/00 (20060101); D02G 3/36 (20060101);