FUEL ADDITIVE

Abstract

A composition for use as a fuel additive for a hydrocarbon fuel. The additive is in the form of particles of one or more complex oxides having a nominal composition as set out in formula (1): AxB1−yMyOn   (1) Wherein A is selected from one or more group III elements including the lanthanide elements or one or more divalent or monovalent cations; B is selected from one or more elements with atomic number 22 to 24, 40 to 42 and 72 to 75; M is selected from one or more elements with atomic number 25 to 30; x is defined as a number where 0<x<1 ; and y is defined as a number where 0<y<0.5.

Description

FIELD OF THE INVENTION

The present invention relates to a fuel additive. In a more specific embodiment, the present invention relates to a fuel additive that is effective even with high sulphur content in the fuel.

BACKGROUND TO THE INVENTION

Cerium oxide has been extensively used as a component in the catalyst of three-way converters for the elimination of toxic exhaust emissions in automobiles. The cerium oxide contained within the catalyst can act as a chemically active component, working as an oxygen store by the release of oxygen in the presence of reductive gases, and removal of oxygen by interaction with oxidised species. Cerium oxide may store and release oxygen by the following processes:

2CeO_2<=>Ce2O₃+0.5 O₂

Cerium oxide has also been used as an additive to be added to fuels. In such uses, the cerium oxide provides a catalytic effect that has been found to reduce the emission of toxic exhaust gases. Addition of cerium oxide has also been found to improve the combustion of the fuel as it passes through an internal combustion engine. Due to improved combustion, far less pollutants are formed. For example, when cerium oxide is used as a fuel additive for diesel engines, an increase in efficiency of approx 10% has been achieved and a reduction in emissions of NOx gases of up to 65% has also been measured [ref Oxonica Website].

In order to keep the cerium oxide particles suspended in the fuel, it is usually necessary to prepare a colloidal dispersion of the cerium oxide particles which requires the cerium oxide particles to be very fine, for example, sub-micron particles having a maximum particle size of up to 300 nm.

There have been several documents described in the patent literature that discuss the use of cerium oxide, or modified forms of cerium oxide, as fuel additives.

WO 03/040270 (the entire contents of which are herein incorporated by cross reference) describes a fuel additive which comprises a particle of cerium oxide which has been doped with a divalent or trivalent metal or metalloid which is a rare earth metal, a transition metal, including a noble metal, or a metal of groups IIA, IIIB, VB, or VIB of the periodic table, and a polar or non-polar organic solvent.

The doped cerium oxide particle described in this patent application may have the following formula:

Ce_1−xM_xO₂,

where M is the metal or metalloid as described above, particularly Rh, Cu, Ag, Au, Pd, Pt, Sb, Se, Fe, Ga, Mg, Mn, Cr, Be, B, Co, V and Ca as well as Pr, Sm, and Gd and x has a value of up to 0.3. Copper is particularly preferred.

Alternatively, the doped cerium oxide particle may have following formula:

[(CeO₂)_1−n(REO_y)_n]_1−kM′_k

where M′ is said metal or metalloid other than a rare earth, RE is a rare earth, y is one or 1.5 and each of n and k has a value up to 0.5, preferably up to 0.3.

Copper is the preferred metal or metalloid.

WO 2004/065529 (the entire contents of which are herein incorporated by cross reference) has a similar disclosure, but it relates to a method of improving the efficiency of a fuel for an internal combustion engine which comprises adding to the fuel prior to the introduction of the fuel to a vehicle or other apparatus comprising an internal combustion engine, cerium oxide and/or doped cerium oxide and, optionally, one or more fuel additives.

The doped cerium oxides that may be used in the invention described in this patent application will have the formula Ce_1−xM_xO₂, where M is the metal or metalloid as described above, particularly Rh, Cu, Ag, Au, Pd, Pt, Sb, Se, Fe, Ti, Ga, Mg, Mn, Cr, Be, B, Co, V and Ca as well as Pr, Sm, and Gd.

The fuel additive may be provided in the form of a product to be mixed with the fuel at the point of dispensing the fuel (for example, at a service station). In these embodiments, the fuel additive may be poured directly into the fuel tank of a motor vehicle prior to or just after filling up the fuel tank of the motor vehicle. Alternatively, the fuel additive may be mixed with the fuel in the fuel storage tanks at the service station. However, it is even more desirable to have the fuel additive mixed with the fuel at the point of production of the fuel, which is typically at an oil refinery.

In our copending international patent application number PCT/AU 2007/000488, the entire contents of which are herein incorporated by cross reference, we describe a material that is useful as an exhaust emissions catalyst.

The present applicant does not concede that the prior art discussed here in forms part of the common general knowledge in Australia or elsewhere.

Throughout this specification, the word “comprising” and its grammatical equivalents shall be taken to have an inclusive meaning unless the context of use clearly indicates otherwise.

BRIEF DESCRIPTION OF THE INVENTION

The present inventors have now discovered that the catalytic material described in our copending international patent application number PCT/AU 2007/000488 is also especially useful as a fuel additive.

In a first aspect, the present invention provides a fuel additive comprising one or more complex oxides having a nominal composition as set out in formula (1):

A_xB_1−yM_yO_n   (1)

wherein

A is selected from one or more group III elements including the lanthanide elements or one or more divalent or monovalent cations;

B is selected from one or more elements with atomic number 22 to 24, 40 to 42 and 72 to 75;

M is selected from one or more elements with atomic number 25 to 30;

x is defined as a number where 0<x≦1;

y is defined as a number where 0≦y<0.5.

In one embodiment, the one or more complex oxides have a general composition as set out in formula (2):

A_xA′_wB_1−yM_yO_n   (2)

wherein

A is one or more group III elements including the lanthanide elements;

A′ is one or more divalent or monovalent cations;

w is defined as a number where 0≦w≦1;

0.5<x+w<1 and

B, M, P, x and y are as set out in formula (1).

In a preferred embodiment A is selected from La, Ce, Sm and Nd, A′ is selected from Sr, Ba, and Ca, B is selected from Ti, V, W and Mo, and M is selected from Cu and Ni.

In a more preferred embodiment A is La and/or Ce, A′ is Sr, B is Ti, and M is Cu and/or Ni. In this embodiment, the complex oxide has the general formula as set out in formula (3):

(La,Ce)_xSr_wTi_1−yM_yO_n   (3)

In a further preferred embodiment at least one of the complex oxide phases is a perovskite with a general formula (4):

A_xA′_wB_1−yM_yO₃   (4)

and more preferably of formula (5):

(La,Ce)_xSr_wTi_1−yM_yO₃   (5)

where the terms in (4) and (5) are as defined in (1) and (2) above.

The perovskite component of the formula may suitably exhibit substantially homogenous and phase-pure composition.

The complex oxide material may have an initial surface area greater than approximately 15 m²/g, preferably greater than approximately 20 m²/g, more preferably greater than approximately 30 m²/g, and a surface area after aging for 2 hours at 1000° C. in air greater than approximately 5 m²/g, preferably greater than approximately 10 m²/g, more preferably greater than approximately 15 m²/g.

The complex oxide material may generally exhibit an average grain size of approximately 2 nm to approximately 150 nm, preferably approximately 2 to 100 nm and has pores ranging in size from approximately 7 nm to approximately 250 nm, more preferably approximately 10 nm to approximately 150 nm. However, the average grain and pore size of the complex oxide materials may vary, depending on the specific complex oxide selected.

More preferably, the complex oxide material may exhibit a substantially disperse pore size range.

The complex oxide material of the invention may be formed by mixing precursors of the elements described above in the general formula (1) followed by appropriate heat treatment to form the target phases. The precursors may be of any suitable form such as salts, oxides or metals of the elements used. The precursor mixture may be in the form of a mixture of solids, a solution or a combination of solids and solutions. The solutions may be formed by dissolving salts in a solvent such as water, acid, alkali or alcohols. The salts may be but are not limited to nitrates, carbonates, oxides, acetates, oxalates, and chlorides. Organometallic form of elements such as alkoxides may also be used.

Solid dispersions may also be used as suitable precursor materials.

Various methods of mixing precursors to produce the complex oxide may include but are not limited to techniques such as, mixing and grinding, co-precipitation, thermal evaporation and spray pyrolysis, polymer and surfactant complex mixing and sol gel. Where necessary, the final phase composition is achieved by thermal processing following mixing. The heating step may be carried out using any suitable heating apparatus and may include but are not limited to, hot plates or other heated substrates such as used in spray pyrolysis, ovens stationary table furnaces, rotary furnaces, induction furnaces, fluid bed furnace, bath furnace, flash furnace, vacuum furnace, rotary dryers, spray dryers, spin-flash dryers.

In a preferred embodiment a homogeneous complex oxide is formed by the method outlined in U.S. Pat. No. 6,752,679, “Production of Fine-Grained Particles”, the entire contents of which are herein incorporated by cross reference.

In a further preferred embodiment a homogeneous complex oxide is formed, has nano-sized grains in the size range indicated and nano-scale pores in the size range indicated by using the method outlined in U.S. Pat. No. 6,752,679 and U.S. Patent application 60/538867, the entire contents of which are herein incorporated by cross reference.

In a more preferred embodiment a homogeneous complex oxide is formed, has nano-sized grains in the size range indicated and nano-scale pores in the size range indicated and uses an aqueous colloidal dispersion of nano-scale particles as one of the precursor elements by using the method outlined in U.S. Pat. No. 6,752,679 and U.S. Patent application 60/538867 and U.S. patent application 60/582905, the entire contents of which are herein incorporated by cross reference.

In some embodiments, the complex oxide is provided in the form of dispersed particles. The dispersed particles may have a particle size of up to 300 nm. The dispersed particles may be formed by forming the complex oxide material in accordance with the methods as described in U.S. Pat. No. 6,752,679 or U.S. Patent application 60/538867 or U.S. patent application 60/582905 and subsequently grinding the complex oxide material to form dispersed particles. It has been surprisingly found that the agglomerated particles that are formed by the methods described in our U.S. Pat. No. 6,752,679 and U.S. Patent application 60/538867 and U.S. patent application 60/582905 are only loosely agglomerated and can be easily ground or milled to form dispersed particles.

In some embodiments of the present invention, A is Ce, B is Ti, y is zero, z is zero and n is 4. This results in a complex oxide having the formula CeTiO₄.

The fuel additive in accordance with the present invention may further comprise one or more solvents. The one or more solvents may comprise an organic solvent. The one or more solvents may comprise a non-polar organic solvent or a polar organic solvent. The person skilled in the art will readily understand that a number of solvents may be used in the fuel additive in accordance with the present invention. The solvents are soluble in the fuel and act as a carrier or delivery agent for the particles of metal oxide.

A number of other components may also be added to the fuel additive. These other components may include:

• • Detergents,
  • dehazers
  • anti-foaming agents
  • ignition improvers
  • anti-rust agents or corrosion inhibitors
  • deodorants
  • antioxidants
  • metal deactivatorss
  • lubricating agents
  • dyes.

The skilled person will readily understand the nature and sources of supply of the above additives. The skilled person will also understand how much of each additive may be added to the fuel additive.

The present inventors have found that complex metal oxides, as described with reference to the first aspect of the present invention, are particularly suitable for use as fuel additives in accordance with the present invention. In particular, the fuel additives of the present invention show enhanced resistance to deactivation or poisoning by sulphur. The present inventors believe that, due to the enhanced resistance to deactivation or poisoning by sulphur, the fuel additive in accordance with the present invention is particularly suitable for adding to fuels, such as diesel fuel, at the manufacturing facility of the fuels (which will typically be an oil refinery) or at bulk storage facilities for the fuel. Previous efforts to incorporate cerium oxide-based fuel additives into fuels at an oil refinery or bulk storage facilities have resulted in inadequate performance of the fuel additive, which the present inventors have postulated is due to deactivation or poisoning by sulphur. In this regard, it will be understood that even modern high quality diesel fuels contain up to 50 ppm sulphur.

In a second aspect, the present invention provides a method for making a fuel additive comprising the steps of forming a complex metal oxide of formula (1) as described above, the complex metal oxide being formed in the form of the agglomerated particles having nano sized grains, breaking the agglomerates of particles to form dispersed particles of complex metal oxide having a particle size of less than 300 nm and adding said particles to a fuel.

In some embodiments, the method may further comprise the step of mixing the particles with one or more solvents. The solvent(s) are soluble in the fuel and act as a carrier or delivery agent for the particles of metal oxide. Other additives, as described above, may also be added to the fuel additive.

In a third aspect, the present invention provides a fuel additive comprising a solvent and one or more complex oxides having a nominal composition as set out in formula (1) above. The solvent(s) are soluble in the fuel and act as a carrier or delivery agent for the particles of metal oxide. The fuel additive may be in the form of a suspension or a dispersion of particles of the complex oxide in the solvent.

In a further aspect, the present invention also provides a fuel comprising a hydrocarbon-based fuel and a fuel additive as described herein. The hydrocarbon-based fuel may be diesel fuel.

As will be understood by the person skilled in the art, in all of the chemical formulae given in this specification, n will be a value that essentially balances the oxygen with the metallic species in the formulae.

EXAMPLES

Material Preparation

Example 1

A complex metal oxide of the nominal formula La_0.8Sr_0.2TiO₃ plus 10 w % CeO₂ was produced as follows.

A solution containing all the required elements except Ti was made by mixing 45 mls of water, 10 g of nitric acid, 46.29 g of lanthanum nitrate hexahydrate, 5.66 g of strontium nitrate and 7.57 g of cerium nitrate hexahydrate.

10.67 g of Titanium-based nano-particles were added to the solution and stirred at a temperature of 50° C. until the particles were dispersed and a clear solution was formed.

The solution was then added to 16 g of carbon black and mixed with a high-speed stirrer. The resulting mixture was added to 70 g of anionic surfactant and again mixed with a high-speed stirrer.

The final mixture was heat treated slowly to 650° C. and then treated at 800° C. for 2 hrs and a further 2 hrs at 1000° C. XRD analysis showed that the perovskite phase LaSr₀₅Ti₂O₆ and (Ce,La)₂Ti₂O₇ were the main types of phases present in Example 1.

Example 2

A complex metal oxide of nominal formula La_0.5Sr_0.25Ti_0.96Ni_0.040_n plus 10 w % CeO₂ was produced using a similar method to Example 1. XRD analysis showed that the perovskite phase LaSr_0.5Ti₂O₆ and (Ce,La)₂Ti₂O₇ were the main types of phases present.

Example 3

A complex metal oxide of nominal formula La_0.8Sr_0.2Ti_0.96Ni_0.04O_n plus 10 w % CeO₂ was produced using a similar method to Example 1. XRD analysis showed that the perovskite phase LaSr_0.5Ti₂O₆ and (Ce,La)₂Ti₂O₇ were the main types of phases present.

Example 4

A complex metal oxide of nominal formula La_0.8Sr_0.2Ti_0.93Ni_0.04Cu_0.03O_n plus 10 w % CeO₂ was produced using a similar method to Example 1. XRD analysis showed that the perovskite phase LaSr_0.5Ti₂O₆ and (Ce,La)₂Ti₂O₇ were the main types of phases present.

Example 5

A complex metal oxide of nominal formula LaTi_0.96Ni_0.04O_n plus 10 w % CeO₂ was produced using a similar method to Example 1. XRD analysis showed that the perovskite phase LaSr_0.5Ti₂O₆ and (Ce,La)₂Ti₂O₇ were the main types of phases present.

Example 6

A complex metal oxide of nominal formula CeTi_0.96Ni_0.04O_n was produced using a similar method to Example 1. XRD analysis showed that the (Ce,La)₂Ti₂O₇ phase was the main type of phase present.

Claims

1-18. (canceled)

19. A composition for use as a fuel additive comprising particles of one or more complex oxides having a nominal composition as set out in formula (1): wherein

AxB1−yMyOn   (1)

A is selected from one or more group III elements including the lanthanide elements or one or more divalent or monovalent cations;

B is selected from one or more elements with atomic number 22 to 24, 40 to 42 and 72 to 75;

M is selected from one or more elements with atomic number 25 to 30;

x is defined as a number where 0<x<1; and

y is defined as a number where 0<y<0.5.

20. A composition for use as a fuel additive as claimed in claim 19, wherein the one or more complex oxides have a nominal composition as set out in formula (2): wherein

AxA′wB1−yMyOn   (2)

A is one or more group III elements including the lanthanide elements;

A′ is one or more divalent or monovalent cations;

w is defined as a number where 0≦w≦1; and

0.5<x+w<1.

21. A composition for use as a fuel additive as claimed in claim 20 wherein A is selected from La, Ce, Sm and Nd, A′ is selected from Sr, Ba, and Ca, B is selected from Ti, V, W and Mo, and M is selected from Cu and Ni.

22. A composition for use as a fuel additive as claimed in claim 21 wherein A is La or Ce, A′ is Sr, B is Ti, and M is Cu or Ni and the complex oxide has the general formula as set out in formula (3):

(La,Ce)xSrwTi1−yMyOn   (3).

23. A composition for use as a fuel additive as claimed in claim 20 wherein at least one complex oxide phase is a perovskite with a general formula (4):

AxA′wB1−yMyO3   (4).

24. A composition for use as a fuel additive as claimed in claim 23 wherein at least one complex oxide phase is a perovskite with a general formula (5):

(La,Ce)xSrwTi1−yMyO3   (5).

25. A composition for use as a fuel additive as claimed in claim 19 wherein the complex oxide material has an initial surface area greater than approximately 15 m2/g, and a surface area after aging for 2 hours at 1000° C. in air greater than approximately 5 m2/g.

26. A composition for use as a fuel additive as claimed in claim 25 wherein the complex oxide material has an initial surface area greater than approximately 30 m2/g, and a surface area after aging for 2 hours at 1000° C. in air greater than approximately 15 m2/g.

27. A composition for use as a fuel additive as claimed in claim 19 wherein the complex oxide material exhibits an average grain size of approximately 2 nm to approximately 150 nm and has pores ranging in size from approximately 7 nm to approximately 250 nm.

28. A composition for use as a fuel additive as claimed in any one of the preceding claims wherein A is Ce, B is Ti, y is zero, and n is 4 and the complex oxide has the formula CeTiO4.

29. A composition comprising a fuel and the fuel additive of claim 19.

30. A composition as claimed in claim 29 wherein the fuel comprises a hydrocarbon-based fuel.

31. A composition as claimed in claim 29 wherein the fuel is a diesel fuel.

32. A composition as claimed in claim 29 further comprising one or more solvents that are soluble in the fuel and that form a suspension or dispersion of the oxide particles in the solvent which then acts as a carrier or delivery agent for the fuel additive.

33. A composition as claimed in claim 29 further comprising other components or additives selected from the group comprising detergents, dehazers, anti-foaming agents, ignition improvers, anti-rust agents or corrosion inhibitors, deodorants, antioxidants, metal deactivators, lubricating agents, dyes or mixtures of two or more thereof.

34. A method for making a fuel additive comprising one or more complex oxides having a nominal composition as set out in formula (1): wherein which method comprises:

AxB1−yMyOn   (1)

A is selected from one or more group III elements including the lanthanide elements or one or more divalent or monovalent cations;

B is selected from one or more elements with atomic number 22 to 24, 40 to 42 and 72 to 75;

M is selected from one or more elements with atomic number 25 to 30;

x is defined as a number where 0<x<1; and

y is defined as a number where 0<y<0.5,

forming a complex metal oxide of formula (1), the complex metal oxide being formed in the form of the agglomerated particles having nano sized grains;

breaking the agglomerates of particles to form dispersed particles of complex metal oxide having a particle size of less than 300 nm; and

adding the particles to a fuel.

35. A method as claimed in claim 34 which further comprises mixing the particles with one or more solvents that are soluble in the fuel and that form a suspension or dispersion of the oxide particles in the solvent which then acts as a carrier or delivery agent for the fuel additive.

36. A method as claimed in claim 35 wherein the fuel comprises a hydrocarbon-based fuel.

37. A method as claimed in claim 35 wherein the fuel is a diesel fuel.

38. A method for making a fuel comprising refining oil at a refinery to form a fuel and adding a composition for use as a fuel additive as claimed in of claim 19 to the fuel at the refinery or at a bulk storage facility for the fuel.

39. A method as claimed in claim 39 wherein the fuel comprises a hydrocarbon-based fuel.

40. A method as claimed in claim 40 wherein the fuel is a diesel fuel.