MACHINING OF AN ARTICLE
A method of forming a profile of a leading edge on an aerofoil having a leading edge extending along an axis and providing a fluid jet that has a Gaussian energy distribution profile. The jet is traversed along a path that substantially follows the axis, the maximum energy of the fluid jet being directed to a location offset from the axis.
Latest ROLLS-ROYCE PLC Patents:
The invention relates to machining of an article and particularly to machining a leading edge on an aerofoil using a fluid jet.
BACKGROUND OF INVENTIONAerofoils are used to turn flow of a fluid and have a leading edge, a trailing edge and suction and pressure flanks that connect the leading and trailing edges. The leading edge is generally narrow and its profile can affect the flutter margin of the aerofoil.
Leading edges generally approximate a circle but more recently in the field of gas turbines the leading edge can have an elliptical profile. The aerofoil leading edges can become worn or damaged in use and may require re-dressing back to an aerodynamically acceptable profile.
Since every aerofoil will wear at a different rate it is difficult to automatically determine machine tool paths and the leading edges are therefore typically hand dressed. Hand dressing requires skilled workers and has a risk of manual handling or machining errors that could cause the blade to be irreparable.
In one application GB 2454187 there is described a machining apparatus that uses a water jet to machine a leading edge. The water jet is fixed in an axiostatic direction and by suitable simultaneous axial rotational and transverse manipulation of the aerofoil within the fixed and static water jet stream it is possible to machine the leading edge to a desired profile. The water jet is used to roughen out the shape the prior to the application of a chip machining or grinding process.
It is an object of the present invention to seek to provide an improved method of water jet machining a leading edge that does not require additional chip machining or grinding.
STATEMENTS OF INVENTIONAccording to a first aspect of the invention there is provided a method of forming a curved profile of an edge on an aerofoil, the curve having a profile axis, the method comprising: providing an aerofoil having an edge extending along a length; providing a fluid jet that has a Gaussian energy distribution profile; traversing the fluid jet along a path that substantially follows the length of the edge to machine an edge having the curved profile, the maximum energy of the fluid jet being directed to a location offset from the profile axis.
Preferably the Gaussian energy distribution is a normal energy distribution profile. Advantageously, the shape of the leading edge may be determined by the Gaussian energy distribution of the fluid jet and the energy distribution. The energy distribution may be selected to provide an elliptical leading edge with a ratio of the major axis to the minor axis of 3:1 or more. Preferably the ratio of the major axis to the minor axis is 4:1 to 7:1 or more.
The offset may be constant along the length of the axis so that the jet follows a linear traverse.
The leading edge profile preferably transitions into a suction flank at one side and into a pressure surface at the other side and follows an elliptical curve, the maximum width of the leading edge in a direction perpendicular to the axis being equal to the minor axis of the ellipse, the offset being greater than or equal to the minor radius of the ellipse. The ratio of the major axis to the minor axis may be between 1:1 and 8:1. The profile axis may be the major axis of the ellipse.
The fluid jet may comprise abrasive particles, which may be in grit or bead form and selected from the group comprising glass, garnet, or aluminium, silicon or boron based ceramics or a mixture thereof. Particle sizes in the range between 4 and 600 microns may be used.
Preferably the abrasive particles are added to the fluid jet at a rate of between 15 and 55 g/min, and more preferably between 15 and 35 g/min.
The fluid jet may have an axis that is directed towards a tangent of the ellipse. The angle of the fluid jet axis to the major axis of the ellipse may be constant as the fluid jet traverses along the path.
The traverse of the fluid jet may be followed by traverse of a second fluid jet at a higher or lower traverse speed and a lower stand-off to the leading edge. The maximum energy of the second fluid jet is preferably directed to a location that has a greater offset from the axis than the first fluid jet.
The fluid may be water. The edge may be a leading edge.
The fluid projected from the aperture is preferably water as the fluid is cheap and readily available; but it will be appreciated that other fluids may also be used. For the rest of the specification the term “water” will be used, but this term should be understood to include any other suitable fluid. The water may, and preferably, include hard particles that assist in the machining process.
An orifice 5 of 0.004 inches (0.1016 mm) is used to eject jet from a water pressure of around 55,000 psi supplied from a pressurised source 7. Using a 0.004″ (0.1016 mm) orifice in the nozzle results in a fine and narrow jet with a very concentrated energy distribution towards the centre and which follows the Gaussian normal distribution 8a shown in
The focussing tube traditionally has a circular cross-section and is straight along its axis but may have other shapes e.g. elliptical, semi-circular, semi-elliptical, rectangular, square, diamond or triangular. The shape of the tube along the axis may also be selected to vary along the axis to have a converging, diverging, converging-diverging, or venture profile, as appropriate. The actual shape chosen is dependent on cost, manufacturability and the desired energy distribution of the jet.
Due to the relatively high fall off in the energy of the jet from its centre point the stand-off distance between the leading edge and the orifice is selected to be around 20 mm though appropriate results were achieved with stand-offs of between 5 mm and 40 mm. The stand-off to the test piece is a major influential factor and is tightly controlled by the position of the clamp and thereby the jet head. At shorter distances it is possible to create a sharper profile but the risk of impaired operation is increased due to an atomisation of the jet that can cause abrasive particles in a particle hopper to agglomerate and block the orifice.
For the material of the leading edge of an aerofoil, typically titanium or some other metal, the presence of an abrasive is desirable to ensure that machining occurs at an appropriate rate. Suitable materials for the abrasive, in grit or bead form, are glass, garnet, or aluminium, silicon or boron based ceramics or a mixture thereof supplied from a hopper 9. Other hard particles may also be used. The particles must be suitable sized to pass through the orifice or focussing tube without blocking. Accordingly, particle sizes in the range between 4 and 600 microns are preferred.
The concentration of the particles in the water jet can be varied dynamically, but more preferably is a static value selected before the start of machining. The feedrate is measured in grams per minute and can be between 0 g/m and 60 g/min. However, for the provision of a leading edge with an elliptical profile a low feed rate of between 15 and 55 g/min is preferred. A feed rate between 15 g/min and 35 g/min gave an ellipse with an ratio ellipse between 2:1 and 8:1. It was found to be possible to produce a high ratio ellipse between 6:1 and 8:1 at a feed rate of around 17 g/min.
A leading edge profile of an aerofoil is depicted in
The leading edge 12 of the aerofoil connects the suction surface 14 to the pressure surface 16. The leading edge is circular or elliptical in form with the ellipse having a major axis A-A and a minor axis B-B. Where the leading edge is circular the major and minor axes are in the ratio 1:1. High ratio ellipses in the range 4:1 to 8:1 for the major:minor axis ratios are desirable. The minor axis signifies the point of transition between the leading edge and the suction and pressure surfaces.
Advantageously, the offset allows the natural Gaussian energy distribution to at least partially control the machined leading edge profile. An offset of equal to or greater than the radius of the minor axis is of particular importance where a minimum of wear at the leading edge point is required.
To form the leading edge the aerofoil is aligned to the nozzle and the water jet started. The jet is then moved to bring it into contact with the aerofoil leading edge and then traversed in the direction of arrow D along the length of the leading edge. In some circumstances it is desirable to repeat the traverse in a multipass approach. The position of the nozzle relative to the leading edge can be varied between the passes to increase the window of possible profiles that may be produced. The positional variation may include one or more of the stand-off distance or the offset.
The traverse speed along the leading edge is between 0.005″ (0.127 mm) per minute to up to 10″ (254 mm) per minute. It has been found that the traverse speed has little effect on the elliptical ratio, but a slower traverse speed marginally increases the ratio. Increasing the head speed reduces the machining time but also removes less material an increase in abrasive concentration may be used to offset the reduction in material removal.
Further machining time savings may be achieved by simultaneously machining both sides of the leading edge as shown in
As discussed above a loss of material at the leading edge point can be reduced by increasing the offset in the x-direction which ensures that, due to the Gaussian energy distribution of the jet, the jet has relatively low energy at the point of impact with the leading edge point.
Further modifications to the machining process can be made by angling the jet relative to the leading edge. The angle may be towards the tangent of the leading edge profile as shown in
By angling the jet relative to the leading edge it is possible to reduce the spray caused by atomisation of the jet against the leading edge and this reduces the risk of blocking caused by agglomeration of the particles.
Claims
1. A method of forming a curved profile of an edge on an aerofoil, the curve having a profile axis, the method comprising:
- providing an aerofoil having an edge extending along a length;
- providing a fluid jet that has a Gaussian energy distribution profile;
- traversing the fluid jet along a path that substantially follows the length of the edge to machine an edge having the curved profile, the maximum energy of the fluid jet being directed to a location offset from the profile axis.
2. A method according to claim 1, wherein the Gaussian energy distribution is a normal energy distribution profile.
3. A method according to claim 1, wherein the offset is constant along the length of edge.
4. A method according to claim 1, wherein the edge profile transitions into a suction flank at one side and into a pressure surface at the other side and follows an elliptical curve, and wherein the maximum width of the leading edge in a direction perpendicular to the major axis or the ellipse being equal to the length of the minor axis of the ellipse, the offset being greater than or equal to the minor radius of the ellipse.
5. A method according to claim 4, wherein the length of the major axis has a ratio of between 1:1 and 8:1 of the length of the minor axis.
6. A method according to claim 4, wherein the profile axis is the major axis of the ellipse.
7. A method according to claim 1, wherein the shape of the edge is determined by the Gaussian energy distribution of the fluid jet and the energy distribution is selected to provide an elliptical leading edge with a ratio of the major axis to the minor axis of 3:1 or more.
8. A method according to claim 1, wherein the fluid jet comprises abrasive particles.
9. A method according to claim 8, wherein the abrasive particles are added to the fluid jet at a rate of between 15 and 55 g/min.
10. A method according to claim 9, wherein the abrasive particles are added to the fluid jet at a rate of between 15 and 35 g/min.
11. A method according to claim 4, wherein the fluid jet has an axis that is directed towards a tangent of the ellipse.
12. A method according to claim 11, wherein the angle of the fluid jet axis to the major axis of the ellipse is constant as the fluid jet traverses along the path.
13. A method according to claim 1, wherein the traverse of the fluid jet is followed by traverse of a second fluid jet.
14. A method according to claim 13, wherein the maximum energy of the second fluid jet is directed to a location that has a greater offset from the axis than the first fluid jet.
15. A method according to claim 1, wherein the edge is a leading edge.
16. A method of forming a curved profile of a leading edge on an aerofoil, the curve having a profile axis, the method comprising:
- providing an aerofoil having an edge extending along a length;
- providing a fluid jet that has a Gaussian energy distribution profile;
- traversing the fluid jet along a path that substantially follows the length of the edge to machine an edge having the curved profile, the maximum energy of the fluid jet being directed to a location offset from the profile axis, the fluid jet having an axis that is directed towards a tangent of the ellipse.
17. A method according to claim 16, wherein the edge profile transitions into a suction flank at one side and into a pressure surface at the other side and follows an elliptical curve, and wherein the maximum width of the leading edge in a direction perpendicular to the major axis or the ellipse being equal to the length of the minor axis of the ellipse, the offset being greater than or equal to the minor radius of the ellipse.
18. A method according to claim 16, wherein the angle of the fluid jet axis to the major axis of the ellipse is constant as the fluid jet traverses along the path.
19. A method according to claim 6, wherein the traverse of the fluid jet is followed by traverse of a second fluid jet.
20. A method according to claim 19, wherein the maximum energy of the second fluid jet is directed to a location that has a greater offset from the axis than the first fluid jet.
Type: Application
Filed: Aug 21, 2013
Publication Date: Mar 27, 2014
Applicant: ROLLS-ROYCE PLC (London)
Inventors: Ka Him CHAN (Derby), Matthew James WILSON (Narberth), Zhidong XI (Shanxi Province), Haolei HU (Shanghai)
Application Number: 13/972,548