METAL-ORGANIC MATERIALS FOR C02 ADSORPTION

Embodiments of the present disclosure provide for metal-organic materials (MOMs), systems that exhibit permanent porosity and using hydrophobic MOMs to separate components in a gas, methods of separating CO2 from a gas, and the like.

Skip to: Description  ·  Claims  · Patent History  ·  Patent History
Description
CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation in-part application of U.S. Utility Application entitled “METAL-ORGANIC MATERIALS (MOMS) FOR CO2 ADSORPTION AND METHODS OF USING MOMS” and Ser. No. 13/800,690, filed Mar. 13, 2013; which claims priority to and the benefit of U.S. Provisional Application entitled “METAL ORGANIC COMPOSITION, FOR CARBON DIOXIDE SEPARATION AND CAPTURE,” having Ser. No. 61/682,017, filed on Aug. 10, 2012, and also claims priority to U.S. provisional application entitled “METAL ORGANIC COMPOSITION, FOR CARBON DIOXIDE SEPARATION AND CAPTURE,” having Ser. No. 61/723,533, filed on Nov. 7, 2012, each of which are entirely incorporated herein by reference.

This application claims priority to U.S. provisional application entitled “AIR CAPTURE, TRACES AND LOW CONCENTRATION CO2 REMOVAL IN CONFINED SPACES AND CLOSED BREATHING LOOPS USING PHYSICAL ABSORBENTS FROM THE CLASS METAL ORGANIC FRAMEWORK (MOFS),” having Ser. No. 61/941,151, filed on Feb. 18, 2014, which is entirely incorporated herein by reference.

BACKGROUND

Metal-organic framework (MOF) materials that exhibit permanent porosity have received extensive interest due to their potential applications for gas storage or capture. However, many of the currently used MOFs have limitations, and thus, other types of MOFs having desired characteristics are needed to be used in certain applications.

SUMMARY

Embodiments of the present disclosure provide for metal-organic materials (MOMs), systems using MOMs to separate components in a gas, methods of separating CO2 from a gas, and the like.

An embodiment of the method of capturing CO2 in a gas, among others, includes: exposing the gas to a metal-organic material (MOM), wherein the gas includes CO2 at a concentration in the gas of about 5% or less; and capturing the CO2 in the MOM.

An embodiment of the system for capturing CO2 in a gas mixture, among others, includes: a first structure including a metal-organic material (MOM), wherein the gas includes CO2 at a concentration in the gas of about 5% or less; and a second structure for introducing the gas to the first structure, wherein CO2 is removed from the gas after the exposure to the MOM to form a modified gas (CO2 free), wherein the second structure flows the modified gas away from the first structure.

An embodiment of the method of separating components in a gas mixture, among others, includes: exposing a gas including a CO2 and a second component to a metal-organic material (MOM), wherein the MOM has a greater relative affinity (kinetic and thermodynamic) for the CO2 over a second component, wherein the CO2 is at a concentration in the gas of about 5% or less; and capturing the first component in the MOM.

An embodiment of the system for separating components in a gas, among others, includes: a first structure including a metal-organic material (MOM), wherein the gas includes CO2 and a second component, wherein the MOM has a greater relative affinity for CO2 over the second component, wherein the CO2 is at a concentration in the gas of about 5% or less; and a second structure for introducing the gas to the first structure, wherein CO2 is removed from the gas after the exposure to the MOM to form a modified gas, wherein the second structure flows the modified gas away from the first structure.

An embodiment of the composition, among others, includes: a MOM comprising [Cu(pyr)2(SiF6)]n, wherein n is 1 to 100,000,000, and wherein the MOM has a pore size of about 3.5 Å.

BRIEF DESCRIPTION OF THE DRAWINGS

Many aspects of the disclosed devices and methods can be better understood with reference to the following drawings. The components in the drawings are not necessarily to scale, emphasis instead being placed upon clearly illustrating the relevant principles. Moreover, in the drawings, like reference numerals designate corresponding parts throughout the several views.

FIG. 1 is a schematic that illustrates the ability of pore size tuning in the channel structures of SIFSIX-2-Cu-i, SIFSIX-3-Zn or/and SIFSIX-3-Cu. In particular, a) SIFSIX-2-Cu-i; pores size 5.15 Å, BET apparent surface area (N2 adsorption) 735 m2g−1; b) SIFSIX-3-Zn; pores size 3.84 Å, BET apparent surface area (determined from CO2 adsorption isotherm) 250 m2g−1; and c) SIFSIX-3-Cu; pores size 3.3.5 Å, BET apparent surface area (determined from CO2 adsorption isotherm) 300 m2g−1. Color code: Dipyridilacetylene (dpa, thick light grey polyhedral), pyrazine (pyz, medium grey polyhedral), Zn, Cu (darker grey polyhedral), Si (light grey spheres), F (light grey spheres). All guest molecules are omitted for clarity. Note that the grey net represents the interpenetrated net in SIFSIX-Cu-2-i.

FIG. 2A illustrates the variable temperature adsorption isotherms of CO2 for SIFSIX-Cu-3). FIG. 2B illustrates the pore size distribution from CO2 sorption isotherms at 77 K for SIFSIX-Cu-3.

FIG. 3A illustrates the CO2 volumetric uptake on SIFSIX-Cu-3, SIFSIX-Zn-3 and SIFSIX-Cu-2-i as compared to Mg-MOF-74. FIG. 3B illustrates the isosteric heats of adsorption at low coverage for SIFSIX-Cu-3, SIFSIX-Zn-3 and SIFSIX-Cu-2-i.

FIG. 4A illustrates the column breakthrough test of CO2/N2:1000 ppm/99.99% for SIFSIX-Cu-3, SIFSIX-Zn-3 in dry condition. FIG. 4B illustrates the column breakthrough test of CO2/N2:1000 ppm/99.99% for SIFSIX-Cu-3 in dry as well as at 74% RH.

FIG. 5 illustrates a comparison of PXRD diagrams of SIFSIX-3-Cu with other SIFSIX-pyz MOFs (λCu=1.5406 nm).

FIG. 6 illustrates a Lebail fit for SIFSIX-3-Cu (λCu=1.5406 nm).

FIG. 7 illustrates a comparison of calculated and experimental PXRD diagrams for SIFSIX-3-Cu (λCu=1.5406 nm).

FIG. 8 illustrates a comparison of the metal environment in SIFSIX based MOFs through the metal-nitrogen (top) and metal-fluorine (bottom) distances.

FIG. 9 illustrates variable temperature adsorption isotherms for SIFISX-2-Cu-i.

FIG. 10 illustrates variable temperature adsorption isotherms for SIFISX-3-Zn.

FIG. 11 illustrates a CO2 adsorption isotherms at very low pressures up to 0.25 bar (250 mbar) for SIFSIX-Cu-3, SIFSIX-Zn-3 and SIFSIX-Cu-2-i as compared to Mg-MOF-74[J. Am. Chem. Soc. 130, 10870-10871 (2008)] and UTSA-16 [Nat. Commun. 3:954 doi: 10.1038/ncomms1956 (2012)].

FIG. 12 illustrates competitive adsorption kinetics of CO2/N2:10/90 gas mixture as compared to the kinetics of adsorption of pure CO2 at 1 bar and 298 K.

FIG. 13 illustrates a column breakthrough test of CO2/N2:1000 ppm/99.99% for SIFSIX-Zn-3 in dry as well as at 74% RH.

FIG. 14 illustrates adsorption isotherms of CO2, N2 and O2 on Sif6-3-cu at 298 K.

FIG. 15 illustrates a comparison of experimental PXRD diagrams for SIFSIX-3-Cu (λCu=1.5406 nm) as prepared (bottom curve), after high pressure experiments and exposed to air (middle curve) and after break-through experiments under dry and humid conditions (top curve).

DISCUSSION

Before the present disclosure is described in greater detail, it is to be understood that this disclosure is not limited to particular embodiments described, as such may, of course, vary. It is also to be understood that the terminology used herein is for the purpose of describing particular embodiments only, and is not intended to be limiting, since the scope of the present disclosure will be limited only by the appended claims.

Where a range of values is provided, it is understood that each intervening value, to the tenth of the unit of the lower limit (unless the context clearly dictates otherwise), between the upper and lower limit of that range, and any other stated or intervening value in that stated range, is encompassed within the disclosure. The upper and lower limits of these smaller ranges may independently be included in the smaller ranges and are also encompassed within the disclosure, subject to any specifically excluded limit in the stated range. Where the stated range includes one or both of the limits, ranges excluding either or both of those included limits are also included in the disclosure.

Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. Although any methods and materials similar or equivalent to those described herein can also be used in the practice or testing of the present disclosure, the preferred methods and materials are now described.

As will be apparent to those of skill in the art upon reading this disclosure, each of the individual embodiments described and illustrated herein has discrete components and features which may be readily separated from or combined with the features of any of the other several embodiments without departing from the scope or spirit of the present disclosure. Any recited method can be carried out in the order of events recited or in any other order that is logically possible.

Embodiments of the present disclosure will employ, unless otherwise indicated, techniques of chemistry, organic chemistry, organometallic chemistry, coordination chemistry and the like, which are within the skill of the art. Such techniques are explained fully in the literature.

The following examples are put forth so as to provide those of ordinary skill in the art with a complete disclosure and description of how to perform the methods and use the compositions and compounds disclosed and claimed herein. Efforts have been made to ensure accuracy with respect to numbers (e.g., amounts, temperature, etc.), but some errors and deviations should be accounted for. Unless indicated otherwise, parts are parts by weight, temperature is in ° C., and pressure is at or near atmospheric. Standard temperature and pressure are defined as 25° C. and 1 atmosphere.

Before the embodiments of the present disclosure are described in detail, it is to be understood that, unless otherwise indicated, the present disclosure is not limited to particular materials, reagents, reaction materials, manufacturing processes, or the like, as such can vary. It is also to be understood that the terminology used herein is for purposes of describing particular embodiments only, and is not intended to be limiting. It is also possible in the present disclosure that steps can be executed in different sequence where this is logically possible.

It must be noted that, as used in the specification and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a support” includes a plurality of supports. In this specification and in the claims that follow, reference will be made to a number of terms that shall be defined to have the following meanings unless a contrary intention is apparent.

General Discussion:

Embodiments of the present disclosure provide for metal-organic materials (MOMs), systems using MOMs to separate components in a gas, methods of separating CO2 from a gas, and the like. In an embodiment, the MOM can be used to remove or separate CO2 in a gas at a variety of concentrations. In a particular embodiment, the MOM can be used to remove or separate trace levels of CO2 in a gas (e.g., CO2 at a concentration of about 5% or less in a gas) with high specificity and removal capacity, which can be advantageous in a number of industries.

The growing interest in combatting the greenhouse gas effect triggered a rising interest in the Direct Air Capture (CAD) as a viable option to reduce greenhouse gases emissions in uniform way. Although more challenging than post-combustion capture, embodiments of the present disclosure can be used in CAD since embodiments of the MOM have suitable uptake, kinetics, energetics and CO2 selectivity, which enables removal or separation of trace levels of CO2 concentration.

Removal of trace amounts of CO2 from air for industrial purposes is important particularly for pre-purification of air when atmospheric air is used during the separation of nitrogen and oxygen. In a particular system, prior to air separation using cryogenic distillation or pressure swing adsorption (PSA), air must be CO2 free to avoid (i) blockage of heat-exchange equipment due to frozen CO2 during the liquefaction process and (ii) adsorbents (e.g., zeolites) contamination used for oxygen production by PSA. MOMs of the present disclosure can be used to remove CO2 for air separation using cryogenic distillation or PSA.

In another application, alkaline Fuel Cells (AFCs) require the oxygen and hydrogen used as feedstock to be CO2 free as trace amounts of CO2 (300 ppm) degrade the electrolyte in AFCs. In this regard, MOMs of the present disclosure can be used in AFCs to remove CO2.

Efficient removal of CO2 at low concentrations is also vital for the proper operation of breathing systems in confined spaces such as submarines, planes, aerospace shuttles, and the like. In particular, in long-term space flight and submarine missions, CO2 must be removed from the air and recycled because resupply opportunities are less frequent or non-existent. Humans require oxygen, and in return emit carbon dioxide. An average crew member requires approximately 0.84 kg of oxygen and emits approximately 1 kg of carbon dioxide. As a result, the ability to continuously purify the exhaled air (with a CO2 concentration of 5% or less) can lead to an optimal recycling and considerable reduction in fresh air supply in closed, confined spaces such as space shuttles, planes and submarines. In this regard, embodiments of the MOMs can be used in breathing systems to manage CO2 concentration.

Efficient CO2 removal is also of importance in mining and rescue missions and diving. Thus, embodiments of the MOMs can be used to manage CO2 concentration.

CO2 removal is also a concern in medical applications such as anesthesia machines. The use of anesthesia machines is a growing clinical trend throughout the world, driven by the need to reduce cost and improve patient care. CO2 removal in anesthesia machines is particularly important in semi- or closed rebreathing systems in which the rebreathing fraction is at least 50% of the exhaled gas volume is directed back to the patient after proper carbon dioxide removal in the next exhalation. Current solutions are costly, have limited recyclability, and have large disposal costs associated with them, while MOMs of the present disclosure can be used to remove and manage CO2 concentration levels in anesthesia machines and in some situations can have a lifetime that is 10,000 times greater than current standards.

In an embodiment, the MOM can be porous and can be a three dimensional net so that molecules can be disposed (e.g., captured) within (e.g., pores or cavities) the MOM to the exclusion of other molecules. In an embodiment, the MOM combines sorption thermodynamics and kinetics to achieve advantageous results. Embodiments of the present disclosure describe MOMs that have no unsaturated metal centers and the pore walls have no hydrogen bonding donors or acceptors, while having strong electrostatics for inducing dipoles in polarizable molecules such as CO2. For example, a gas such as CO2 is absorbed faster and stronger than other gases in the gas mixture, so that CO2 can be captured in the MOMs to the substantial exclusion of the other gases. In particular, the MOM can be used to remove or separate CO2 in a gas, where the gas includes CO2 at a concentration of about 5% or less. In an embodiment of the present disclosure have enhanced CO2 interactions at the same time have reduced interactions with water vapor.

In an embodiment, the MOM can be a hydrophobic MOM. In an embodiment, the hydrophobic MOM can be used to separate CO2 from one or more other gases, where the gas includes water vapor. Due to its hydrophobic characteristic, hydrophobic MOMs can be used in methods and systems that use gases that include water vapor, which was not previously possible in porous materials that exhibit strong physisorption towards CO2. This is advantageous because other systems and methods that use other MOMs or other porous materials must separate water vapor from the gas prior to the gas being introduced to the other MOMs or porous materials since the other MOMs or porous materials have a higher affinity for the water vapor than CO2. If the water vapor is not removed, the other MOMs are not effective at removing CO2. In addition, MOMs of the present disclosure can remove trace levels of CO2. Embodiments of the systems and methods can be simplified and result in reduced expenditure since the water vapor does not have to be removed prior to introduction to the hydrophobic MOMs. Even in the presence of water vapor, hydrophobic MOMs used in embodiments of the present disclosure are still effective at removing CO2 and are highly selective in separating CO2 from other gases such as N2, H2, and/or CH4, even at trace levels of CO2.

In particular, embodiments of the present disclosure can be used in CO2 capture systems where the gas has trace levels of CO2, and these can include direct air capture systems, pre-purification systems (e.g., PSA and cryogenic distillation), AFCs, breathing systems, mining and rescue missions, diving, and in medical applications. In addition, embodiments of the present disclosure can be used in post-combustion systems (e.g., flue gas to separate CO2 and N2), pre-combustion systems (e.g., shifted synthesis gas stream to separate CO2 and H2), and/or natural gas upgrading (e.g., natural gas cleanup to separate CO2 and CH4). In an embodiment, the hydrophobic MOMs can be used to separate other gases and can be used in processes such as He separation from natural gas, Ar separation, Kr separation, and H2/D2 separation.

Embodiments of the present disclosure provide for MOMs that are three dimensional nets that have a primitive cubic topology (See FIG. 1) that can be used in methods and systems of the present disclosure. In an embodiment, the MOM (e.g., [Cu(pyr)2(SiF6)]n) can be designed and synthesized using two dimensional square grids (or nets) (e.g., Cu (4,4′-dipyridylacetylene)2) that are linked via metal nodes using a pillar (e.g., SiF62−). In an embodiment, the two dimensional square grids include metal cations, metal cluster molecular building blocks (MBBs), or metal-organic polyhedral supermolecular building blocks (SBBs). The MBBs or SBBs serve the geometric role of the node in a network and they are connected by organic molecules, inorganic anions and/or metal complexes, which serve as linkers. The two dimensional square grids are connected to one another using other linkers or pillars that connect the metal nodes. In an embodiment, the components of the MOM (the two dimensional square grids, and its components, and pillars) can be selected to design a MOM that can be used in a system or method that includes trace levels of CO2 and/or water vapor and is highly effective at separating gases due to the MOM having a higher relative affinity for one component of the gas (e.g., CO2) over one or more other components (e.g., N2, H2, and CH4) in the gas. In this way not only is the MOM able to operate in methods and systems having high water vapor conditions, but the MOM is highly selective between or among CO2 and other components, even where the CO2 concentration is at trace levels.

In an embodiment, a method of the present disclosure includes exposing a gas to a MOM (e.g., [Cu(pyr)2(SiF6)]n). As noted above, the MOM has a greater relative affinity for a first component (e.g., trace levels of CO2) of the gas over a second component of the gas. The phrase “greater relative affinity” or similar phrases mean that a MOM can interact with a first component much more strongly than a second component so that the MOM and the first component interact to the substantial exclusion of the second component. Thus, the first component can be captured (e.g., separated) from the gas mixture to form a modified gas, where the modified gas includes the second component and a substantially reduced amount (e.g., greater than about 80% or more, about 90% or more, about 95% or more, about 99% or more, about 99.9% or more, removal of the first component from the gas) of the first component.

In an embodiment, the selectivity for CO2/N2 can be about 100 or more, about 500 or more, about 1000 or more, or about 2000 or more, based on column breakthrough experiments and at conditions of 25° C. and 1 bar total pressure using gas stream with CO2 in the range 400 ppm to 50%. The column breakthrough tests were run by passing the non-treated gas stream trough a column containing the MOFs. The gas downstream the column is monitored by a gas analyzer to determine the change in composition of each gas.

In an embodiment, the MOM has a removal capacity of about 1.2-2 mmol/g (44-71 cm3 (STP)/cm3) at 400 ppm or about 2.2-2.5-mmol/g (80-88 cm3 (STP)/cm3) at 5000 ppm.

In an embodiment, the system for capturing CO2 in a gas mixture can includes pressure (vacuum) swing adsorption, temperature swing adsorption, and combination thereof. In an embodiment, the method of separating components in a gas mixture can include removal of high CO2 concentrations, removal of intermediate CO2 concentrations, and very low CO2 concentration. In an embodiment, the method of capturing CO2 in a gas can include bulk CO2 separation (50% CO2>), CO2 purification (<5%) and CO2 ultra-purification (<1%).

As described herein, a substantial advantage of some embodiments of the present disclosure is that methods and systems using the MOMs can be conducted using a gas having water vapor, which is a completely unexpected result since most of other MOMs and related inorganic porous materials are typically hydrophilic and have a strong affinity for water so that the water vapor needs to be substantially or completely removed from the gas for the MOM to be commercially viable. In an embodiment, the water vapor in the gas can be at a concentration of about 1% to 10% at a temperature of about 273K to 340K.

In an embodiment, the gas can include two or more components and can include water vapor. In an embodiment, gas does not include water vapor. It should be noted that in many situations, the gas may primarily include a few components or only a few components that are important to the desired separation. In an embodiment, the component can include one or more of the following: CO2 (e.g., trace levels), N2, H2, CH4, He, hydrocarbons having 2 or more carbons (saturated or unsaturated and/or linear or branched), and a combination thereof. In an embodiment, CO2 can be in the gas in an amount of about 400 ppm to 50% or in an amount of about 5% or less. In an embodiment, N2 can be in the gas in an amount of about 50% to 99.99%. In an embodiment, H2 can be in the gas in an amount of about 50% to 99.99%. In an embodiment, CH4 can be in the gas in an amount of about 50% to 99.99%. In an embodiment, He can be in the gas in an amount of about 50% to 99.99%.

In an embodiment, the components in a gas can be separated using a system to introduce the gas to the MOM and remove the modified gas. In an embodiment, a first structure or device including the MOM can be interfaced with a second structure or device to introduce a gas to the first structure so that the gas and the MOM can interact so that the MOM can capture the first component (e.g., trace levels of CO2). After a sufficient period of time and under appropriate temperature conditions, the remaining gas or modified gas can be removed from the first structure. This process can be repeated as appropriate for the particular system. After a period of time, the first component can be removed from the MOM and the MOM can be reused and/or recycled using an appropriate gas handling system.

In an embodiment, the first structure and the second structure can include those used in systems such as direct air capture systems, pre-purification systems (e.g., PSA and cryogenic distillation), AFCs, breathing systems, mining and rescue missions, diving, medical applications, post-combustion systems, pre-combustion systems, natural gas upgrading systems, and He separation systems. In particular, the first structure can include structures such as those used in typical systems mentioned above. In an embodiment, the second structure can include standard gas handling systems, valves, pumps, flow meters, and the like.

As noted above, MOMs can be three dimensional nets that can have a primitive cubic topology but they could also exhibit a different topology (See FIG. 1). In an embodiment, the MOM can be designed and synthesized using two dimensional square nets that are linked via metal nodes using a molecule or ion that serves the role of a pillar. In an embodiment, the two dimensional square nets can include metal cations, MBBs, or SBBs, and linkers can be used to bond the metal ions and the MBB and the SBB.

In an embodiment, MOMs can have one of the following generic structure: (M(L)a(P)n), where M is the metal ion, L is the linker, and P is the pillar, a is 2 and n is 1. In an embodiment, the MOM has a pore size of about 3.3 Å to 3.9 Å or about 3.5 Å. L and P can be difunctional ligands that are capable of linking the metal clusters or ions such as pyrazine, 4,4′-bipyridine, 1,4-benzenedicarboxylate, hexaflourosilicate, and hexaflourotitanate. In an embodiment, these types of MOMs are described in references 13-15 below in the Example, which are incorporated herein by reference for how to describe MOMs and MOFs and the components of each.

In an embodiment, the metal cations can include M1+ (e.g., Na, K, Li, Ag, etc.); M2+ (e.g., Cu, Zn, Co, Mn, Mo, Cr, Fe, Ca, Ba, Cs, Pb, Pt, Pd, Ru, Rh, Cd, etc.); M3+ (e.g. In, Fe, Y, Ln (Yb, Tb, etc.)); M4+ (e.g., Zr, Ti, V, etc.); or other higher oxidative state metals such as +4, +5, +6, +7, and +8. In an embodiment, the MBBs and SBBs can include these metal cations as well.

In an embodiment, the linkers in the two dimensional square grid can include organic molecules, inorganic anions and/or metal complexes. In an embodiment, the linkers can include pyrazine (substituted and unsubstituted) and derivatives thereof, bipyridine (substituted and unsubstituted) and derivatives thereof, and the like.

In an embodiment, the pillars can include organic molecules, inorganic anions and/or metal complexes. In an embodiment, the pillars can include SiF62−, GeF62−, TiF62−, SnF62−, PF6, and NO3.

In an embodiment, MOMs of the present disclosure can be designed consistent with the description of (M(L)a(P)n) so that the MOM has a pore size of about 3.3 Å to 3.9 Å or about 3.5 Å. As described in the Example, MOMs having pore sizes in this range and having a high charge density are effective at trapping CO2 at concentrations of about 5% or less, about 4% or less, about 0.1 to 5%, or about 0.1 to 4%. In an embodiment, the MOM can include: [Cu(pyr)2(SiF6)]n, wherein n is 1 to 100,000,000.

EXAMPLE

Now having described the embodiments of the present disclosure, in general, the Examples describe some additional embodiments of the present disclosure. While embodiments of present disclosure are described in connection with the Examples and the corresponding text and figures, there is no intent to limit embodiments of the present disclosure to these descriptions. On the contrary, the intent is to cover all alternatives, modifications, and equivalents included within the spirit and scope of embodiments of the present disclosure.

Example 1 Brief Introduction

Direct air capture (DAC) is another alternative approach to mitigate the increasing CO2 emissions while accounting for both carbon emissions from various sources such as transportation sector and stationary power plants sources. We previously we reported how a material design and engineering approaches to pore size control, in combination with suitable sorption energetics of favourable electrostatics from an array of inorganic anions, affords MOFs with unprecedented CO2 uptake and selectivity in the context of bulk (5% and higher) CO2 capture. Herein, we report how this same approach can be used to develop isostructural materials rather suitable to air capture and traces CO2 removal. In contrast to amine scrubbing systems, amine supported materials, and sodalime sorbents, these materials exhibit also very high but non-reactive and uniformly distributed CO2 energetics, pushing the borders in enhancement of physical interactions in MOFs, in addition to fully reversible physical driven adsorption-desorption operations at very mild condition. This work shows that due to their ability for rational pore size modification and inorganic-organics moieties substitution, MOFs with periodically arrayed hexaflourosilicate (SIFSIX) pillars offers for the first time remarkable CO2 adsorption, uptake and selectivity in highly diluted gas streams that other plain class of materials are unable to achieve.

Introduction/Discussion:

The growing interest in combatting the greenhouse gas effect1 triggered a rising interest in the direct air capture (DAC) as a viable option to reduce greenhouse gases emissions in a uniform way.2-5 Although more challenging than post-combustion capture, it is recognized that DAC might be feasible, provided that suitable adsorbent combining optimum uptake, kinetics, energetics and CO2 selectivity is available at traces CO2 concentration.6

Particularly the removal of traces of CO2 from air for industrial purposes is a growing area of research and development, owing to its substantial importance particularly for pre-purification of air, when atmospheric air is used during the separation of nitrogen and oxygen. In fact, prior to air separation using cryogenic distillation or pressure swing adsorption (PSA), air must be CO2 free to avoid (i) blockage of heat-exchange equipment as a result of frozen CO2 during the liquefaction process7,8 and (ii) adsorbents (e.g., zeolites) contamination used for oxygen production by PSA.9

At the same level of importance, alkaline fuel cells (AFCs) require oxygen and hydrogen used as feedstock to be CO2 free. Indeed, trace amounts of CO2 (300 ppm) degrade the electrolyte in AFCs.10-12In addition, humans require oxygen, and in return emit carbon dioxide. Therefore, efficient removal of CO2 at low concentrations is also vital for the proper operation of breathing systems in confined spaces such as submarines and aerospace shuttles.13-15 In fact, in long-term space flight and submarine missions, CO2 must be removed from the air and recycled because resupply opportunities are less frequent or non-existent. An average crew member requires approximately 0.84 kg of oxygen and emits approximately 1 kg of carbon dioxide.15 Thus the ability to continuously purify the exhaled air (with a maximum CO2 concentration of 2-5%) will lead to an optimal recycling and considerable reduction in fresh air supply in closed, confined spaces.

Efficient CO2 removal and resupply of fresh air is also of prime importance in mining and rescue missions,16 diving, and most importantly in medical applications such as anaesthesia machines.17 The use of anaesthesia machine was and still a growing clinical trend throughout the world, driven by the need to reduce cost and improve patient care via the use of efficient CO2 sorbents. CO2 removal feature in anaesthesia machine is particularly important in semi-closed or closed rebreathing systems, as the rebreathing fraction is at least 50% of the exhaled gas volume, directed back to the patient after proper CO2 removal in the next exhalation. Sodalime is currently the sorbent of choice in most commercially available anaesthesia machines. This sorbent exhibits a high CO2 removal efficiency from exhaled air, with an average continuous operation of about 24 hours using a pre-packed commercial cartridge.18 Nevertheless, a major drawback of this technology is that one sodalime cartridge can only be used for a single cycle and is non-regenerable, generating therefore a huge amount of waste that should be disposed properly. Recently, a growing interest to low CO2 concentration removal applications,12 was spotted and few materials were reported to adsorb efficiently traces of CO2, particularly with regards to DAC using a variety of amine supported (silica based) materials.12,19 Recently, metal-organic frameworks (MOFs), which is a burgeoning class of porous materials, was intensively investigated for intermediate and high CO2 concentration removal applications such as post-combustion, pre-combustion capture, natural gas and biogas upgrading.20-23 However, the capability of MOFs to remove traces and low CO2 concentration from gas streams was rarely debated.24-27 The main reason for this lack of studies is that most of MOFs reported so far with or without unsaturated metal sites (UMC) or/and functionalized ligands exhibited relatively low selectivity and uptake particularly at low CO2 partial pressure. With the aim to enhance the CO2 adsorption energetics and uptake in MOFs and covalent organic frameworks (COFs), a few scientist,26,27 were inspired by the amine chemistry and the huge know how gained so far from amine-supported silica.20-22 In fact, recently, Jones and co-workers studied for the first time the effect of ethylenediamine (ED) grafting with Mg-MOF-74 as a support for CO2 adsorption from ultra-dilute gas streams such as ambient air.28 Long and co-workers investigated the effect of N,N-dimethylethylenediamine grafting for DAC using an expanded version of Mg-MOF-74.28 Thus, the few strategies reported so far targeting air capture using MOFs rely on the ability of grafted amines to form strong chemical bonding (at least 70 kJ/mol) with CO2, affording high affinity toward CO2 and therefore high CO2 selectivity. Interestingly, there is no work reported so far on tuning pore size of plain MOFs with the optimal CO2 energetics (strong, uniform and enough low to allow reversible physical adsorption-desorption) to target traces CO2 removal in general and DAC application in particular.

Results and Discussion:

Recently, we reported a CO2 study on a series of isoreticular MOFs with periodically arrayed hexaflourosilicate (SIFSIX) pillars, called SIFSIX-2-Cu-i and SIFSIX-3-Zn (FIG. 1). These porous MOFs having a combination of tunable pore size (rather than large surface area) coupled with requisite chemistry led to materials exhibiting fast and highly selective CO2 behaviour over N2, CH4 and H2 with uniformly aligned strong CO2 adsorption sites.23 Particularly the denser isoreticular analogue of SIFSIX pillars; SIFSIX-3-Zn revealed very steeper variable CO2 adsorption isotherms (FIG. 12) than SIFSIX-2-Cu-I (FIG. 11) suitable for post-combustion capture (at the CO2 partial pressure of 100-mbar), but also excellent features suitable for natural and biogas upgrading, as well as pre-combustion capture[20] (high CO2 concentration and high pressure).

Because of the importance of this discovery and the unprecedented steep CO2 adsorption isotherms over a wide range of temperature, particularly for this class of materials; MOFs, we found it compelling to explore the capability of these SIFSIX MOFs for CO2 adsorption in trace concentration (diluted streams in vacuum or in mixture containing large fraction of N2 up to 95%). In order to highlight the concealed capability of these MOFs for low CO2 concentration related applications involving CO2 concentration below 5% (below 50 mbar CO2 partial pressure) such as anaesthesia machines, pre-purification before air separation and air capture, single gas CO2 adsorption was investigated for SIFSIX-2-Cu-i and SIFSIX-3-Zn. Upon contraction the pore size from 5.15 Å (for SIFSIX-2-Cu-i) to 3.8 Å (for SIFSIX-3-Zn) the CO2 uptake increased drastically (FIG. 13) resulting to the highest CO2 uptake ever reported for MOFs in the range of below 5% CO2. For example, SIFSIX-3-Zn showed an order of magnitude higher volumetric CO2 uptake (55 cm3 (STP)/cm3) than Mg-MOF-74,20 (28 cm3 (STP)/cm3) at 10 mbar (1% CO2), while UTSA-16,29 exhibited much lower CO2 uptake similar to SIFSIX-2-Cu-I.

To further investigate the effect of tuning further the pore size on the adsorption properties of SIFSIX-3-M, and by studying other coordination polymers constructed from hexaflourosilicate ions with pyrazine, we found that the bonding of the Cu(II) with pyrazine leads to a slightly shorter M-N (nitrogen) bond than the zinc (see table S1 in SI),30 which will lead to further decrease in the pore size of the constructed 3D MOF, if we could substitute Zn by Cu. In order to explore this prospect, we deliberately intended to prepare the SIFSIX-3-Cu analogue which was never reported before and it was successfully prepared by layering a methanol solution (5.0 mL) of pyrazine (pyz, 0.30 g, 3.0 mmol) in a glass tube onto a methanol solution (5.0 mL) of CuSiF6.xH2O (0.325 g, 0.6 mmol). Upon layering, an extremely fast formation of light violet powder was observed, and the powder was left for 24 hours in the mother solution. The powder was then collected and washed extensively with methanol then dried under vacuum and characterized using powder X-ray diffraction (PXRD).

The PXRD diagram was found not to match with any of the related reported structures, i.e. the Cu-2D structures or the 3D Zn analogue reported by Kita et al.30 (FIG. 5). Despite extensive attempts, it was not possible to isolate synthetic conditions affording single crystals of sufficient size for single crystal diffraction (SCD), and the structure was then solved from PXRD using direct methods. The structural model was then energetically and geometrically refined, and the good agreement between experimental and calculated PXRD diagrams validates our model (FIGS. 6 and 7). Analysis of the structure revealed the formula of the Cu analogue; [Cu(SiF6)(pyz)2.solv]. As initially expected, it is in very good agreement with the 3D structure of the Zn analogue reported previously (FIG. 1),30 but with a slightly smaller unit cell (375 vs. 388 Å3) attributed to the stronger bonding between the Cu(II) and the pyrazine (Table S1 in SI).30 The smaller unit cell of the Cu analogue was in good agreement with the relatively sharp pore size distribution (PSD) analysis centred at 3.5 Å (average pore size), as determined from the CO2 isotherms, which shows smaller average pore size than the SIFSIX-3-Zn (3.5-4 Å) (FIG. 2(right)). The thermal gravimetric analysis (TGA) of the SIFSIX-3-Cu was tested in the temperature range 25-250° C. The thermogram (FIG. 8) shows a mass loss of about 10% for the dried sample in the range of 50-150 corresponding to guest molecules. Further gradual loss was observed above 150° C. due to the decomposition and loss of pyrazine and SiF6 ions. The TGA for the SIFSIX-3-Cu is in a good a greement with the one reported for the SIFSIX-3-Zn.30 Infra-red (IR) spectrum for the SIFSIX-3-Cu (FIG. 9), exhibits bands characteristic of the C—H araomatic bonds of the pyrazine at 3114 and 3073 cm−1 and bands characteristic for the C—N bond at 1445, 1122 and 1070 cm−1. In addition to that the characteristic bands for the octahedral SiF6 were also observed at 743 and 833 cm−1.31

It is logically expected that this new Cu analogue should at least show the same promising adsorption properties as the SIFSIX-3-Zn.23 Surprisingly, the Cu analogue showed even steeper variable temperature adsorption isotherms (FIG. 2(left)) at very low pressure indicative of the stronger CO2-SIFSIX-3-Cu interactions.

The mechanistic behind the unprecedented selective CO2 adsorption involving the unique synergetic effect of thermodynamics and kinetics23 was confirmed by the competitive kinetics of CO2/N2: 10/90 gas mixture adsorption (FIG. 14). As was expected and based on the similar study carried out on the Zn analogue,23 the uptake at equal times for variable CO2 compositions mixtures follow the behaviour of pure CO2 (FIG. 10). In addition at equilibrium, the total uptake of the CO2 containing gas mixtures overlay perfectly with the equilibrium uptake for pure CO2 (FIG. 10). These findings show that similarly to SIFSIX-3-Zn, when CO2 containing mixtures are in contact with SIFSIX-3-Cu, CO2 adsorbs more strongly and faster than N2 (and by analogy also O2, CH4 and H2 (FIG. 14, thus occupying all the available space and sorption sites and excluding other gases which is a desirable feature in many CO2 separation and purification applications. Examination of the SIFSIX-3-M adsorption results in the spectra of low concentration applications (400 ppm-5%) showed that the Cu analogue exhibits even steeper adsorption isotherms at very low CO2 concentration (FIG. 3a) translated into the highest uptake ever reported for MOFs without UMC or amino groups at low CO2 pressure below 38 torr (0.05 bar). This unprecedented finding is even more interesting owing to its fully physical adsorption nature where complete desorption of CO2 was established at only 323 K. At 7.6 torr (0.01 bar) SIFSIX-3-Cu exhibited 82.6 cm3(STP)/cm3 vs. 55 and 28 cm3(STP)/cm3 for SIFSIX-3-Zn and Mg-MOF-74, respectively. Interestingly, the gravimetric uptake of SIFSIX-3-Cu at 400 ppm and 298 K (1.24 mmol/g) is 10 and 15.5 times higher than the corresponding uptakes for SIFSIX-3-Zn (0.13 mmol/g) and Mg-MOF-74 (0.08 mmol/g) and even higher than the uptake of most of amine-supported silica materials (with optimal compromise of amine loading and kinetics)32 at 298 K (for example TRI-PE-MCM-411-23 (1 mmol/g)). Table 1 shows a summary of the adsorption uptake at variable low CO2 concentration (partial pressures) for SIFSIX compounds as compared to Mg-MOF-74 and amine supported materials (including MOFs); relevant to different traces CO2 removal applications. It is to notice that SIFSIX-3-Cu showed even higher CO2 uptake at 400 ppm and 328 K as compared to the corresponding uptake at 323 K for amine functionalized Mg-dobpdc-mmen (Table S3).

TABLE 1 ((CO2 adsorption uptake at various traces CO2 concentration and at 298 K in comparison to various amine supported materials)) uptake at 400 Uptake at 5000 Uptake at 10000 CO2 Qst Adsorbent ppm (0.4 mbar) ppm (5 mbar) ppm (10 mbar) (kJ/mol) SIFSIX-2-Cu-i 0.0684c/0.2d 0.097c/2.7d   0.19c/5.32d 32 SIFSIX-3-Zn  0.13c/5.6d 1.12c/39.26d 1.53c/53.97d 45 SIFSIX-3-Cu  1.24c/43.9d 2.26c/79.8d 2.34c/82.5d 54 Mg-MOF-74 0.088c/1.8d 0.7c/14.3d 1.27c/25.86d 47 Mg-MOF-74-EDa 1.5c ND ND ND Mg-dobpdc-mmenb 2c   2.5c 2.75c 70 TRI-PE-MCM-41f 1c   1.45c 1.6c 92 HASf 1.7c ND ND ND a((Ethylenediamine functionnalized24)); b((N,N-dimethylethylenediamine functionnalized25)); cmmol/g; dcm3 (STP)/cm3; [e] at 328 K; fAmine supported silica. ND: non determined; Interestingly, upon the substitution of Zn by Cu, the Qst of CO2 adsorption in the contracted structure increased by 20%, from 45 to 54 kJ mol−1 (FIG. 3b), in perfect agreement with the relatively steeper CO2 adsorption isotherms in case of the Cu analogue at very low pressure. This increase is mainly attributed to the small unit cell and the small pore size of the Cu analogue. The Qst of CO2 adsorption is an intrinsic property that dictates the affinity of the pore surface toward CO2; this in turn plays a major role in determining the adsorption selectivity and the necessary energy to release CO2 during the regeneration step. Although the Qst for CO2 was slightly above the range of fully reversible CO2 adsorption (30-50 kJ mol−1)23, SIFSIX-3-Cu was fully evacuated at 50° C. in vacuum (or in N2 environment). As in case of SIFSIX-3-Zn and SIFSIX-2-Cu-i, the Qst for CO2 adsorption was relatively constant up to high CO2 loadings indicating homogenous binding sites over the full range of CO2 loading (FIG. 3b).23

The CO2 selectivity of SIFSIX-3-Zn and SIFSIX-3-Cu was investigated experimentally using column breakthrough tests for binary CO2/N2:1000 ppm/99.99% mixture (FIG. 4 left) at 298 K in dry as well as in humid conditions. In dry condition, the first CO2 signal downstream the column was observed only after ca. 798 and ca.1922 min/g for SIFSIX-3-Zn and SIFSIX-3-Cu, respectively after starting continuous CO2/N2 gas mixture flux (5 cm3 min−1), while N2 breakthrough occurred in a few seconds. Accordingly, at 1000 ppm CO2 and breakthrough time, SIFSIX-3-Cu showed higher selectivity (ca. 10500) than SIFSIX-3-Zn (7259). We also note that the calculated and measured selectivity exceeding 1000-2000 are often subject to uncertainties associated with measurement of the gas uptake of weakly adsorbed gases (N2) in the mixture, thus the reported selectivity is highly qualitative and aiming the comparison of the studied compounds only.

The CO2 removal selectivity at 1000 ppm CO2 on SIFSIX-3-Cu was not affected by the presence of humidity as shown from the column breakthrough tests performed on both compounds at the relative humidity (RH) of 74% (FIG. 4(right)). This unprecedented finding was also valid in case of SIFSIX-3-Zn for the removal of low (FIG. 15) and higher CO2 concentration.23

In conclusion, we showed herein how a material design and engineering approaches to pore size control in combination with suitable energetics of favourable electrostatics from an array of inorganic anions affords MOFs with unprecedented CO2 uptake and selectivity in the context of air capture and traces CO2 removal. These materials exhibit very high (non-reactive) CO2 energetics but fully reversible physical driven adsorption-desorption operations at very mild conditions, without the well documented drawbacks associated with amine reactive chemistry.

This work shows for the first time that thanks to their ability for rational pore size modification and inorganic-organics moieties substitution, MOFs offers remarkable CO2 adsorption attributes in highly diluted gas streams that other plain class of materials are unable to achieve. Further works will be dedicated to study the effect of substituting other metals such as cadmium, cobalt, chromium etc., on the CO2 separation properties in diluted CO2-containing gases.

Methods: SIFSIX-3-Cu:

A methanol solution (5.0 mL) of pyrazine (pyz, 0.30 g, 3.0 mmol) was layered in a glass tube onto a methanol solution (5.0 mL) of CuSiF.xH2O (0.325 g, 0.6 mmol). Upon layering, a fast formation of light violet powder was observed, and the powder was left for 24 hours in the mother solution. The powder was then collected and washed extensively with methanol then dried under vacuum Characterization:

The powder PXRD patterns were recorded on a Panalytical X'pert PRO MPD X-ray Diffractometer with Cu Kα radiation=0.15418 nm, 45 kV, 40 mA).

Low pressure gas sorption measurements were performed on a fully automated micropore gas analyzer Autosorb-1C (Quantachrome Instruments) at relative pressures up to 1 atm. The cryogenic temperatures were controlled using a liquid nitrogen bath at 77 K. Pore size analyses were performed using a cylindrical NLDFT pore model system by assuming an oxidic (zeolitic) surface.

High Pressure Adsorption:

Adsorption equilibrium measurements of pure gases were performed using a Rubotherm gravimetric-densimetric apparatus (Bochum, Germany) (Scheme S1), composed mainly of a magnetic suspension balance (MSB) and a network of valves, mass flowmeters and temperature and pressure sensors. The MSB overcomes the disadvantages of other commercially available gravimetric instruments by separating the sensitive microbalance from the sample and the measuring atmosphere and is able to perform adsorption measurements across a wide pressure range, i.e. from 0 to 20 MPa. The adsorption temperature may also be controlled within the range of 77 K to 423 K. In a typical adsorption experiment, the adsorbent is precisely weighed and placed in a basket suspended by a permanent magnet through an electromagnet. The cell in which the basket is housed is then closed and vacuum or high pressure is applied. The gravimetric method allows the direct measurement of the reduced gas adsorbed amount Q. Correction for the buoyancy effect is required to determine the excess and absolute adsorbed amount using equation 1 and 2, where Vadsorbent and Vss and Vadsorbed phase refer to the volume of the adsorbent, the volume of the suspension system and the volume of the adsorbed phase, respectively.


Ω=mabsolute−ρgas(Vadsorbent+Vss+Vadsorbed-phase)  (1)


Ω=mexcess−ρgas(Vadsorbent+Vss)  (2)

The buoyancy effect resulted from the adsorbed phase maybe taken into account via correlation with the pore volume or with the theoretical density of the sample.

Structure Determination

DICVOL06 was used for pattern indexing of SIFSIX-3-Cu; the cell refinement was carried out by a structureless whole pattern profile refinement using the FullProf software and its graphical interface WinPlotr. (J. Epdic 7: European Powder Diffraction, Pts 1 and 2 Vol. 378-3 Materials Science Forum (eds R. Delhez & E. J. Mittemeijer) 118-123 (2001)) The structure of SIFSIX-3-Cu was solved ab initio on the as-synthesized solid using powder X-Ray diffraction (PXRD) data by direct method using Expo2009. (J. Appl. Crystallogr. 42, 1197-1202, (2009)). All framework atoms were found directly and their coordinates geometrically and energetically refined through Forcite in Materials Studio 6.0.0.

TABLE S2 Crystallographic data of SIFSIX-3-Cu. Compound SIFSIX-3-Cu Formula (dried solid) C8N4H8CuSiF6 Molar weight (g · mol−1) 365.80 Calculated density (g · cm−3) (dried solid) 1.62 Symmetry Tetragonal Space group P 4/m m m (no 123) a (Å) 6.901(1) b (Å) 6.901(1) c (Å) 7.886(1) V (Å3) 375.5 Z 1 Wavelength λ(Cu K) 1.5406 Temperature (K) 298 Angular range 2-theta (°) 3-80 Number of independent atoms (dried solid) 8

TABLE S3 Gravimetric CO2 uptake at 400 ppm and 328 K for SiF6-Cu-3, SiF6-Zn-3 and SiF6-Cu-2-i in comparison to Mg-dobpdc-mmen Uptake at 400 ppm (0.4 Adsorbent mbar) mmm/g SIF6-2-Cu-i negligible SIF6-3-Zn 0.0287 SIF6-3-Cu 0.242 Mg-dobpdc-mmenb ≈0.12 bat 323 K

REFERENCES

  • 1 Chu, S. Carbon Capture and Sequestration. Science 325, 1599-1599, doi:10.1126/science.1181637 (2009).
  • 2 Lackner, K. S. & Wright, A. B. Removal of carbon dioxide from fluid involves bringing the gas in contact with resin, wetting resin with water, collecting water vapor and carbon dioxide, separating and delivering carbon dioxide for further processing. WO2009105566-A2; U52009232861-A1; WO2009105566-A3; MX2010009059-A1; CA2715874-A1.
  • 3 Major, C. J., Sollami, B. J. & Kammerme, K. CARBON DIOXIDE REMOVAL FROM AIR BY ADSORBENTS. Industrial & Engineering Chemistry Process Design and Development 4, 327-&, doi:10.1021/i260015a019 (1965).
  • 4 Stolaroff, J. K., Keith, D. W. & Lowry, G. V. Carbon dioxide capture from atmospheric air using sodium hydroxide spray. Environmental Science & Technology 42, 2728-2735, doi:10.1021/es702607w (2008).
  • 5 Nikulshina, V., Gebald, C. & Steinfeld, A. CO2 capture from atmospheric air via consecutive CaO-carbonation and CaCO3-calcination cycles in a fluidized-bed solar reactor. Chemical Engineering Journal 146, 244-248, doi:10.1016/j.cej.2008.06.005 (2009).
  • 6 Goeppert, A., Czaun, M., Prakash, G. K. S. & Olah, G. A. Air as the renewable carbon source of the future: an overview of CO2 capture from the atmosphere. Energy & Environmental Science 5, 7833-7853, doi:10.1039/c2ee21586a (2012).
  • 7 Rege, S. U., Yang, R. T. & Buzanowski, M. A. Sorbents for air prepurification in air separation. Chemical Engineering Science 55, 4827-4838, doi:10.1016/s0009-2509(00)00122-6 (2000).
  • 8 Rege, S. U., Yang, R. T., Qian, K. Y. & Buzanowski, M. A. Air-prepurification by pressure swing adsorption using single/layered beds. Chemical Engineering Science 56, 2745-2759, doi:10.1016/s0009-2509(00)00531-5 (2001).
  • 9 Santos, J. C., Magalhaes, F. D. & Mendes, A. Contamination of zeolites used in oxygen production by PSA: Effects of water and carbon dioxide. Industrial & Engineering Chemistry Research 47, 6197-6203, doi:10.1021/ie800024c (2008).
  • 10 Kordesch, K. et al. Alkaline fuel cells applications. J. Power Sources 86, 162-165 (2000).
  • 11 Haring, H. W. Industrial Gases Processing. Wiley-VCH Verlag GmbH & Co: Weinheim (2008).
  • 12 Belmabkhout, Y., Serna-Guerrero, R. & Sayari, A. Adsorption of CO2-containing gas mixtures over amine-bearing pore-expanded MCM-41 silica: application for CO2 separation. Adsorption-Journal of the International Adsorption Society 17, 395-401, doi:10.1007/s10450-011-9348-0 (2011).
  • 13 Ernsting, J. Breathing systems in aerospace. IEE Seminar. Low Flow Anaesthesia Breathing Systems—Technology, Safety and Economics (Ref No. 1999/060), 7/1-4 (1999).
  • 14 Satyapal, S., Filburn, T., Trela, J. & Strange, J. Performance and properties of a solid amine sorbent for carbon dioxide removal in space life support applications. Energy & Fuels 15, 250-255, doi:10.1021/ef0002391 (2001).
  • 15 Mattox, E. M., Knox, J. C. & Bardot, D. M. Carbon dioxide removal system for closed loop atmosphere revitalization, candidate sorbents screening and test results. Acta Astronautica 86, 39-46 (2013).
  • 16 Moore, P. Miner Protection. Mining Magazine 196, 35-38 and 40-41 (2007).
  • 17 Dosch, M. P. The Anesthesia Gas Machine. http://www.udmercy.edu/crna/agm (2006).
  • 18 http://www.gehealthcare.com/euen/anesthesia/products/airway-management-accesories-supplies/medisorb-CO2-absorbent/index.html.
  • 19 Sayari, A. & Belmabkhout, Y. Stabilization of Amine-Containing CO2 Adsorbents: Dramatic Effect of Water Vapor. Journal of the American Chemical Society 132, 6312-6313, doi:10.1021/ja1013773 (2010).
  • 20 Caskey, S. R., Wong-Foy, A. G. & Matzger, A. J. Dramatic tuning of carbon dioxide uptake via metal substitution in a coordination polymer with cylindrical pores. Journal of the American Chemical Society 130, 10870-10873, doi:10.1021/ja8036096 (2008).
  • 21 Sumida, K. et al. Carbon Dioxide Capture in Metal-Organic Frameworks. Chemical Reviews 112, 724-781, doi:10.1021/cr2003272 (2012).
  • 22 Sayari, A., Belmabkhout, Y. & Serna-Guerrero, R. Flue gas treatment via CO2 adsorption. Chemical Engineering Journal 171, 760-774, doi:10.1016/j.cej.2011.02.007 (2011).
  • 23 Nugent, P. et al. Porous materials with optimal adsorption thermodynamics and kinetics for CO2 separation. Nature 495, 80-84, doi:10.1038/nature11893 (2013).
  • 24 Xue, D. X. et al. Tunable Rare-Earth fcu-MOFs: A Platform for Systematic Enhancement of CO2 Adsorption Energetics and Uptake. J. Am. Chem. Soc. 135, 7660-7667 (2013).
  • 25 Belmabkhout, Y. & al., e. Highly stable rht-MOF decorated with nitrogen donor groups: An unprecedented step toward trace carbon dioxide removal. Energy & Environmental science submitted (2013).
  • 26 McDonald, T. M. et al. Capture of Carbon Dioxide from Air and Flue Gas in the Alkylamine-Appended Metal-Organic Framework mmen-Mg-2(dobpdc). Journal of the American Chemical Society 134, 7056-7065, doi:10.1021/ja300034j (2012).
  • 27 Choi, S., Drese, J. H., Eisenberger, P. M. & Jones, C. W. Application of Amine-Tethered Solid Sorbents for Direct CO2 Capture from the Ambient Air. Environmental Science & Technology 45, 2420-2427, doi:10.1021/es102797w (2011).
  • 28 Didas, S. A., Kulkarni, A. R., Sholl, D. S. & Jones, C. W. Role of Amine Structure on Carbon Dioxide Adsorption from Ultradilute Gas Streams such as Ambient Air. Chemsuschem 5, 2058-2064, doi:10.1002/cssc.201200196 (2012).
  • 29 Xiang, S. et al. Microporous metal-organic framework with potential for carbon dioxide capture at ambient conditions. Nature Communications 3, doi:10.1038/ncomms1956 (2012).
  • 30 Uemura, K., Maeda, A., Maji, T. K., Kanoo, P. & Kita, H. Crystal structires and adsorption properties of ultramicroporous coordiunation polymers constructed ions from hexafluorosilicate ions and pyrazine. Eur. J. inorg. Chem., 2329-2337 (2009).
  • 31 Conley, B. D., Yearwood, B. C., Parkin, S. & Atwood, D. A Ammonium hexaflurosilicate salts. Journal of Fluorine Chemistry 115, 155-160 (2002).
  • 32 It is important to notice that hyperbranched aminosilica material (HAS)25 was reported to exhibit higher gravimetric uptake (1.7 mmol/g) at 390 ppm and 298 K, however the kientics of adsorption was much slower due the diffusion limitation caused by the high amine loading. To overcome this issue, The strategy of use of higly porous materials as MOFs as support for amine grafting is a clever pathway to develop highly CO2 selective MOFs with high uptake and optimal CO2 adsorption kinetics as reported recently27,28. ED amine grafted Mg-dobdc27 and N,N-dimethylethylenediamine Mg-dobdc28 were reported recently to exhibit 1.5 and 2 mmol/g uptake at 390 ppm, respectively. Nevertheless reactive air capture of CO2 using amines may have relatively larger energy input in term of desorption and regeneration options is yet to be studied.

In regard to the discussion herein including the Examples above and the claims, it should be noted that ratios, concentrations, amounts, and other numerical data may be expressed herein in a range format. It is to be understood that such a range format is used for convenience and brevity, and thus, should be interpreted in a flexible manner to include not only the numerical values explicitly recited as the limits of the range, but also to include all the individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited. To illustrate, a concentration range of “about 0.1% to about 5%” should be interpreted to include not only the explicitly recited concentration of about 0.1 wt % to about 5 wt %, but also include individual concentrations (e.g., 1%, 2%, 3%, and 4%) and the sub-ranges (e.g., 0.5%, 1.1%, 2.2%, 3.3%, and 4.4%) within the indicated range. In an embodiment, the term “about” can include traditional rounding according to measurement techniques and the units of the numerical value. In addition, the phrase “about ‘x’ to ‘y’” includes “about ‘x’ to about ‘y’”.

Many variations and modifications may be made to the above-described embodiments. All such modifications and variations are intended to be included herein within the scope of this disclosure and protected by the following claims.

Claims

1. A method of capturing CO2 in a gas, comprising:

exposing the gas to a metal-organic material (MOM), wherein the gas includes CO2 at a concentration in the gas of about 5% or less; and
capturing the CO2 in the MOM.

2. The method of claim 1, wherein the gas includes at least one of the following gases: N2, H2, or CH4, wherein the MOM has a greater relative affinity for CO2 over each one of N2, H2, and CH4.

3. The method of claim 1, wherein the MOM is [Cu(pyr)2(SiF6)]n, wherein n is 1 to 100,000,000.

4. The method of claim 1, wherein the MOM has a pore size of about 3.35 Å.

5. The method of claim 1, wherein the gas includes N2.

6. The method of claim 1, wherein the gas includes H2.

7. The method of claim 1, wherein the gas includes CH4.

8. A system for capturing CO2 in a gas, comprising:

a first structure including a metal-organic material (MOM), wherein the gas includes CO2 at a concentration in the gas of about 5% or less; and
a second structure for introducing the gas to the first structure, wherein CO2 is removed from the gas after the exposure to the MOM to form a modified gas, wherein the second structure flows the modified gas away from the first structure.

9. The system of claim 8, wherein the gas includes at least one of the following gases: N2, H2, and CH4, wherein the MOM has a greater relative affinity for CO2 over each one of N2, H2, and CH4.

10. The system of claim 8, wherein the MOM is [Cu(pyr)2(SiF6)]n, wherein n is 1 to 100,000,000, and wherein the MOM has a pore size of about 3.35 Å.

11. The system of claim 8, wherein the gas a second component, wherein the MOM has a greater relative affinity for CO2 over the second component.

12. The system of claim 8, wherein the MOM has a greater relative affinity for CO2 over water vapor present in the gas.

13. The system of claim 8, wherein the second gas is selected from the group consisting of: N2, H2, CH4, or a combination thereof.

14. The system of claim 8, wherein the MOM is a hydrophobic MOM.

15. A composition, comprising: a MOM comprising [Cu(pyr)2(SiF6)]n, wherein n is 1 to 100,000,000, and wherein the MOM has a pore size of about 3.35 Å.

16. The composition of claim 15, wherein the MOM is a hydrophobic MOM.

Patent History
Publication number: 20170113204
Type: Application
Filed: Feb 18, 2015
Publication Date: Apr 27, 2017
Inventors: Mohamed EDDAOUDI (Tampa, FL), Michael J. ZAWOROTKO (Tampa, FL), Patrick NUGENT (Tampa, FL), Stephen BURD (Tampa, FL), Ryan LUEBKE (Thuwal), Youssef BELMABKHOUT (Thuwal), Osama SHEKHAH (Thuwal)
Application Number: 15/119,870
Classifications
International Classification: B01J 20/22 (20060101); B01J 20/28 (20060101); B01D 53/02 (20060101);