Abstract: High-strength brass alloy having superior wear maintains single-structure ? phase and Fe-Cr-Si-based intermetallic compounds dispersed in the ? phase. A high-strength brass alloy for sliding member comprises, Zn from 17% to 28%, Al from 3% to 10%, Fe from 1% to 4%, Cr from 0.1% to 4%, Si from 0.5% to 3%, mass ratio, and the remnant including Cu and inevitable impurities. The high-strength brass alloy has structure in which the matrix shows single-phase structure of ? phase and Fe-Cr-Si-based intermetallic compounds are dispersed in the ? phase. The high-strength brass alloy for sliding member has the structure in which the matrix shows single-structure of ? phase and hard Fe-Cr-Si-based intermetallic compounds are dispersed in the ? phase. Thus the hardness is increased and wear resistance is improved.