Abstract: A method for controlling morphology of a silicone organic block copolymer includes adding an MQ resin to the silicone organic block copolymer and annealing. The method is useful for forming thin films, which are useful in electronic device fabrication. The method is also useful for forming adhesives, release coatings, and reversible elastomers.

Abstract: A liquid coating composition comprising a resin solids content comprising (i) a binder solids content comprising at least one hydroxyl-functional binder A and 0.5 to less than 5 wt. % of at least one polyurethane resin B with functional groups selected from the group consisting of hydroxyl groups, free isocyanate groups and blocked isocyanate groups and (ii) at least one cross-linker C, wherein the at least one polyurethane resin B is present as particles having a melting temperature of 40 to 200° C.

Abstract: A block copolymer composition containing a diblock copolymer blend including a first poly(methyl methacrylate)-b-poly((trimethylsilyl)methyl methacrylate) diblock copolymer; and, a second poly(methyl methacrylate)-b-poly((trimethylsilyl)methyl methacrylate) diblock copolymer. Also provided are substrates treated with the block copolymer composition.

Abstract: An inkjet ink composition includes: (a) particles of a polymer compound having at least one reactive functional group selected from the group consisting of an epoxy group, an acetoacetoxy group, a halomethyl group, a carboxylic acid anhydride, an amino group, a hydroxyl group, a phenolic hydroxyl group, and a carboxy group; (b) a reactive compound having a functional group that reacts with the reactive functional group of the (a) particles of the polymer compound by energy application; (c) a coloring agent; and (d) a water-soluble organic solvent.

Abstract: A copolymer composition including a block copolymer having a poly(methyl methacrylate) block and a poly((trimethylsilyl)methyl methacrylate) block is provided; wherein the block copolymer exhibits a number average molecular weight, MN, of 1 to 1,000 kg/mol; and, wherein the block copolymer exhibits a polydispersity, PD, of 1 to 2. Also provided are substrates treated with the copolymer composition.

Abstract: A coating composition for metal or refractories includes a polysilazane resin; and one or more additives that alter the thermal conductivity and/or the abrasion resistance of the cured polysilazane resin. The coating composition may be applied to a metal or refractory material substrate and heated to form a ceramic layer on the substrate. The ceramic layer exhibits lower thermal conductivity and increased abrasion resistance.

Abstract: The invention relates to a crosslinker composition comprising a reaction product of a cyclic urea U and a multi-functional aliphatic aldehyde A, and at least one crosslinker selected from the group consisting of reaction products of an amino-triazine and at least one aldehyde selected from the group consisting of aliphatic monoaldehydes and multifunctional aliphatic aldehydes having the structure Y(CHO)n, where Y is an n-functional aliphatic residue, and n is greater than 1; reaction products of urea and/or cyclic ureas and formaldehyde; alkoxycarbonyl-aminotriazines; multifunctional isocyanates which may be partially or completely blocked; reaction products of phenols and aliphatic monoaldehydes; multifunctional epoxides; multifunctional aziridines; and multifunctional carbodiimides, wherein any of the crosslinkers which have hydroxyl groups may be etherified with one or more linear, branched, or cyclic aliphatic alcohols.

Abstract: The invention relates to a membrane having a pore-free separating laye including a polymer mixture for separating simple alcohols and water fr their mixtures with other organic fluids by means of pervaporation or vapor permeation. In accordance with the invention, the polymer mixtu is composed of at least two polymer components which are taken from t group of polymer components which includes of the following polymer components: Polyvinyl alcohol, other polymers such as poly N-N-dimethylaminoethyl methacrylate (poly DMAEMA), a copolymer of DMAEMA and N-vinyl pyrrolidone (NVP) or of DMAEMA and N-vinyl caprolactam (NVCL), a terpolymer of DMAE, NVP and NVCL or of vinyl acetate ethylene vinyl chloride or from vinyl chloride ethylene acrylic es or from vinyl acetate vinyl chloride acrylic ester. The invention further relates to the use and to a method for manufacturing a membrane in accordance with the invention.

Abstract: A method for forming a film, containing the following steps (1) to (4), and a film obtained by the method for forming a film: step (1): preparing an aqueous dispersion liquid containing (A) a hydrophilic functional group-containing resin, (B) an ammonium salt, and (C) a nonionic thickener, a mixed amount of the component (B) being from 0.25 to 10 parts by mass per 100 parts by mass of a solid content of the component (A); step (2): coating the aqueous dispersion liquid on at least one surface of a substrate to form a coated film; step (3): subjecting the coated film to a thermal gelation treatment to form a gelled film; and step (4): drying and solidifying the gelled film to form a film.

Abstract: The invention relates to an electrode for electrolytic applications, optionally an oxygen-evolving anode, obtained on a titanium substrate and having a highly compact dual barrier layer comprising titanium and tantalum oxides and a catalytic layer. A method for forming the dual barrier layer comprises the thermal decomposition of a precursor solution applied to the substrate optionally followed by a quenching step and a lengthy thermal treatment at elevated temperature.

Abstract: The invention pertains to a printing form and a process for preparing the printing form from a solvent-free curable composition that includes, in prescribed relative amounts, an epoxy novolac resin; a bisphenol-A epoxy resin or a bisphenol-F epoxy resin; a monofunctional reactive diluent; a multifunctional reactive diluent; and a stoichiometric amount of an amine curing agent. The ratio of the epoxy novolac resin to the bisphenol epoxy resin is 1:3 to 3:1 by weight. The process includes applying the curable composition to a supporting substrate to form a layer, curing the layer at one or more temperatures in a temperature range, and engraving to form at least one cell in the cured layer. The process prepares printing forms, particularly gravure printing forms, having a cured resin composition layer that is engravable, resistant to solvent inks and to mechanical wear, and capable of printing gravure-quality images.

Abstract: Disclosed herein are embodiments of a rotary gas separation device, such as a rotary pressure swing adsorption device. The rotary pressure swing device can include, for example, a rotor with a plurality of adsorber elements, a stator with a plurality of conduits, and a rotary valve comprising a seal assembly positioned between the rotor and the stator.

Abstract: There is stably provided a hydrophilic cured product, such as a single-layer film, in which anionic hydrophilic groups are concentrated at a surface that is in contact with the air and which is excellent in transparency and adhesion to a substrate and tends to be rarely cracked. The hydrophilic cured product or single-layer film comprising a resin composition is produced by applying a mixture containing a polyvalent monomer (II) having two or more (meth) acryloyl groups and a compound (IV) having a specific group and a sulfonic acid group to a substrate or the like, drying the mixture if necessary, and then performing polymerization.

Abstract: A coated string for a stringed device which includes a coating applied to the surface of the string. The coating includes a base layer bonded to the surface of the string and an at least partially transparent low-friction top coat applied to the base layer. The base layer includes heat activated pigments that change color when heated above a color shifting temperature. In one embodiment, the color of the pigment in one area contrasts with the color of the pigment in an adjacent area without otherwise affecting the low-friction surface of the coating. The areas of different color created in locations along the length of the low-friction coated string.

Abstract: An object of the present invention is to provide a method for forming a coating film that is capable of forming a coating film having excellent smoothness, distinctness of image and luster using an aqueous coating composition. The present invention provides a method for forming a coating film comprising: Step (1): forming an uncured coating film by applying to a substrate an aqueous coating composition that contains a copolymer of monomer components comprising one or more N-substituted (meth)acrylamide compounds, the copolymer being a graft copolymer comprising (A) a main chain having a lower critical solution temperature T1 in water within the range of 30 to 95° C., and (B) at least one hydrophobic side chain; Step (2): preheating the uncured coating film formed in Step (1) under heating conditions such that a preheating temperature T2 falls within the range of 60 to 100° C.

Abstract: A method of imparting hydrophilicity to a surface of a material, which comprises providing a base material comprising a surface; applying and chemically fixing a siloxane oligomer represented by Chemical Formula 1 to the surface of the base material to form a siloxane-modified surface; and applying a phosphonic acid compound represented by Chemical Formula 2 to the siloxane-modified surface and carrying out a reaction therebetween to form an organosiloxane coating: wherein in Chemical Formula 1, R1, R2, and R3 are the same or different, and are each independently hydrogen or a C1 to C3 alkyl group, A is a single bond or a C1 to C5 alkylene group, and n ranges from 2 to 30; GN[CH2PO3H2]2??Chemical Formula 2 wherein in Chemical Formula 2, G is —CH2PO3H2, a group represented by Chemical Formula 3, or a group represented by Chemical Formula 4 as defined herein.

Abstract: A new roofing tile with enhanced surface durability and processes for manufacturing the same. The abstract of the disclosure is submitted herewith as required by 37 C.F.R. §1.72(b). As stated in 37 C.F.R. §1.72(b): A brief abstract of the technical disclosure in the specification must commence on a separate sheet, preferably following the claims, under the heading “Abstract of the Disclosure.” The purpose of the abstract is to enable the Patent and Trademark Office and the public generally to determine quickly from a cursory inspection the nature and gist of the technical disclosure. The abstract shall not be used for interpreting the scope of the claims. Therefore, any statements made relating to the abstract are not intended to limit the claims in any manner and should not be interpreted as limiting the claims in any manner.

Abstract: The present invention relates to modified geopolymer compositions, geopolymer-coated organic polymer substrates, and methods of manufacturing and articles comprising same.

Abstract: The present invention relates to a method for preparing a functional film via coffee oil, comprising (a) extracting a coffee oil from coffee; (b) modifying the coffee oil to obtain an epoxidized coffee oil; (c) adding an alcohol into the epoxidized coffee oil to obtain a coffee polyol; (d) synthesizing a polyurethane dispersive solution with the coffee polyol; (e) coating a surface of a substrate with the polyurethane dispersive solution; and (f) drying and fixing the surface of the substrate. The present invention further provides a functional textile comprising a functional film prepared by the method of above.

Abstract: A coating method of forming a plurality of layers on a belt-like support continuously traveling, comprising: a step of applying a first coating liquid onto a front surface of the support to form a lower layer on the support; a drying step of removing a solvent in the lower layer until an amount of the residual solvent reaches not more than 100 mg/m2; a step of applying a second coating liquid onto the lower layer after drying to form an upper layer; and a drying step of removing moisture of the upper layer; wherein the drying step of removing moisture of the upper layer comprises: a first drying step of removing moisture in the upper layer until a moisture content of the upper layer reaches not more than 10% of moisture at the time of application within a range in which a following conditional expression (1) is satisfied: (1) temperature (Tw) of the support?average softening temperature (T0) of the lower layer+10° C.

Abstract: The invention relates to a circuit board having high density circuit and excellent connection reliability and lamination reliability. A resin fabric cloth (4) is provided by arranging single fibers (4a) or fiber bundles composed of a plurality of single fibers, which single fiber has a linear thermal expansion coefficient smaller than that of silicon, at least in two directions and alternately weaving them. In the board, the resin fabric cloth is covered with a resin portion (5) made of a resin material having a linear thermal expansion coefficient larger than that of silicon.

Abstract: A holding sealing material includes a mat, an inorganic binder and an organic binder. The mat includes inorganic fibers and has an upper part, a center part, and a lower part in a thickness direction. The inorganic binder is loaded on the mat. The organic binder is loaded mainly on the upper part and the lower part of the mat. The holding sealing material is disposed between an exhaust gas-treating body and a casing for housing the exhaust gas-treating body to form an exhaust gas purifying apparatus.

Abstract: A scratch-and-sniff coating is provided comprised of a first coating on a substrate having a water- and heat-resistant second coating thereon, the first coating being comprised of a non-encapsulated flavor/fragrance component and a polysaccharide component, and the second coating comprised of a shellac component. The scratch-and-sniff coating is made by forming a first coating comprised of a non-encapsulated flavor/fragrance component and a polysaccharide component and drying the first coating, and forming a water- and heat-resistant shellac-containing second coating on the first coating, and drying the second coating. An encapsulated flavor/fragrance component may optionally be present in the first coating. The scratch-and-sniff coating can be applied to a package for a consumer article.

Abstract: The invention relates to polymeric systems for stabilizing, storing and delivering hypohalide salts. One system consists of material coated with two layers: one prepared from polyethylene glycol epoxide and melamine solution and second prepared from inorganic hypohalide salt solution. The material can be fabric, cotton, bamboo, cellulosic materials, blend of cellulosic and synthetic fibres. Antimicrobial materials comprising this system are also described. Another system consists of material containing pre-formed spaces coated with water-polyethylene glycol solution of hypohalide salt and encapsulated by film forming polymer. Hypohalide salts within both systems are in some cases storage stable for at least three months.

Abstract: A process for producing a polyimide film laminate includes a substrate and a polyimide film, which includes forming a coating film including a polyamic acid solution composition on the surface of a substrate to produce a laminate composed of the substrate and the polyamic acid solution composition, heating the laminate composed of the substrate and the polyamic acid solution composition at a temperature ranging from at least 150 to 200° C. for 10 minutes or longer, and then heating the heated laminate at a temperature up to 400 to 550° C.

Abstract: Provided are: a thermosetting resin composition in which a cured product is excellent in low warp properties, thermal cycle characteristics, and the like, and occurrence of cracking of a coating film in a B-stage state is suppressed; a cured product thereof; and a printed wiring board in which the cured product is used. The thermosetting resin composition comprises: (A) an epoxy resin; (B) a curing agent for an epoxy resin; (C) spherical silicon dioxide and/or spherical aluminum oxide; and (D) a block copolymer.

Abstract: A method for forming a protective coat upon an article includes forming a liquid coating mixture comprising a cross-linking agent and a polymer dissolved within a solvent; applying a first coat of the coating mixture upon the article; evaporating the solvent from the first coat; and cross-linking the article. Also disclosed is a device containing an exterior surface at least partially covered by a coating comprising a cross-linked polymer and a filler material that is selected from the group consisting of a fullerene, a micro-encapsulated material, and a combination of two or more thereof.

Abstract: Water-entrained compositions comprising colloidal or suspensoidal solutions comprising polyimide pre-polymers/oligomers are described. These compositions are obtained in water by initial dispersion of the resin constituents in water to from colloids or suspensoids. The water-entrained polyimide compositions can be applied to numerous surfaces or more beneficially used for composite fabrication. The coated surfaces or polyimide-pre-polymer impregnated reinforcing materials are subsequently cured and are ideal for providing thermal protection.

Abstract: A coating for an ink jet printhead front face, wherein the coating comprises an oleophobic low adhesion coating having high thermal stability as indicated by less than about 15 percent weight loss when heated to up to 300° C., and wherein a drop of ultra-violet (UV) gel ink or a drop of solid ink exhibits a contact angle of greater than about 45° and sliding angle of less than about 30° with a surface of the coating, wherein the coating maintains the contact angle and sliding angle after the coating has been exposed to a temperature of at least 200° C. for at least 30 minutes.

Abstract: Disclosed is an anti-reflection film comprising a high refractive index layer comprising a first binder including a crosslinked polymer of a multifunctional (meth)acrylate compound, and nano silica particles dispersed in the first binder; and a low refractive index layer laminated on the high refractive index layer, and comprising a second binder including a crosslinked copolymer of a multifunctional (meth)acrylate compound and a fluorine-based (meth)acrylate compound, and hollow silica particles and hollow silica particles coated with a fluorine-based compound on the surface, which are dispersed in the second binder. Also disclosed is a method for manufacturing the anti-reflection film using a composition that is separated into at least two layers by phase separation after single layer coating by a more simplified process.

Abstract: The present invention provides an oven range. In the present invention, a method for coating an oxidation protective layer for a carbon/carbon composite, comprising: dissolving a polymer resin in a solvent to form a solution of polymer resin; dispersing ceramic powders in the solution of polymer resin to form a mixed solution; coating the mixed solution on a carbon fiber; performing a first heat-treatment to treat the carbon fiber by heat in air; and performing a second heat-treatment to treat the carbon fiber by heat under an inert gas.

Abstract: The present disclosure relates to a refinish coating system comprising two or more coating compositions wherein each coating composition uses the same tint composition. The coating system can provide a coating that more closely matches a color standard than does a system utilizing two differently tinted coating compositions.

Abstract: There is provided a barrier layer comprising silicate chemically coupled to a polymer matrix. There is also provided a process for making the barrier layer and uses thereof.

Abstract: Disclosed is a method of bonding ionomer compositions to metal using partially cured epoxy primers. The method is useful for preparing highly abrasion-resistant tubular articles such as pipes comprising ionomer liner layers.

Abstract: Described herein are methods for applying multiple layers of a composition to an article. Also presented are articles produced by the methods described herein. The methods include applying a first composition to the outer surface of a game card to produce a first layer, applying a second composition to the outer surface of the first layer to produce a second layer, applying an ink to the outer surface of the first layer, or the outer surface of the second layer, or both, so as to form an image, and applying a third composition to the outer surface of the second layer to produce a third layer.

Abstract: The present teachings include a coating composition which includes a liquid, fluoropolymer particles, carbon nanotubes, and a dispersant. The dispersant has a thermal degradation temperature below the melting temperature of the fluoropolymer particles.

Abstract: The invention relates to a composition suitable for producing anti-graffiti coatings, comprising substantially water-soluble and substantially fully hydrolyzed oligomeric organosiloxanes and at least one polyoxyalkylene block copolymer as a coverage agent and water, to a method for producing same, and to the use thereof. The compositions according to the invention comprise improved film formation properties evident in that cohesive films can be generated during application, such as on porous mineral substrates, without forming droplets.

Abstract: A surface-modified fibrous material is provided for incorporation in a thermoplastic matrix to form a fiber-reinforced composite article. Good binding between the fibrous material and the thermoplastic matrix is achieved through the presence of finely roughened surfaces on the fibers of nanoparticles of an inorganic material. Such nanoparticles are provided from an alkaline aqueous size composition containing the nanoparticles dispersed therein (as described). The fibrous material may be provided in continuous or discontinuous form. In a preferred embodiment glass fibers are initially provided in continuous form followed by cutting into discontinuous lengths and drying with the retention of the nanoparticles on the surfaces of the fibers. The surface-roughened fibrous material is incorporated in a thermoplastic matrix as fibrous reinforcement with the application of heat whereby the thermoplastic matrix is rendered melt processable. In preferred embodiments injection or compression molding is utilized.

Abstract: The present disclosure provides articles that include polymer coatings on substrates primed with a primer coating containing silica nanoparticles, and methods of coating. The polymer coating is preferably a silicone-based polymeric material.

Abstract: A method and structure for an ink jet printhead aperture plate assembly which can be part of an ink jet printhead and an ink jet printer. The present teachings can include the use of a protective coverlay interposed between a press plate of a press and an anti-wetting coating on a polyimide layer which forms part of the aperture plate assembly. The coverlay can include a base material which has an elastic modulus which is at least a specified value. An embodiment of the present teachings can form an aperture plate assembly and an ink jet printhead having reduced dimpling and deformation around a nozzle opening in the aperture plate assembly.

Abstract: Subject The present invention aims to provide an anode for electrolysis by an ion exchange membrane process and the manufacturing method thereof which can show a lower concentration of by-product oxygen gas in chlorine gas and a lower overvoltage stably for a long time, compared with conventional anodes.

Abstract: The invention relates to an electrode formulation comprising a catalytic layer containing tin, ruthenium, iridium, palladium and niobium oxides applied to a titanium or other valve metal substrate. A protective layer based on titanium oxide modified with oxides of other elements such as tantalum, niobium or bismuth may be interposed between the substrate and the catalytic layer. The thus obtained electrode is suitable for use as an anode in electrolysis cells for chlorine production.

Abstract: Methods of coating a magnesium substrate are provided along with coated magnesium substrates. A low melting point material is cold sprayed onto a region of the magnesium substrate. A corrosion resistant material or a zinc material is cold sprayed over at least a portion of the low melting point material to form a coated magnesium substrate. The coated magnesium substrate is then heated.

Abstract: A method for forming a protective coat upon an article includes forming a liquid coating mixture comprising a cross-linking agent and a polymer dissolved within a solvent; applying a first coat of the coating mixture upon the article; evaporating the solvent from the first coat; and cross-linking the article. Also disclosed is a device containing an exterior surface at least partially covered by a coating comprising a cross-linked polymer and a filler material that is selected from the group consisting of a fullerene, a micro-encapsulated material, and a combination of two or more thereof.

Abstract: A chromium-free fluoropolymer-containing primer composition, which can provide a coated article having excellent higher corrosion resistance by forming a fluoropolymer coating film, and a primer layer having sufficient adhesive strength to the fluoropolymer coating film on the surface of a substrate such as metal, glass, ceramic and heat resistant plastics, a method for manufacturing a coating film using the same, and a coated article using the same. The coating composition contains at least one kind of a fluoropolymer component selected from a reactive functional group-containing fluoropolymer, and a fluoropolymer having a melt flow rate (MFR), measured under a load of 5 kg and at 372° C., in accordance with ASTM D1238, of 10 to 100 g/10 minutes, and an organic titanate, wherein content of titanium contained in the organic titanate, relative to the fluoropolymer component, is 1 to 40% by weight.

Abstract: Mechanisms for coating surfaces of materials, the resulting coated materials, and solutions for use in material-coating processes are described. Triblock molecule components may be selected for desired properties. When applied in solution to a material, the molecules self-assemble into similarly oriented micro- or nanostructures coating the surface of the material. Various molecule properties can be tailored to produce a range of desirable surface coating properties. The surface coating may optionally be self cleaning if selected to be appropriately hydrophobic, allowing water and particulates to roll off of the surface with minimal friction.

Abstract: The invention relates to a method of depositing a layer of material onto the surface of an object, of the type comprising the deposition of a layer of solution of said material in a first liquid followed by the evaporation of the first liquid to form the layer of material. According to the invention, the method comprises the formation of a layer of a second liquid interposed between the object and the layer of solution, the second liquid being immiscible with the first liquid, of density greater than that of the first liquid and with an evaporating temperature higher than that of the first liquid.

Abstract: A method for depositing sol-gel derived coatings on substrates to form coated substrates includes the steps of providing a first solution including at least one sol precursor and at least one solvent. A water comprising solution is added to the first solution to form a sol-gel. The sol-gel is deposited on a substrate. The sol-gel layer on the substrate is dried/cured at a temperature ?100° C. for at least 10 minutes to form a solid layer, wherein the solid layer has a thickness from 50 nm to 110 nm. The depositing and curing steps are repeated at least once until combined thickness of the solid layers forms a coating of a predetermined thickness. The resulting solid layers are low water content layers that can be evidenced by transmission measurements. The coated substrate can be an IR transmissive substrate having a recrystallization temperature <130° C.

Abstract: The present invention provides electroactive polymers, transducers and devices that maintain pre-strain in one or more portions of an electroactive polymer. Electroactive polymers described herein may include a pre-strained portion and a stiffened portion configured to maintain pre-strain in the pre-strained portion. One fabrication technique applies pre-strain to a partially cured electroactive polymer. The partially cured polymer is then further cured to stiffen and maintain the pre-strain. In another fabrication technique, a support layer is coupled to the polymer that maintains pre-strain in a portion of an electroactive polymer. Another embodiment of the invention cures a polymer precursor to maintain pre-strain in an electroactive polymer.

Abstract: The present invention relates to coating compositions for polyurethane coating materials that feature new catalysts.