Abstract: It is an object of the present invention to provide a modified propylene resin containing very small amounts of low-crystalline and low-molecular-weight components. The present invention relates to a modified propylene resin characterized by satisfying the following requirements (1) to (4). (1) The melting point (Tm) measured with a differential scanning calorimeter (DSC) is 140° C. or higher. (2) The amount of grafts of ethylenic unsaturated bond-containing monomer after hot xylene washing is 0.1 to 5 percent by weight. (3) The amount of components soluble in o-dichlorobenzene at 70° C. is 1.5 percent by weight or less. (4) The intrinsic viscosity [?] is 0.1 to 4 dl/g.

Abstract: A process for lowering the stiffness of filled thermoplastic polymer formulations is disclosed wherein the process comprises including in said formulation a low modulus coupling agent wherein said coupling agent comprises a blend of at least two functionalized polyolefins. Also disclosed is a process for producing soft coupling agents comprising blending at least two functionalized polyolefins in pre-determined ratios, whereby chemical and physical properties of the coupling agents can be controlled.

Abstract: The invention relates to a plastic component for use in a lighting system, the plastic component comprising a semi-aromatic polyamide (X) comprising repeat units derived from aliphatic diamines and dicarboxylic acids wherein: (a) the aliphatic diamines consist a mixture of 10-70 mole % of a short chain aliphatic diamine with 2-5 C atoms and 30-90 mole % of a long chain aliphatic diamine with at least 6 C atoms; (b) the dicarboxylic acids consist of a mixture of 5-65 mole % aliphatic dicarboxylic acid and optionally aromatic dicarboxylic acid other than terephthalic acid, and 35-95 mole % terephthalic acid; and (c) the combined molar amount of terephthalic acid and the long chain aliphatic diamine is at least 60 mole %, relative to the total molar amount of the dicarboxylic acids and diamines. The invention also relates to a polymer composition that can be used for making the said plastic component comprising 100 pbw of a semi-aromatic polyamide (X) and 1-250 pbw of an inorganic material.

Abstract: To provide a dental alginate impression material composition capable of solving a problem that the permeation rate of water with respect to the whole powder of an alginate impression material is slow at the time of use so that a kneading time is long and a sufficient operational time cannot be secured, and a problem that a kneaded material drops into a throat due to aging of the material at the time of taking an impression, the dental alginate impression material composition comprises 0.001 to 1% by weight of one or more kinds selected from oils mainly consisting of a fatty acid and an ester of alcohol, waxes mainly consisting of a fatty acid and an ester of glycerin, and a fatty acid ester; 0.01 to 10% by weight of a surfactant; and 0.01 to 10% by weight of one or more kinds of specific polysaccharides.

Abstract: A polymer blend composition, in an exemplary embodiment, includes an impact modified polypropylene copolymer, and a low density polyethylene polymer. The ratio of an amount, by weight, of the impact modified polypropylene copolymer to an amount, by weight, of the low density polyethylene polymer is between about 6:4 to about 9:1.

Abstract: The invention relates to a specific and novel use of a moulding compound having the following constituents: (A) between 30 and 100 wt. % of a polyamide mixture containing (A1) between 50 and 95 wt. % of an aliphatic, partially crystalline homopolyamide or copolyamide or a mixture of such polyamides, and (A2) between 5 and 50 wt. % of a transparent homopolyamide or copolyamide or a mixture of such polyamides; and (B) between 0 and 70 wt. % of filling and reinforcing materials, and optionally auxiliary materials and additives. According to the invention, the moulding compound can be used to produce a moulded part for drinking water, especially a container or a line, in which, depending on the use, at least some regions of the processed moulding compound are essentially directly exposed to the drinking water.

Abstract: The present invention relates to the field of natural fiber reinforced polyamide compositions, particularly it relates to natural fiber reinforced polyamide compositions for manufacturing environmentally friendly electronic device housings that exhibit good mechanical properties.

Abstract: An epoxy resin composition comprises an isocyanate modified epoxy resin, which is a reaction product of (a) a multi-functional epoxy resin having an epoxy functionality of greater than about 2.2 and (b) a diisocyanate compound. An epoxy powder coating composition comprises the epoxy resin composition. The isocyanate modified epoxy resin has a high resin softening point and a high cross-linked glass transition temperature Tg for powder coating applications.

Abstract: Disclosed is a coating material for forming a gas barrier. The coating material includes a polyalcohol polymer, a polycarboxylic acid polymer, and a divalent or higher-valent metal compound whose surface is coated with a poorly water-soluble component, or alternatively a monovalent metal compound whose surface is coated with a poorly water-soluble component and a divalent or higher-valent metal compound whose surface is coated with a poorly water-soluble component. By applying this coating material to a plastic substrate layer, a gas-barrier multilayer body having a gas-barrier layer formed thereon is obtained.

Abstract: The invention relates to a polyamide moulding compound consisting of the following constituents: (A) between 25 and 70 wt. % of an aliphatic polyamide selected from the group PA1010, PA1012, PA1014, PA1210, PA1212, PA1214, PA12 and PA11, or a mixture of at least two of said systems; (B) between 8 and 35 wt. % of a transparent polyamide selected from the group MACM9-36, MACM9-36/PACM9-36, MACMI/12, MACMI/MACMT/12, or a mixture of at least two of said systems; (C) between 10 and 60 wt. % of reinforcing materials; (D) between 0 and 30 wt. % of particulate and/or layered filling materials; and (E) between 0 and 5 wt. % of auxiliary materials and/or additives, the sum of the constituents (A)-(E) amounting to 100 wt. %. Fibres are used at least partially as reinforcing materials (C), the cross-sectional surface of the fibres being either circular or the dimensional ratio of the main cross-sectional axis to the secondary cross-sectional axis being below 2.

Abstract: Tin-free, single-component silicone compositions which are stable with respect to storage in the absence of moisture, and which can be crosslinked into an elastomer by means of polycondensation reactions at ambient temperature and in the presence of water; such elastomers are adherent on various supports and harden rapidly and the silicone compositions contain an alkoxy-functional polyorganosiloxane (POS), a carboxylic acid and/or a carboxylic acid anhydride, and, optionally, a mineral filler of fumed silica type, an alkoxy-functional POS resin and an organometallic compound (containing no tin).

Abstract: A baking-drying water damping paint composition from which heavy film-thickness damping paint films can be obtained, heavy film-thickness damping paint films, in which an inorganic filler is filled into the resinous component of paints to higher extent, and which are free from the occurrence of cracks and swelling in the paint films when the paint films are baked and dried.

Abstract: Method for enhancing the crystallization rates of engineering thermoplastics through the use and incorporation of particulate additives with dimensions on the order of 10-1000 nm is described. The presence of nanoparticles at concentrations of, e.g., less than 10 weight percent of the composition, reduces the viscosity of the thermoplastics as compared to the respective homopolymer, thereby increasing polymer chain transport and diffusion to the crystallizing growth front. The prescription of this technology has been shown to reduce crystallization half times of some engineering thermoplastics by as much as 40 percent at optimal crystallization temperatures, an effect that is magnified as the temperature is reduced towards the glassy state of the amorphous phase. Nano-modified engineering thermoplastics with rapid crystallization kinetics and relatively low viscosities can be utilized in component fabrication processes that require rapid processing times, e.g., for the sake of cost efficiency.

Abstract: The invention relates to compositions intended, to be applied to the surfaces of freshly poured mortars and/or concretes, before the beginning of the setting, in order simultaneously to prevent the evaporation of the water present in said mortars and/or concretes, which is necessary for their setting and then for their hardening, and in order to create, on said treated surfaces, high adhesiveness for the finishing materials intended to cover them, these compositions being provided in the form of aqueous emulsions comprising at least one paraffin wax (a), alone or in combination with at least one hydrocarbon compound (b) and/or with at least one other hydrocarbon compound (c) different from the hydrocarbon compound (b), and also comprising at least one latex (d) formed of a colloidal aqueous emulsion of at least one polymer, and at least one pulverulent inorganic or organic filler (e).

Abstract: Polymer compositions are disclosed that are blends of polyesters prepared from terephthalic acid, 2,2,4,4-tetramethyl-1,3-cyclobutanediol, and optionally 1,4-cyclohexanedimethanol, with a reinforcing mineral filler. The composition of the blend includes up to about 40 weight % of the mineral. These formulations have a combination of toughness, heat resistance, and high modulus making the materials particularly useful in engineering molding plastics.

Abstract: Barium sulfate particles having an average particle diameter d50 of from 0.1 to 10 ?m which are produced by precipitation can be dispersed better if they are covered with at least one organic additive.

Abstract: The resin composition includes a color pigment (A) and a curable resin (B) and gives a cured film satisfying the following requirements (I), (II), (III), (IV) and (V): (I) the maximum transmittance of light having wavelengths of 500 nm to 550 nm is not less than 90%; (II) the minimum transmittance of light having wavelengths of 600 nm to 650 nm is less than 80%; (III) the maximum reflectance of light having wavelengths of 500 nm to 550 nm is less than 12%; (IV) the minimum reflectance of light having wavelengths of 600 nm to 650 nm is less than 7%; (V) the 60° gloss value measured with white light is not less than 80.

Abstract: The present invention provides novel antimicrobial polyurethane compositions having excellent mechanical and biocompatibility properties, and methods to prepare them. The antimicrobial polyurethane compositions include a homogenous distribution of silver ions by incorporating this antimicrobial agent into the composition prior to the complete polymerization of the polyurethane. In preferred embodiments, the silver ion is associated with a carrier, such as zirconium phosphate or soluble glass powder. The present invention also includes components made from the antimicrobial polyurethane compositions, such as medical devices.

Abstract: The invention discloses polymeric esters of terephthalic acid with deagglomerated barium sulphate having an average primary particle size of less than 0.5 ?m, containing a crystallization inhibitor and being coated with a dispersant, as filler. The dispersant has preferably reactive groups which are able to interact with the surface of the barium sulphate; particular preference is given to dispersants which are able to endow the barium sulphate with a hydrophilic surface and have reactive groups for coupling to or into polymers. Also disclosed is a corresponding precursor based on macrocyclic oligoesters which comprise such barium sulphate.

Abstract: A thermoplastic compound is disclosed, comprising polyhydroxyalkanoate and macrocyclic poly(alkylene dicarboxylate) oligomer. Optionally the compound also includes additional polymers and functional additives to modify physical properties of the compound. Molded or extruded plastic articles can be made from the compound. The compound is ductile, in comparison to the polyhydroxyalkanoate without the macrocyclic poly(alkylene dicarboxylate) oligomer.

Abstract: Thermoplastically processable PVC mixtures having enhanced stability are prepared by incorporating at least one stabilizer containing metal ions and a modified polyvinyl alcohol co-stabilizer.

Abstract: An organopolysiloxane composition capable of cure to an elastomeric body, the composition Comprising an organopolysiloxane containing polymer having not less than two reactable silicon-bonded groups selected from alkenyl group, condensable groups, silyl-hydride groups and/or one or more trialkylsilyl containing terminal groups, optionally a siloxane and/or silane cross-linker having at least two groups per molecule which are reactable with the reactable groups in (a); 5 to 50% by weight of the composition of at least one compatible natural oil and/or natural oil derivative based extender and/or plasticiser; a suitable cure catalyst and optionally one or more fillers. The compositions are particularly useful as sealants.

Abstract: A polylactide-based polymer or copolymer (PLA) compositions with improved flame retardancy properties as obtained by conventional melt-blending of PLA polyester matrix (1) with both calcium sulfate (2) and organo-modified layered silicates (OMLS) (3). Combination of CaSO4 and OMLS exhibits synergistic effects on PLA flame retardancy by both significantly increasing the time to ignition and decreasing the heat release rate per unit area, and promoting non-dripping properties. Moreover, all other properties of PLA remain almost unchanged or are improved as regards to pristine PLA, especially thermal and mechanical properties.

Abstract: A coating composition comprising an effective corrosion-inhibiting amount of a rare earth compound, a neutral to slightly acidic generating extender or an acidic generating extender, or combinations thereof is provided. In one embodiment, the corrosion-inhibiting components are combined with other components such as extenders, amino acids and amino acid derivatives, gelatin and gelatin derivatives, organic-based exchange resins, and combinations thereof, to enhance the corrosion resistance of the resultant coating film. The coating compositions have good adhesion to substrates such as metals, including aluminum and aluminum alloys.

Abstract: The present invention relates to a compound coating for wood comprising an alkyd resin undercoat and a siliceous coating applied on top of this undercoat. The alkyd resin undercoat may be obtained from a coating material comprising a long oil alkyd resin and a mineral component. The siliceous coating to be applied on top of the undercoat is obtainable from a coating material comprising water glass or a mixture of silica sol and water glass having a ratio of 5 to 30 mol of SiO2 per mol of alkali oxide and a mineral component.

Abstract: A moisture curable composition capable of cure to an elastomeric body comprising (a) a diluted polymer comprising (i) a silicon containing polymer of the formula X-A-X1 where X and X1 are independently selected from silyl groups which contain one or more condensable substituents per group and A is a polymeric chain having a number average molecular weight (Mn) of at least 132 000; and a degree of polymerisation of at least 1800. (ii) an organic extender and/or plasticiser which diluted polymer is obtained by polymerisation in the presence of the said organic extender and/or plasticiser (b) a suitable cross-linking agent which comprises at least two groups which are reactable with the condensable groups in the diluted polymer, (c) a suitable condensation catalyst and optionally (e) one or more fillers.

Abstract: A highly reflective coating painting product, particularly suitable as a coating for integrating spheres, comprises a diffusely reflective product such as, for example, barium sulphate, and an acrylic binder or glue, which are dispersed in a liquid vehicle, preferably constituted by a mixture of water and alcohol. The acrylic binder or glue is a product based on acrylic polymer or copolymer the quantity of which in the coating product is between about 1% and 15%, and preferably between 3% and 4%, by weight, relative to the reflective product. The coating product is applied to a surface in successive layers until a thickness of at least 0.5 mm is reached. The surface coated with the product is then subjected to heating, preferably at about 100° C., for about 1 hour.

Abstract: Wood pulp is treated with an esterase formulation in combination with a metal ion or cationic polymer to increase the stability or activity or both of esterase enzymes at high temperature, or at extreme pH ranges of acidic and alkaline conditions. The treatment by esterase together with metals ion or cationic polymer can be used to treat pitch containing pulp at high temperatures prior to, during or after refining of wood chip/pulp, in order to enhance the reduction of pitch problems and facilitate in the manufacture of paper.

Abstract: An adhesive composition includes 100 parts by weight of a polyolefin polymer derived from an olefin monomer copolymerized with at least one co-monomer that is different form the olefin monomer; 1˜100 parts by weight of an adhesion promoting agent comprising a polybutadiene polymer, which has a molecular weight of 1,000˜10,000 and has an anhydride group grafted thereon; 0.1˜5 parts by weight of an antioxidant; and 0.5˜15 parts by weight of a curative agent. An adhesive composition includes 100 parts by weight of a polyolefin polymer derived from an olefin monomer copolymerized with at least one co-monomer that is different form the olefin monomer, where in the polyolefin polymer comprises an anhydride group grafted thereon; 0.1˜5 parts by weight of an antioxidant; and 0.5˜15 parts by weight of a curative agent.

Abstract: Methods and compositions are provided for protecting exterior surfaces of automobiles and other products, or components of products, against abrasion, abrasive dust, water, acid rain, etc. The methods involve applying to a surface a protective coating composition comprising a polyvinyl butyrate emulsion and a relatively inert extender. The emulsion is dried to form a water-resistant protective coating that can be removed from the underlying surface by peeling when no longer desired.

Abstract: The invention provides a method for manufacturing a water-based dispersion of a self-dispersing polymer, including: obtaining a copolymer solution including a copolymer having a hydrophilic constituent unit and a hydrophobic constituent unit, and a solvent dissolving that dissolves the copolymer; obtaining a water-based dispersion of the copolymer through dispersion using the copolymer solution and water; and adding a water-soluble electrolyte selected from an acidic compound and the salt thereof to either or both of the copolymer solution and the water-based dispersion, as well as a water-based ink composition including the water-based dispersion, an ink set including the water-based ink composition, and an image forming method using the water-based ink composition or the ink set.

Abstract: A polyorganosiloxane polyoxyalkylene block copolymer having one or more polyorganosiloxane blocks and one or more polyoxyalkylene blocks linked to each other via divalent radicals which comprises at least two silicon-bonded alkoxy groups, cc preferably of the form PS (A PO)m(A PS)n, wherein PO is a polyoxyalkylene block, PS represents a polyorganosiloxane block, A is a divalent radical, m and n have independently a value of at least 1, comprising at least one alkoxy-substituted siloxane unit of the formula (R?)q(OR)—SiO3-q/2, wherein R represents an alkyl group having 1 to 4 carbon atoms and each R? represents an alkyl group having 1 to 6 carbon atoms, a phenyl group, or an alkoxy group of the formula —OR and q has a value of 0, 1 or 2, provided at least two silicon-bonded groups OR are present in the block copolymer.

Abstract: The present invention relates to a pigment dispersion solution, a pigment photoresist and a color filter. The pigment dispersion solution includes a colored pigment, a dispersant, a binder resin and a solvent, and further includes particles of white pigment. The pigment photoresist using the pigment dispersion solution of the present invention includes an alkali-soluble resin, a monomer, a photo initiator and an additive. The color filter using the pigment photoresist of the present invention includes a substrate, and the pigment photoresist is developed to be shaped in regions corresponding to pixels on the substrate. The present invention adopts a technical means that adding the particles of the white pigment into the pigment dispersion solution, thereby taking advantage of properties such as high reflectivity and diffused reflection on surface of the white pigment, so as to increase transmitting path and absorbing path of lights in the pigment dispersion solution.

Abstract: Emulsion paint type damping coatings show an excellent film forming property even if it leaves at low temperature from 5 to 20° C. It does not generate a defective coated film like swellings after baking drying and brings out an excellent damping performance within a range of 20 to 60° C. That is, it contains one or more than two kinds of organic chemicals within a range of 0.5% to 5% by weight in total and the MFT, the minimum film forming temperature of the entire resin emulsion is within a range of 5 to 15° C. and the boiling point for a film forming assistant is within a range of 150 to 240° C., thus, it enables to obtain an excellent film forming property at 5° C. and even in baking drying and does not generate a defective coated film like swellings as well. As a result, emulsion paint type damping coatings bring out an excellent damping performance within a range of 20 to 60° C.

Abstract: The present invention provides an acrylic acid ester copolymer emulsion composition, and redispersible powders made therefrom. The acrylic acid ester copolymer emulsion composition comprises polyvinyl alcohol having a degree of saponification of 85 mol % or more, and an average degree of polymerization of 300 to 1400; hydrophilic ethylenic unsaturated monomers having a water solubility of 1% or more; hydrophobic ethylenic unsaturated monomers having a water solubility of less than 1%; and a lipophilic initiator. The acrylic acid ester copolymer composition according to the present invention has excellent polymerization stability, and improved water resistance, alkali resistance, and fluidity, and the redispersible powders prepared by a spray-dry of the acrylic acid ester copolymer composition have improved water redispersibility, and thus, can be used in various fields such as an additive to a hydraulic material, a powder paint, and an adhesive.

Abstract: The present invention relates to novel drug depot implant designs for optimal delivery of therapeutic agents to subjects. The invention provides a method for alleviating pain associated with neuromuscular or skeletal injury or inflammation by targeted delivery of one or more therapeutic agents to inhibit the inflammatory response which ultimately causes acute or chronic pain. Controlled and directed delivery can be provided by drug depot implants, comprising therapeutic agents, specifically designed to deliver the therapeutic agent to the desired location by facilitating their implantation, minimizing their migration from the desired tissue location, and without disrupting normal joint and soft tissue movement.

Abstract: A filled polymer composition comprises (i) an ethylene/?-olefin interpolymer, and (ii) a filler. The ethylene/?-olefin interpolymer is a block copolymer having at least a hard block and at least a soft block. The soft block comprises a higher amount of comonomers than the hard block. The block interpolymer has a number of unique characteristics disclosed here. The filled polymer compositions provided herein, in certain embodiments, have relatively higher heat resistance and improved noise, vibration and harshness properties and can be used in automotive floorings, roofings, wire and cable coating applications.

Abstract: The present invention relates to nanocomposites and a process for preparing polymer nanocomposites (e.g., a continuous process). More particularly, the present invention relates to polymer nanocomposites containing a combination of one or more polymers (e.g., one or more polyolefins or one or more polyamides) with one or more types of nanoparticles, and to methods to produce such nanocomposites. In one embodiment, the present invention relates to polyamide nanocomposites wherein organoclay particles are intercalated with a polyamide polymer.

Abstract: Compacted additive blends, or polymer stabilization agent blends, can be added during the post-polymerization process to enhance the processability performance of polymers. The addition of certain compaction aids, such as high melting or non-melting metallic silicates and others, increases the resistance to friability of the compacted additive pellets. These compaction aids are non-migratory during the compaction process and after introduction into the polymer resin and thus have no deleterious effects. The additive blend can contain a variety of suitable additives in addition to the compaction aids.

Abstract: Thermal barrier synthetic polymer composite embraces a synthetic polymer matrix made from reaction of a mixture of at least an isocyanate and an active hydrogen-containing compound, in intimate admixture and combination with at least one water-releasing mineral additive. Thermal barrier, fire resistance, fire retardant, and smoke reducing properties are provided by the composite.

Abstract: A coating for preparing a floor underlayment to receive an adhesive includes a water-soluble, latex polymer, a defoamer and a dual-function surface enhancing agent. The surface enhancing agent includes a set accelerator that also functions to cross link the adhesive, hardening the surface of the underlayment using at least two mechanisms. One embodiment of the invention is a dry mixture that forms a coating when added to water. The dry mixture includes from about 10% to about 50% of the redispersible polymer by weight based on the mixture, from about 50% to about 90% of the surface enhancing agent and from about 0.15% to about 0.25% of the defoamer by weight based on the mixture. Other embodiments describe a liquid coating formed by adding from about 1 to about 8 parts water to 1 part of the dry mixture by volume based on the mixture.

Abstract: A long-fiber-reinforced, thermoplastic molding compound of plastics material has outstanding impact strength and notched impact strength if it contains 30 to 90% by weight of at least one thermoplastic polyolefin, 9 to 69% by weight of at least one glass-like reinforcing fiber and 1 to 30% by weight of at least one mineral filler of an average particle size in the range from 0.1 to 2 ?m. The molding compound is produced by the pultrusion method and is used in the production of domestic appliances such as washing machines or washer-dryers or electrical appliances such as coffeemakers or toasters or refrigerators or in automobile construction.

Abstract: An object of the present invention is to provide a new granulating process which can recover desired coagulated latex particles with a significantly excellent yield, and can suppress secondary coagulation under the condition having a higher temperature than a softening point of a polymer, without deteriorating the original quality of the polymer itself. A process for producing coagulated latex particles which can suppress the secondary coagulation under the condition having the broad temperature range, without deteriorating the original quality of the polymer itself by spraying or dropping a polymer latex into a gas-phase containing an inorganic salt and/or an acid, and a dispersant in an aerosol form, and dropping or feeding the droplets of the polymer latex into an aqueous phase containing a dispersant.

Abstract: The instant invention generally provides a process for extruding a melt of a mixture comprising a molecularly self-assembling (MSA) material and at least one first rheological additive to give a shaped MSA material, a shaped MSA material produced by the process, and an article comprising the shaped MSA material. The instant invention also generally provides a composition comprising a MSA material and at least one second rheological additive, a process of electrospinning the composition, and a fiber prepared by the electrospinning process.

Abstract: Plastic toughened plastics include a polymer composition having a polypropylene component and a second polymer component. The polypropylene component is present in an amount from about 50 to about 95 weight percent based on the total weight of the blend. The second polymer component is present in an amount from about 5 to about 50 weight percent based on the total weight of the blend, is a BOCD or BCD blend of at least two ssPE components, and has an overall density greater than about 0.90 g/cm3. Optionally, the plastic toughened plastics include one or more third polymer component selected from propylene-olefin elastomers and ethylene-propylene rubbers, which are present in an amount from about 1 to about 50 weight percent, based on the total weight of the blend.

Abstract: A method of producing a stable aqueous dispersion of a latex, solid particles and a dispersing agent, comprising contacting the latex with an anionic dispersing agent to form a modified latex, feeding the modified latex and the solid particles to a zone of high shear forces, and simultaneously subjecting essentially all of the modified latex and the solid particles fed to said zone to high shear forces to form a latex-particle slurry. By means of the invention, over 60 wt-% of the latex can be adsorbed on the solids. Latex immobilization increases the surface strength of final coating layer and allows for a decrease of latex consumption in paper and cardboard and paint applications.

Abstract: The disclosure provides a melt processible theromoplastic composition, comprising a major proportion of a base polymer comprising a first melt processible thermoplastic polymer having a first Fedor's solubility parameter and a first viscosity; and a combination of a carrier polymer and a surface modifying additive, the carrier polymer comprising a second melt processible thermoplastic polymer which has a second Fedor's solubility parameter that is at least about 2.5 (J/cm3)1/2 lower than the first Fedor's solubility parameter, and a second viscosity, the carrier polymer being adhered to the surface modifying additive, and wherein the first viscosity is at least about 10 times the second viscosity.

Abstract: The present invention relates to a pressure sensitive adhesive composition comprising a continuous phase and a discontinuous phase wherein a) the continuous phase comprises a water vapour permeable hydrophobic polymer; and b) the discontinuous phase comprises a water soluble salt.

Abstract: The present invention relates to a composition comprising a colored recycled polyethylene terephthalate (RPET) and an opacifying material. The composition can further comprise a virgin polyethylene terephthalate (PET), a high gas barrier or an oxygen scavenging compound. Suitable opacifying material, suitable high gas barrier polymer and suitable oxygen scavenging compound are disclosed herein. Other embodiments of the present invention include articles produced from these compositions and processes for producing these compositions.

Abstract: A composition, having an improved resistance to yellowing under heat aging, comprising at least 20 weight % of at least one polycondensation polymer having a heat deflection temperature of above 80° C. under a load of 1.82 MPa when measured according to ASTM D648, from 0 to 5 weight % of at least one polymer having a heat deflection temperature of at most 80° C. under a load of 1.82 MPa when measured according to ASTM D648, a white pigment; and a black pigment provides resistance to heat aging induced yellowing. The polycondensation polymers are advantageously selected from the group consisting of polyarylethersulfones, at least partially aromatic polyamides, polyamideimides, liquid crystalline polymers, polyimides, polyetherimides, polyaryletherketones, and polyphenylene sulfides. The polymer composition can be molded to form a variety of articles, including LED components, such as reflectors, reflector cups, and scramblers.