Abstract: A polymer useful in coating compositions is described. The polymer is preferably an unsaturated polyurethane polymer, which preferably has an iodine value of at least 10. The polymer may be combined with one or more liquid carriers to form a liquid coating composition useful in coating a variety of substrates, including planar metal substrates.

Abstract: A process is disclosed wherein ricinoleic acid from petroleum alternative vegetable castor oil that has a hydroxyl group at the 12-position or a derivative thereof (an ester or a hydrogenated compound thereof) is polymerized in the presence of a synthetic zeolite and an immobilized lipase at around normal temperature without using any harmful polymerization catalysts or organic solvents which can cause environmental pollution whereby a polyester useful in the industry that has a weight average molecular weight of 20,000 or more is obtained. This high-molecular weight polyester is crosslinked to give a crosslinked elastomer that is comparable to synthetic rubbers.

Abstract: A crosslinking agent that is an ungelled reaction product of (a) at least one aminoplast resin and (b) at least one tall oil rosin wherein the crosslinking agent is essentially free of active hydrogen functional groups and has a glass transition temperature of at least 10° C. is disclosed. Methods for preparing crosslinking agents are also disclosed. Further provided is a curable powder coating composition including a polymer having a glass transition temperature of at least 30° C. containing reactive functional groups and the present crosslinking agent; a multilayer composite coating composition and substrates coated therewith are also disclosed.

Abstract: A non-aqueous coating composition based on an oxidatively drying alkyd resin and a photo-initiator. An acid or latent acid and one or more compounds of the group of vinyl ethers, acetals, and alkoxysilanes which are reactive in the presence of an acid are incorporated into the coating composition. The vinyl ethers, acetals, and alkoxysilanes preferably are covalently bounded to the alkyd resin. The ratio of the number of oxidatively drying groups present in the alkyd resin to the number of groups reactive in the presence of an acid preferably is in the range of 1/10 to 15/1. The acid preferably is the phosphoric acid dibutyl ester.